Fracture toughness evaluation of WC–10 wt% Co hardmetal sintered under high pressure and high temperature
This work focused on fracture toughness studies of WC–10 wt% Co hardmetal fabricated through the high pressure/high-temperature technique. A powder mixture of WC–10 wt% Co was sintered at 1500–1900°C under a pressure of 7.7 GPa for 2 and 3 min. Vickers hardness test at two different loads of 15 and...
Na minha lista:
Principais autores: | Mashhadikarimi, Meysam, Gomes, Uílame Umbelino, Oliveira, M. P., Guimarães, R. D. S., Mello Júnior, M. M. B., Filgueira, Marcello |
---|---|
Formato: | article |
Idioma: | English |
Publicado em: |
Taylor and Francis Group
|
Assuntos: | |
Endereço do item: | https://repositorio.ufrn.br/handle/123456789/33243 |
Tags: |
Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
|
Registros relacionados
-
Niobium as a new binder for polycrystalline diamond (PCD) sintered via High Pressure-High Temperature (HPHT)
por: Mashhadikarimi, Meysam, et al.
Publicado em: (2021) -
Effect of High Energy Milling on the Magnetic Properties of the WC-10wt.%Co Cemented Carbides
por: Araujo, Jose Humberto, et al.
Publicado em: (2021) -
Cement slurries of oil wells under high temperature and pressure: the effects of the use of ceramic waste and silica flour
por: Souza, P. P., et al.
Publicado em: (2021) -
The influence of powder preparation condition on densification and microstructural properties of WC-Co- Al2O3 cermets
por: Alves, Salete Martins, et al.
Publicado em: (2020) -
Effect of sugarcane biomass waste in cement slurries submitted to high temperature and pressure
por: Anjos, Marcos Alyssandro Soares dos, et al.
Publicado em: (2021)