Caracterização de filmes de poliéster modificados por plasma de O2 a baixa pressão

A polyester film has a vast application field, due some properties that are inherent of this kind of material such as, good mechanical resistance, chemical resistance to acids and bases and low production cost. However, this material has some limitations as low superficial tension, flat surface,...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Principais autores: Costa, Thércio Henrique de Carvalho, Feitor, Michelle Cequeira, Alves Junior, Clodomiro, Bezerra, Clovis de Medeiros
Formato: article
Idioma:pt_BR
Publicado em: Universidade Federal do Rio de Janeiro
Assuntos:
Tensão superficial
Plasma
Molhabilidade
Ângulo de contato
Poliéster
Endereço do item:https://repositorio.ufrn.br/handle/123456789/45223
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-45223
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language pt_BR
topic Tensão superficial
Plasma
Molhabilidade
Ângulo de contato
Poliéster
spellingShingle Tensão superficial
Plasma
Molhabilidade
Ângulo de contato
Poliéster
Costa, Thércio Henrique de Carvalho
Feitor, Michelle Cequeira
Alves Junior, Clodomiro
Bezerra, Clovis de Medeiros
Caracterização de filmes de poliéster modificados por plasma de O2 a baixa pressão
description A polyester film has a vast application field, due some properties that are inherent of this kind of material such as, good mechanical resistance, chemical resistance to acids and bases and low production cost. However, this material has some limitations as low superficial tension, flat surface, low affinity to dyers, and poor adhesion which impede the use of the same ones for some finality as good wettability. Among the existent techniques to increase the superficial tension, plasma as energy source is the more promising technique, because of their versatility and for not polluting the environment. Then, due to its good acceptance, polyester films were treated with oxygen plasma varying the treatment time from 10 to 60 min with an increase of 10 min to each subsequent treatment. After plasma treatment the samples were characterized by contact angle, surface tension, Raman spectroscopy, Infrared attenuated total reflection (IR ATR) and atomic force microscopy, with the aim to study the wettability increase of treated polyester films as its variables. The plasma technique is very efficient in modifying polyester films, and this is true because all treated films showed a wettability increase and none significant variation was observed at ageing time plasma treated samples. So, plasma treatment contributed for wettability increase through surface functional groups implantation as through creation of roughness at the surface plasma treated samples
format article
author Costa, Thércio Henrique de Carvalho
Feitor, Michelle Cequeira
Alves Junior, Clodomiro
Bezerra, Clovis de Medeiros
author_facet Costa, Thércio Henrique de Carvalho
Feitor, Michelle Cequeira
Alves Junior, Clodomiro
Bezerra, Clovis de Medeiros
author_sort Costa, Thércio Henrique de Carvalho
title Caracterização de filmes de poliéster modificados por plasma de O2 a baixa pressão
title_short Caracterização de filmes de poliéster modificados por plasma de O2 a baixa pressão
title_full Caracterização de filmes de poliéster modificados por plasma de O2 a baixa pressão
title_fullStr Caracterização de filmes de poliéster modificados por plasma de O2 a baixa pressão
title_full_unstemmed Caracterização de filmes de poliéster modificados por plasma de O2 a baixa pressão
title_sort caracterização de filmes de poliéster modificados por plasma de o2 a baixa pressão
publisher Universidade Federal do Rio de Janeiro
publishDate 2021
url https://repositorio.ufrn.br/handle/123456789/45223
work_keys_str_mv AT costatherciohenriquedecarvalho caracterizacaodefilmesdepoliestermodificadosporplasmadeo2abaixapressao
AT feitormichellecequeira caracterizacaodefilmesdepoliestermodificadosporplasmadeo2abaixapressao
AT alvesjuniorclodomiro caracterizacaodefilmesdepoliestermodificadosporplasmadeo2abaixapressao
AT bezerraclovisdemedeiros caracterizacaodefilmesdepoliestermodificadosporplasmadeo2abaixapressao
_version_ 1773960427877695488
