Estudo das curvas de sinterização, microestrutura e microdureza do compósito de Cu-WC

Mostrar outras versões (1)

Composite materials have been produced on a large scale in recent years due to the search for a product with different properties for use in different fields of application. Composites generated from a copper matrix and reinforced with a ceramic and refractory material have important functionality i...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Marques, Anderson Costa
Outros Autores: Mashhadikarimi, Meysam
Formato: bachelorThesis
Idioma:pt_BR
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
Sinterização
Curvas de sinterização
Compósitos Cu-WC
Moagem de alta energia.
Endereço do item:https://repositorio.ufrn.br/handle/123456789/50725
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-50725
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language pt_BR
topic Sinterização
Curvas de sinterização
Compósitos Cu-WC
Moagem de alta energia.
spellingShingle Sinterização
Curvas de sinterização
Compósitos Cu-WC
Moagem de alta energia.
Marques, Anderson Costa
Estudo das curvas de sinterização, microestrutura e microdureza do compósito de Cu-WC
description Composite materials have been produced on a large scale in recent years due to the search for a product with different properties for use in different fields of application. Composites generated from a copper matrix and reinforced with a ceramic and refractory material have important functionality in their various applications in electrical conductors and heat sinks. Thus, the present work aimed to analyze the sintering behavior of the composite powder of copper (Cu) reinforced with tungsten carbide (WC) produced through high energy milling (HEM). The MAE of powders with Cu - 10%WC composition was carried out in humid environment at 400 rpm for 2, 10 and 20 hours, using a mass ratio of powder to balls of 1:4. The powders were compacted in a unidirectional press at 150 MPa and the sintering behavior was studied using a dilatometer, at a temperature of 900°C with an isotherm of 1 hour. In this work, a study was carried out of the effect of high-energy grinding in the Cu-WC sintering process, through the sintering, microstructure and Vickers microhardness curves. The sintering curves showed that the green compacts of the powders processed for a longer milling time initially undergo a large expansion, up to 750°C. After that, a greater contraction is observed, indicating a predominance of the diffusion mechanism during the sintering process from this temperature onwards. Samples sintered after 10 hours showed better distribution and impregnation of tungsten carbide in the copper matrix. The microhardness was higher for the longest milling time, 20h, due to the greater refinement of the microstructure. Therefore, for longer grinding times, we have a greater atomic diffusion for the sintering process, a more homogeneous microstructure and a greater microhardness.
author2 Mashhadikarimi, Meysam
author_facet Mashhadikarimi, Meysam
Marques, Anderson Costa
format bachelorThesis
author Marques, Anderson Costa
author_sort Marques, Anderson Costa
title Estudo das curvas de sinterização, microestrutura e microdureza do compósito de Cu-WC
title_short Estudo das curvas de sinterização, microestrutura e microdureza do compósito de Cu-WC
title_full Estudo das curvas de sinterização, microestrutura e microdureza do compósito de Cu-WC
title_fullStr Estudo das curvas de sinterização, microestrutura e microdureza do compósito de Cu-WC
title_full_unstemmed Estudo das curvas de sinterização, microestrutura e microdureza do compósito de Cu-WC
title_sort estudo das curvas de sinterização, microestrutura e microdureza do compósito de cu-wc
publisher Universidade Federal do Rio Grande do Norte
publishDate 2022
url https://repositorio.ufrn.br/handle/123456789/50725
work_keys_str_mv AT marquesandersoncosta estudodascurvasdesinterizacaomicroestruturaemicrodurezadocompositodecuwc
_version_ 1773967113607708672
