Análise da transformação martensítica induzida por deformação em aços com efeito TRIP
In pursuit of advanced automotive solutions, high strength steels (AHSS, High Strength Steels) have been improved to replace advanced high strength steels as they can enhance and improve the safety of mechanical vehicles. Among the AHSS, TRIP (Transformation Induced Plasticity) steels stand out,...
Na minha lista:
| Autor principal: | |
|---|---|
| Outros Autores: | |
| Formato: | bachelorThesis |
| Idioma: | pt_BR |
| Publicado em: |
Universidade Federal do Rio Grande do Norte
|
| Assuntos: | |
| Endereço do item: | https://repositorio.ufrn.br/handle/123456789/46297 |
| Tags: |
Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
|
| id |
ri-123456789-46297 |
|---|---|
| record_format |
dspace |
| institution |
Repositório Institucional |
| collection |
RI - UFRN |
| language |
pt_BR |
| topic |
Aços TRIP Transformação de fase Propriedades mecânicas Dureza Vickers Microestrutura TRIP Steels Phase transformation Mechanical properties Vickers hardness Microstructure |
| spellingShingle |
Aços TRIP Transformação de fase Propriedades mecânicas Dureza Vickers Microestrutura TRIP Steels Phase transformation Mechanical properties Vickers hardness Microstructure Mares Júnior, João Batista Análise da transformação martensítica induzida por deformação em aços com efeito TRIP |
| description |
In pursuit of advanced automotive solutions, high strength steels (AHSS, High
Strength Steels) have been improved to replace advanced high strength steels as
they can enhance and improve the safety of mechanical vehicles. Among the AHSS,
TRIP (Transformation Induced Plasticity) steels stand out, which propose a
microstructure consisting of ferritic and bainitic grains with austenite islands. One of
the main characteristics of TRIP steels is the occurrence of martensitic
transformation induced by plastic deformation, promoting high coefficient of work
hardening, high plasticity and toughness. In this work, two samples of different
classes of cold rolled TRIP steels were used, with 690 and 780 MPa of resistance
limit with approximately 1.5 mm of thickness. As they were manually bent at 90° with
the aid of a vise and later embedded and metallographically prepared to be made via
EBSD (Electron Backscattering Diffraction). They were carried out along the cross
section of the sample in the deformed and long region of the bend, as a comparative
basis of the microstructural evolution of the material as a function of deformation. It
was possible to study the behavior of the microstructure in different functions,
becoming an applied training model. From the EBSD formation formation variations,
it was possible to evaluate the diversity of plastic formation variations, in addition to
the evaluation of the plastic formation distribution, in addition to the evaluation of the
microstructure formation distribution. Where it was possible to analyze it after the
transformation of the austenite of metastable plasticity in increasing the mechanical
properties of this material, characteristic of this great importance in the control of this
class of steels. |
| author2 |
Castro, Nicolau Apoena |
| author_facet |
Castro, Nicolau Apoena Mares Júnior, João Batista |
| format |
bachelorThesis |
| author |
Mares Júnior, João Batista |
| author_sort |
Mares Júnior, João Batista |
| title |
Análise da transformação martensítica induzida por deformação em aços com efeito TRIP |
| title_short |
Análise da transformação martensítica induzida por deformação em aços com efeito TRIP |
| title_full |
Análise da transformação martensítica induzida por deformação em aços com efeito TRIP |
| title_fullStr |
Análise da transformação martensítica induzida por deformação em aços com efeito TRIP |
| title_full_unstemmed |
Análise da transformação martensítica induzida por deformação em aços com efeito TRIP |
| title_sort |
análise da transformação martensítica induzida por deformação em aços com efeito trip |
| publisher |
Universidade Federal do Rio Grande do Norte |
| publishDate |
2022 |
| url |
https://repositorio.ufrn.br/handle/123456789/46297 |
| work_keys_str_mv |
AT maresjuniorjoaobatista analisedatransformacaomartensiticainduzidapordeformacaoemacoscomefeitotrip |
| _version_ |
1773965021322149888 |
| spelling |
