Pseudo-composito de poli (óxido de etileno), alginato de sódio e perclorato de lítio: estudo cinético

With the technological advance, there was also an increase in the technological demand in search of better and cheaper materials, mainly in the area of electrochemistry in the search and construction of polymeric conductors. This work explores the solution of a polymeric mixture through a physical m...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Oliveira, Rafael Sávio Ribeiro de
Outros Autores: Cavalcante, Maria Gorette
Formato: bachelorThesis
Idioma:pt_BR
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
Química
Cinética de decomposição
Alginato de sódio
Pseudo-compósitos
Poli (óxido de etileno)
Endereço do item:https://repositorio.ufrn.br/handle/123456789/46747
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-46747
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language pt_BR
topic Química
Cinética de decomposição
Alginato de sódio
Pseudo-compósitos
Poli (óxido de etileno)
spellingShingle Química
Cinética de decomposição
Alginato de sódio
Pseudo-compósitos
Poli (óxido de etileno)
Oliveira, Rafael Sávio Ribeiro de
Pseudo-composito de poli (óxido de etileno), alginato de sódio e perclorato de lítio: estudo cinético
description With the technological advance, there was also an increase in the technological demand in search of better and cheaper materials, mainly in the area of electrochemistry in the search and construction of polymeric conductors. This work explores the solution of a polymeric mixture through a physical mixture, with the addition of a salt. These were the pseudo-composites obtained by mixing the semicrystalline polymer poly (ethylene oxide) with the amorphous polymer sodium alginate in different POE/NaAlg ratios, with the addition of lithium perchlorate salt as a doping agent in a fixed amount, which were named: 20/80, 40/60, 60/40 and 80/20. In the characterization of the samples, in powder form, it was used X-ray diffractometry (XRD), spectroscopy in the infrared region with Fourier transformed (FT-IR) and thermogravimetry and its derivative (TG and DTG). The diffractograms of the samples show a shift to values in 2θ of the highest intensity peaks when compared to the diffractogram of the pure lithium perchlorate salt, with the 60/40 sample showing the highest values of shift in relation to the other samples. The IR-FT spectrum for the 60/40 sample revealed bands at: 〖1084 cm〗^(-1), 〖1028 cm〗^(-1) and 〖950 cm〗^(-1) more intense. The TG/DTG curves of the pseudo-composite show the decomposition temperature ranges of both sodium alginate and POE, revealing for the 60/40 sample a widening of the temperature range of the main mass loss. From the data obtained from the thermal analysis, it was possible to carry out a kinetic study, using the Horowitz-Metzger Method, to obtain thermodynamic parameters such as: activation energy, pre-exponential factor or frequency of collisions, enthalpy, entropy and Gibbs free energy.
author2 Cavalcante, Maria Gorette
author_facet Cavalcante, Maria Gorette
Oliveira, Rafael Sávio Ribeiro de
format bachelorThesis
author Oliveira, Rafael Sávio Ribeiro de
author_sort Oliveira, Rafael Sávio Ribeiro de
title Pseudo-composito de poli (óxido de etileno), alginato de sódio e perclorato de lítio: estudo cinético
title_short Pseudo-composito de poli (óxido de etileno), alginato de sódio e perclorato de lítio: estudo cinético
title_full Pseudo-composito de poli (óxido de etileno), alginato de sódio e perclorato de lítio: estudo cinético
title_fullStr Pseudo-composito de poli (óxido de etileno), alginato de sódio e perclorato de lítio: estudo cinético
title_full_unstemmed Pseudo-composito de poli (óxido de etileno), alginato de sódio e perclorato de lítio: estudo cinético
title_sort pseudo-composito de poli (óxido de etileno), alginato de sódio e perclorato de lítio: estudo cinético
publisher Universidade Federal do Rio Grande do Norte
publishDate 2022
url https://repositorio.ufrn.br/handle/123456789/46747
work_keys_str_mv AT oliveirarafaelsavioribeirode pseudocompositodepolioxidodeetilenoalginatodesodioepercloratodelitioestudocinetico
_version_ 1773959654419726336
