Síntese e caracterização de ferrita de níquel e níquel-zinco pelo método de polimerização de complexos
Nickel-zinc ferrites are ferrimagnetic ceramic materials with cubic spinel type crystal structure, space group Fd3m belonging to being a solid solution composition of NiO, ZnO and Fe2O3. The complex polymerization method has enormous potential for obtaining magnetic ceramics, because it is a simple...
Na minha lista:
| Principais autores: | , , , , , , , , |
|---|---|
| Formato: | article |
| Idioma: | pt_BR |
| Publicado em: |
69° Congresso Anual da ABM - Internacional
|
| Assuntos: | |
| Endereço do item: | https://repositorio.ufrn.br/handle/123456789/45733 |
| Tags: |
Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
|
| Resumo: | Nickel-zinc ferrites are ferrimagnetic ceramic materials with cubic spinel type crystal structure, space group Fd3m belonging to being a solid solution composition of NiO, ZnO and Fe2O3. The complex polymerization method has enormous potential for obtaining magnetic ceramics, because it is a simple process, that originates from materials with high purity, which leads to obtaining powders with high chemical homogeneity and high surface area. This work aims to evaluate the structural and morphological characteristics of ferrites Ni0,25Zn0,75Fe2O4 and NiFe2O4 obtained by polymerization complex method. The solution was subjected to a final temperature of 120°C until the formation of the resin pyrolysed at a temperature of 350°C for 2 hours and calcined at 500°C for 2 hours. The resulting powders were characterized by X-ray diffraction (XRD), thermal analysis (TG/ DSC) and scanning electron microscopy (SEM). The results of XRD showed the formation of two compositions majority of ferrite phase. The results of SEM micrographs showed the formation of agglomerated particles with longitudinal plates to both compositions being important microstructural characteristics for magnetic application. The method of polymerization of complexes appeared as a promising method to obtain ceramic powders of nickel ferrite and nickel-zinc alloy for magnetic application. |
|---|