ri-123456789-462972022-02-24T17:21:49Z Análise da transformação martensítica induzida por deformação em aços com efeito TRIP Mares Júnior, João Batista Castro, Nicolau Apoena Rodrigues, Flávio José Saraiva Ferreira, Jetson Lemos Peres, Maurício Mhirdaui Aços TRIP Transformação de fase Propriedades mecânicas Dureza Vickers Microestrutura TRIP Steels Phase transformation Mechanical properties Vickers hardness Microstructure In pursuit of advanced automotive solutions, high strength steels (AHSS, High Strength Steels) have been improved to replace advanced high strength steels as they can enhance and improve the safety of mechanical vehicles. Among the AHSS, TRIP (Transformation Induced Plasticity) steels stand out, which propose a microstructure consisting of ferritic and bainitic grains with austenite islands. One of the main characteristics of TRIP steels is the occurrence of martensitic transformation induced by plastic deformation, promoting high coefficient of work hardening, high plasticity and toughness. In this work, two samples of different classes of cold rolled TRIP steels were used, with 690 and 780 MPa of resistance limit with approximately 1.5 mm of thickness. As they were manually bent at 90° with the aid of a vise and later embedded and metallographically prepared to be made via EBSD (Electron Backscattering Diffraction). They were carried out along the cross section of the sample in the deformed and long region of the bend, as a comparative basis of the microstructural evolution of the material as a function of deformation. It was possible to study the behavior of the microstructure in different functions, becoming an applied training model. From the EBSD formation formation variations, it was possible to evaluate the diversity of plastic formation variations, in addition to the evaluation of the plastic formation distribution, in addition to the evaluation of the microstructure formation distribution. Where it was possible to analyze it after the transformation of the austenite of metastable plasticity in increasing the mechanical properties of this material, characteristic of this great importance in the control of this class of steels. Em busca de soluções automobilísticas, os aços avançados de alta resistência (AHSS, Advanced High Strength Steels) foram desenvolvidos para substituírem os aços convencionais, já que eles apresentam melhores propriedades mecânicas, fornecendo maior eficiência e segurança aos veículos. Dentre os AHSS destacam-se os aços TRIP (Transformation Induced Plasticity), que apresentam microestrutura constituída por grãos ferríticos e bainíticos com ilhas de austenita. Uma das principais características dos aços TRIP é a ocorrência de transformação martensítica induzida pela deformação plástica, promovendo alto coeficiente de encruamento, altas plasticidade e tenacidade. Neste trabalho foram utilizadas duas amostras de diferentes classes de aço TRIP laminadas a frio, com 690 e 780 MPa de limite de resistência, com 1,5mm de espessura. As amostras foram dobradas manualmente a 90° com auxílio de uma morsa e posteriormente embutidas e preparadas metalograficamente para serem analisadas via EBSD (Electron Backscattering Diffraction). Foram realizadas análises ao longo da seção transversal da amostra na região deformada e longe da dobra, como base comparativa da evolução microestrutural do material em função da deformação plástica. Foi possível estudar o comportamento da microestrutura em regiões submetidas a diferentes níveis de tração e de compressão, dado o modo de deformação aplicado. A partir das análises via EBSD foi possível avaliar a fração de austenita presente nas diferentes regiões de deformação, além da avaliação da distribuição da deformação plástica ao longo da microestrutura dos aços. Foi possível analisar, após a deformação plástica, a transformação da austenita retida metaestável em martensita, aumentando assim as propriedades mecânicas deste material, característica essa de grande importância no controle de qualidade dessa classe de aços. 2022-02-24T17:21:48Z 2022-02-24T17:21:48Z 2022-02-15 bachelorThesis MARES JÚNIOR, João Batista. Análise da transformação martensítica induzida por deformação em aços com efeito TRIP. 2022. 71 f. Trabalho de Conclusão de Curso (Graduação em Engenharia de Materiais) - Centro de Tecnologia, Universidade Federal do Rio Grande do Norte, Natal, 2022. https://repositorio.ufrn.br/handle/123456789/46297 pt_BR application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN Engenharia de Materiais Departamento de Engenharia de Materiais |