spelling ri-123456789-467472023-05-22T16:55:13Z Pseudo-composito de poli (óxido de etileno), alginato de sódio e perclorato de lítio: estudo cinético Oliveira, Rafael Sávio Ribeiro de Cavalcante, Maria Gorette Barroso, Marcia Teixeira http://lattes.cnpq.br/4891201029271910 Silva, Djalma Ribeiro da http://lattes.cnpq.br/2791074318745945 Química Cinética de decomposição Alginato de sódio Pseudo-compósitos Poli (óxido de etileno) With the technological advance, there was also an increase in the technological demand in search of better and cheaper materials, mainly in the area of electrochemistry in the search and construction of polymeric conductors. This work explores the solution of a polymeric mixture through a physical mixture, with the addition of a salt. These were the pseudo-composites obtained by mixing the semicrystalline polymer poly (ethylene oxide) with the amorphous polymer sodium alginate in different POE/NaAlg ratios, with the addition of lithium perchlorate salt as a doping agent in a fixed amount, which were named: 20/80, 40/60, 60/40 and 80/20. In the characterization of the samples, in powder form, it was used X-ray diffractometry (XRD), spectroscopy in the infrared region with Fourier transformed (FT-IR) and thermogravimetry and its derivative (TG and DTG). The diffractograms of the samples show a shift to values in 2θ of the highest intensity peaks when compared to the diffractogram of the pure lithium perchlorate salt, with the 60/40 sample showing the highest values of shift in relation to the other samples. The IR-FT spectrum for the 60/40 sample revealed bands at: 〖1084 cm〗^(-1), 〖1028 cm〗^(-1) and 〖950 cm〗^(-1) more intense. The TG/DTG curves of the pseudo-composite show the decomposition temperature ranges of both sodium alginate and POE, revealing for the 60/40 sample a widening of the temperature range of the main mass loss. From the data obtained from the thermal analysis, it was possible to carry out a kinetic study, using the Horowitz-Metzger Method, to obtain thermodynamic parameters such as: activation energy, pre-exponential factor or frequency of collisions, enthalpy, entropy and Gibbs free energy. Com o avanço tecnológico, houve também o aumento da demanda tecnológica à procura por materiais melhores e mais baratos, principalmente na área de eletroquímica na busca e fabricação de matérias poliméricos condutores. Pensando nisso, este trabalho explora a obtenção de uma blenda polimérica através de uma mistura física, com adição de um sal. Dessa foram os obtidos pseudo-compósitos através da mistura do polímero semicristalino poli (óxido de etileno) com o polímero amorfo alginato de sódio em diferentes razões POE/NaAlg, com a adição do sal perclorato de lítio como agente dopante em quantidade fixa, os quais foram denominados: 20/80, 40/60, 60/40 e 80/20. Na caracterização das amostras, em forma de pó, fez-se uso da difratometria de raios X (DRX), da espectroscopia na região do infravermelho com transformada de Fourier (IR-FT) e da termogravimetria e sua derivada (TG e DTG). Os difratogramas das amostras apresentam um deslocamento para valores em 2θ dos picos de maior intensidade quando comparadas ao difratograma do sal perclorato de lítio puro, com a amostra 60/40 apresentando os maiores valores de deslocamento em relação as outras amostras. O espectro de IR-FT para a amostra 60/40 revelou bandas em: 〖1084 cm〗^(-1), 〖1028 cm〗^(-1) e 〖950 cm〗^(-1) mais intensas. As curvas de TG/DTG do pseudo-compósito mostram as faixas de temperatura de decomposição tanto do alginato de sódio quanto do POE, revelando para a amostra 60/40 um alargamento do intervalo de temperatura da principal perda de massa. A partir dos dados obtidos da análise térmica, foi possível realizar um estudo cinético, utilizando-se o Método Horowitz-Metzger, para se obter parâmetros termodinâmicos como: energia de ativação, fator pré-exponencial ou frequência de colisões, entalpia, entropia e energia livre de Gibbs. 2022-03-31T11:24:34Z 2022-03-31T11:24:34Z 2022-02-17 bachelorThesis OLIVEIRA, Rafael Sávio Ribeiro de. PSEUDO-COMPÓSITOS DE POLI (ÓXIDO DE ETILENO), ALGINATO DE SÓDIO E PERCLORATO DE LÍTIO: ESTUDO CINÉTICO. 2021. 33 f. TCC (Graduação) - Curso de Química Bacharelado, Universidade Federal do Rio Grande do Norte, Natal, 2022. https://repositorio.ufrn.br/handle/123456789/46747 pt_BR Attribution-NonCommercial-NoDerivs 3.0 Brazil http://creativecommons.org/licenses/by-nc-nd/3.0/br/ application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN Química Bacharelado Instituto de Química

Registros relacionados