spelling ri-123456789-452232021-12-20T18:12:02Z Caracterização de filmes de poliéster modificados por plasma de O2 a baixa pressão Costa, Thércio Henrique de Carvalho Feitor, Michelle Cequeira Alves Junior, Clodomiro Bezerra, Clovis de Medeiros Tensão superficial Plasma Molhabilidade Ângulo de contato Poliéster A polyester film has a vast application field, due some properties that are inherent of this kind of material such as, good mechanical resistance, chemical resistance to acids and bases and low production cost. However, this material has some limitations as low superficial tension, flat surface, low affinity to dyers, and poor adhesion which impede the use of the same ones for some finality as good wettability. Among the existent techniques to increase the superficial tension, plasma as energy source is the more promising technique, because of their versatility and for not polluting the environment. Then, due to its good acceptance, polyester films were treated with oxygen plasma varying the treatment time from 10 to 60 min with an increase of 10 min to each subsequent treatment. After plasma treatment the samples were characterized by contact angle, surface tension, Raman spectroscopy, Infrared attenuated total reflection (IR ATR) and atomic force microscopy, with the aim to study the wettability increase of treated polyester films as its variables. The plasma technique is very efficient in modifying polyester films, and this is true because all treated films showed a wettability increase and none significant variation was observed at ageing time plasma treated samples. So, plasma treatment contributed for wettability increase through surface functional groups implantation as through creation of roughness at the surface plasma treated samples Filmes de poliéster possuem um vasto campo de aplicação, devido algumas propriedades que são inerentes desse tipo de material, tais como boa resistência mecânica, resistência química a ácidos e bases e baixo custo de produção. Entretanto possuem limitações, como baixa tensão superficial, baixa rugosa, pouca afinidade com corantes, e pouca adesão, que impedem o uso dos mesmos para algumas finalidades principalmente quando esse uso requer que o material possua uma boa molhabilidade. Dentre as varias técnicas existentes para aumentar a tensão superficial, as técnicas que utilizam o plasma, como fonte energética, são as mais promissoras pela versatilidade e por não apresentar agentes nocivos ao meio. Então, tendo em vista a boa aceitabilidade do uso do plasma em materiais poliméricos, trataram-se filmes de poliéster usando plasma com atmosfera gasosa de oxigênio variando-se o tempo de tratamento de 10 - 60 min com incremento de 10 min a cada tratamento subseqüente. Após o tratamento por plasma as amostras foram caracterizadas por medidas de ângulo de contato, tensão superficial, espectroscopia Raman, Espectroscopia de infravermelho de reflexão total atenuada (IR-ATR), e microscopia de força atômica (AFM), onde foi caracterizado o aumento na molhabilidade dos filmes tratados por plasma bem como as variáveis que contribuíram para tal efeito. A técnica de plasma mostrou-se bastante eficiente na modificação de filmes de poliéster, uma vez que se obteve aumento na molhabilidade de todos os filmes tratados e sem nenhuma variação significativa com relação ao tempo de exposição das amostras pelo plasma, o que leva a propor que o tratamento por plasma tanto contribuiu para o aumento da molhabilidade através da implementação de grupos funcionais na superfície dos mesmos como com a criação de rugosidade superficial nas amostras 2021-12-07T14:44:35Z 2021-12-07T14:44:35Z 2008-05-12 article COSTA, Thercio Henrique de Carvalho; FEITOR, Michelle Cequeira; ALVES JUNIOR, Clodomiro; BEZERRA, Clovis de Medeiros. Caracterização de filmes de poliéster modificados por plasma de O2 a baixa pressão. Matéria (Rio de Janeiro), [S. l.], v. 13, n. 1, p. 65-76, mar. 2008. FapUNIFESP (SciELO). Disponível em: https://www.scielo.br/j/rmat/a/bjRNZfmhxKJ6PSwjw99NLbn/?lang=pt. Acesso em: 04 dez. 2021. DOI: http://dx.doi.org/10.1590/s1517-70762008000100008 1517-7076 https://repositorio.ufrn.br/handle/123456789/45223 10.1590/S1517-70762008000100008 pt_BR Attribution 4.0 Brazil https://creativecommons.org/licenses/by-nc/4.0/ application/pdf Universidade Federal do Rio de Janeiro

Registros relacionados