Correlação entre os ensaios de esclerometria pendular e método charpy para aços SAE 1080

More and more practicality and speed in material analysis processes are sought. One of the techniques to quantify the toughness of metallic samples is the Charpy method. However, the application of pendulum scratching test analyses to obtain properties such as toughness and dynamic hardness can b...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Cattaneo, Mariane de Lacerda
Outros Autores: Sousa, Fábio José Pinheiro
Formato: Dissertação
Idioma:pt_BR
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
Engenharia Mecânica
Esclerometria pendular
Método Charpy
Tenacidade ao impacto
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Endereço do item:https://repositorio.ufrn.br/handle/123456789/53028
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-53028
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language pt_BR
topic Engenharia Mecânica
Esclerometria pendular
Método Charpy
Tenacidade ao impacto
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
spellingShingle Engenharia Mecânica
Esclerometria pendular
Método Charpy
Tenacidade ao impacto
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Cattaneo, Mariane de Lacerda
Correlação entre os ensaios de esclerometria pendular e método charpy para aços SAE 1080
description More and more practicality and speed in material analysis processes are sought. One of the techniques to quantify the toughness of metallic samples is the Charpy method. However, the application of pendulum scratching test analyses to obtain properties such as toughness and dynamic hardness can be promising, due to its fast execution and low cost. Furthermore, it is expected to be a more suitable alternative for indirectly measuring the impact toughness of thin metal sheets, which are difficult to measure using the Charpy method. In addition to factors that hinder the use of the Charpy method, such as the plastic behavior of the material, the required standardized thicknesses and the time spent related to the manufacture of samples. Thus, the objective is to seek for a correlation between the two techniques in the characterization of SAE 1080 carbon steel samples. This material was chosen due to the ease of obtaining samples with homogeneous microstructures, through isothermal treatments. A comparison was made between the Charpy method and the pendulum hammer method, including the preparation of the specimens for both equipment, isothermal treatments and the analysis of the energies obtained in the tests. By comparing the results, one can look for a strong correlation between both measured properties. The pendulum scratching test provided results that showed a strong correlation with the results of Charpy tests performed on the samples, with correlation coefficients and Pearson's determination of approximately 0.98 and 0.97, respectively. Such a correlation between significantly different properties encourages further studies that may not only explain the mechanisms involved, but also expand knowledge about the mechanical properties of materials.
author2 Sousa, Fábio José Pinheiro
author_facet Sousa, Fábio José Pinheiro
Cattaneo, Mariane de Lacerda
format masterThesis
author Cattaneo, Mariane de Lacerda
author_sort Cattaneo, Mariane de Lacerda
title Correlação entre os ensaios de esclerometria pendular e método charpy para aços SAE 1080
title_short Correlação entre os ensaios de esclerometria pendular e método charpy para aços SAE 1080
title_full Correlação entre os ensaios de esclerometria pendular e método charpy para aços SAE 1080
title_fullStr Correlação entre os ensaios de esclerometria pendular e método charpy para aços SAE 1080
title_full_unstemmed Correlação entre os ensaios de esclerometria pendular e método charpy para aços SAE 1080
title_sort correlação entre os ensaios de esclerometria pendular e método charpy para aços sae 1080
publisher Universidade Federal do Rio Grande do Norte
publishDate 2023
url https://repositorio.ufrn.br/handle/123456789/53028
work_keys_str_mv AT cattaneomarianedelacerda correlacaoentreosensaiosdeesclerometriapendularemetodocharpyparaacossae1080
AT cattaneomarianedelacerda correlationbetweenpendulumscratchingandcharpymethodtestsforsae1080steels
_version_ 1773957440522420224