spelling ri-123456789-507252022-12-28T11:56:48Z Estudo das curvas de sinterização, microestrutura e microdureza do compósito de Cu-WC Marques, Anderson Costa Mashhadikarimi, Meysam 0000-0002-8846-658X http://lattes.cnpq.br/4372440881887239 http://lattes.cnpq.br/9422624675887080 Paskocimas, Carlos Alberto http://lattes.cnpq.br/2365059843175411 Lourenço, Cleber da Silva http://lattes.cnpq.br/2466694241417558 Sinterização Curvas de sinterização Compósitos Cu-WC Moagem de alta energia. Composite materials have been produced on a large scale in recent years due to the search for a product with different properties for use in different fields of application. Composites generated from a copper matrix and reinforced with a ceramic and refractory material have important functionality in their various applications in electrical conductors and heat sinks. Thus, the present work aimed to analyze the sintering behavior of the composite powder of copper (Cu) reinforced with tungsten carbide (WC) produced through high energy milling (HEM). The MAE of powders with Cu - 10%WC composition was carried out in humid environment at 400 rpm for 2, 10 and 20 hours, using a mass ratio of powder to balls of 1:4. The powders were compacted in a unidirectional press at 150 MPa and the sintering behavior was studied using a dilatometer, at a temperature of 900°C with an isotherm of 1 hour. In this work, a study was carried out of the effect of high-energy grinding in the Cu-WC sintering process, through the sintering, microstructure and Vickers microhardness curves. The sintering curves showed that the green compacts of the powders processed for a longer milling time initially undergo a large expansion, up to 750°C. After that, a greater contraction is observed, indicating a predominance of the diffusion mechanism during the sintering process from this temperature onwards. Samples sintered after 10 hours showed better distribution and impregnation of tungsten carbide in the copper matrix. The microhardness was higher for the longest milling time, 20h, due to the greater refinement of the microstructure. Therefore, for longer grinding times, we have a greater atomic diffusion for the sintering process, a more homogeneous microstructure and a greater microhardness. Universidade Federal do Rio Grande do Norte Os materiais compósitos vêm sendo produzidos em larga escala nos últimos anos devido a busca por um produto com propriedades distintas para uso em diferentes campos de aplicação. Os compósitos gerados a partir de uma matriz de cobre e reforçado com um material cerâmico e refratário apresentam importante funcionalidade nas suas várias aplicações em condutores elétricos e dissipadores de calor. Desse modo, o presente trabalho teve como objetivo, analisar o comportamento de sinterização do pó compósito de cobre (Cu) reforçado com carbeto de tungstênio (WC) produzido por meio da moagem de alta energia (MAE). A MAE dos pós com composição de Cu - 10%WC foi realizada em meio úmido a 400 rpm durante 2,10 e 20 horas, utilizando uma razão em massa de pó para bolas de 1:4. Os pós foram compactados em uma prensa unidirecional a 150 MPa e o comportamento de sinterização foi estudado através de um dilatômetro, na temperatura 900°C com isoterma de 1 hora. Neste trabalho foi realizado um estudo do efeito da moagem de alta energia, no processo de sinterização do Cu-WC, através das curvas de sinterização, microestrutura e microdureza Vickers. As curvas de sinterização mostraram que os compactos verdes dos pós processados por um maior tempo de moagem, sofrem inicialmente uma grande expansão, até 750°C. Após isso, observa-se uma maior contração, indicando uma predominância do mecanismo de difusão durante o processo de sinterização a partir desta temperatura. As amostras sinterizadas a partir de 10 horas, apresentaram uma melhor distribuição e impregnação do carbeto do tungstênio na matriz de cobre. A microdureza foi maior para o tempo de moagem mais longo, 20h, devido o maior refinamento da microestrutura. Portanto, para maiores tempos de moagem, temos uma maior difusão atômica para o processo de sinterização, uma microestrutura mais homogênea e uma maior microdureza. 2022-12-28T11:56:48Z 2022-12-28T11:56:48Z 2022-12-19 bachelorThesis MARQUES, Anderson Costa. Estudo das curvas de sinterização, microestrutura e microdureza do compósito de Cu-WC. 2022. 67 f. Trabalho de Conclusão de Curso (Graduação em Engenharia de Materiais) - Departamento de Engenharia de Materiais, Universidade Federal do Rio Grande do Norte, Natal, 2022. https://repositorio.ufrn.br/handle/123456789/50725 pt_BR Attribution-NoDerivs 3.0 Brazil http://creativecommons.org/licenses/by-nd/3.0/br/ application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN Engenharia de Materiais

Registros relacionados