spelling ri-123456789-530282023-07-04T22:03:42Z Correlação entre os ensaios de esclerometria pendular e método charpy para aços SAE 1080 Correlation between pendulum scratching and Charpy method tests for SAE 1080 steels Cattaneo, Mariane de Lacerda Sousa, Fábio José Pinheiro https://orcid.org/0000-0003-0398-8723 http://lattes.cnpq.br/7149246970833126 https://orcid.org/0000-0002-8381-8806 http://lattes.cnpq.br/9909217959915292 Macedo, Harim Revoredo de http://lattes.cnpq.br/7784386480787292 Castro, Nicolau Apoena Engenharia Mecânica Esclerometria pendular Método Charpy Tenacidade ao impacto CNPQ::ENGENHARIAS::ENGENHARIA MECANICA More and more practicality and speed in material analysis processes are sought. One of the techniques to quantify the toughness of metallic samples is the Charpy method. However, the application of pendulum scratching test analyses to obtain properties such as toughness and dynamic hardness can be promising, due to its fast execution and low cost. Furthermore, it is expected to be a more suitable alternative for indirectly measuring the impact toughness of thin metal sheets, which are difficult to measure using the Charpy method. In addition to factors that hinder the use of the Charpy method, such as the plastic behavior of the material, the required standardized thicknesses and the time spent related to the manufacture of samples. Thus, the objective is to seek for a correlation between the two techniques in the characterization of SAE 1080 carbon steel samples. This material was chosen due to the ease of obtaining samples with homogeneous microstructures, through isothermal treatments. A comparison was made between the Charpy method and the pendulum hammer method, including the preparation of the specimens for both equipment, isothermal treatments and the analysis of the energies obtained in the tests. By comparing the results, one can look for a strong correlation between both measured properties. The pendulum scratching test provided results that showed a strong correlation with the results of Charpy tests performed on the samples, with correlation coefficients and Pearson's determination of approximately 0.98 and 0.97, respectively. Such a correlation between significantly different properties encourages further studies that may not only explain the mechanisms involved, but also expand knowledge about the mechanical properties of materials. Busca-se cada vez mais praticidade e rapidez nos processos de análises de materiais. Uma das técnicas para se quantificar a tenacidade ao impacto de amostras metálicas é o método Charpy. Entretanto, a aplicação de análises esclerométricas pendulares para se obter propriedades como tenacidade ao impacto e dureza dinâmica pode ser promissora, pela rapidez e baixo custo, além disso, espera-se tratar de uma alternativa mais adequada para se medir, de forma indireta, a tenacidade ao impacto de chapas metálicas finas que são de difícil medição pelo método Charpy. Além de fatores que dificultam o uso do método Charpy como o comportamento plástico do material, as espessuras padronizadas necessárias e o tempo gasto relacionado à fabricação das amostras. Assim, buscase a correlação entre as duas técnicas na caracterização de amostras de aço carbono SAE 1080. Este material foi escolhido devido à facilidade de se obter amostras com microestruturas homogêneas, através de tratamentos isotérmicos. Foi feita a comparação entre o método Charpy e o método do esclerômetro pendular, incluindo a preparação dos corpos de prova para ambos os equipamentos e tratamentos isotérmicos, além da análise das energias obtidas nos ensaios. Com a comparação dos resultados, foi investigada uma correlação entre ambos os ensaios. O esclerômetro pendular forneceu resultados que apresentaram uma forte correlação com os resultados dos testes Charpy realizados nas amostras, com coeficientes de correlação e de determinação de Pearson de aproximadamente 0,98 e 0,97, respectivamente. Tal correlação entre propriedades significativamente diferentes incentiva a realização de estudos mais aprofundados que possam vir não apenas a explicar os mecanismos envolvidos, mas também ampliar os conhecimentos sobre as propriedades mecânicas dos materiais. 2023-07-04T22:03:06Z 2023-07-04T22:03:06Z 2023-02-24 masterThesis CATTANEO, Mariane de Lacerda. Correlação entre os ensaios de esclerometria pendular e método charpy para aços SAE 1080. Orientador: Fábio José Pinheiro Sousa. 2023. 81f. Dissertação (Mestrado em Engenharia Mecânica) - Centro de Tecnologia, Universidade Federal do Rio Grande do Norte, Natal, 2023. https://repositorio.ufrn.br/handle/123456789/53028 pt_BR Acesso Aberto application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA

Registros relacionados