Estudo sobre a influência do tempo de polimento por imersão em sílica coloidal nas análises via EBSD de um aço TRIP laminado a frio

Steels assisted by the TRIP effect have stood out due to their multiphase microstructure, which offers a combination of properties that enables the development of automotive parts with excellent mechanical properties. This improvement in properties occurs through the transformation of austenite reta...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Carvalho, Cássia Carla de
Outros Autores: Castro, Nicolau Apoena
Formato: bachelorThesis
Idioma:pt_BR
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
Aço TRIP
EBSD
Austenita retida
Polimento fino
Endereço do item:https://repositorio.ufrn.br/handle/123456789/40383
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-40383
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language pt_BR
topic Aço TRIP
EBSD
Austenita retida
Polimento fino
spellingShingle Aço TRIP
EBSD
Austenita retida
Polimento fino
Carvalho, Cássia Carla de
Estudo sobre a influência do tempo de polimento por imersão em sílica coloidal nas análises via EBSD de um aço TRIP laminado a frio
description Steels assisted by the TRIP effect have stood out due to their multiphase microstructure, which offers a combination of properties that enables the development of automotive parts with excellent mechanical properties. This improvement in properties occurs through the transformation of austenite retained in martensite during plastic deformation. Therefore, the fraction of austenite retained in the steel directly influences its properties, making the microstructural analysis of the steel become one of the most important steps for the development of automotive steels and one of the techniques widely used for the quantification of phases is the EBSD (Electron Backscattering Diffraction). This technique requires well-polished samples for an effective removal of the hardened layer during the preparation steps, thus avoiding obtaining false values in the quantification of the phases. A technique that is efficient in removing the hardened layer is fine polishing on colloidal silica. Therefore, this work aims to study the influence of the polishing time by immersion in colloidal silica on the results of analyzes via EBSD of a cold-rolled TRIP steel. To carry out this work, a TRIP 780 steel was used, in which, after the initial sample preparation steps, polishing was performed on colloidal silica for different times, between 1 and 12 hours. Analyzes were performed via EBSD, in order to follow the evolution of the results obtained with the increase of the polishing time. The results obtained were represented by means of phase maps and crystallographic orientations and by the parameters IQ (Image Quality), KAM (Kernel Average Misorientation) and percentage of phases. Analyzing the behavior of the maps, the IQ and the phase quantification, an increase in the percentage of austenite and the average IQ is noted with the increase in the polishing time. The values obtained in the KAM show a decrease as the polishing time increases. With the T-Student test, it was possible to affirm with 95% of significance that the polishing time presents a significant difference in the mean values of IQ and KAM only up to 4 hours of polishing, so that for longer times there is no more influence on the results evaluated, indicating that this polishing time is sufficient to remove the superficial layers of the samples that have undergone transformations due to the metallographic preparation steps that preceded the final polishing in colloidal silica.
author2 Castro, Nicolau Apoena
author_facet Castro, Nicolau Apoena
Carvalho, Cássia Carla de
format bachelorThesis
author Carvalho, Cássia Carla de
author_sort Carvalho, Cássia Carla de
title Estudo sobre a influência do tempo de polimento por imersão em sílica coloidal nas análises via EBSD de um aço TRIP laminado a frio
title_short Estudo sobre a influência do tempo de polimento por imersão em sílica coloidal nas análises via EBSD de um aço TRIP laminado a frio
title_full Estudo sobre a influência do tempo de polimento por imersão em sílica coloidal nas análises via EBSD de um aço TRIP laminado a frio
title_fullStr Estudo sobre a influência do tempo de polimento por imersão em sílica coloidal nas análises via EBSD de um aço TRIP laminado a frio
title_full_unstemmed Estudo sobre a influência do tempo de polimento por imersão em sílica coloidal nas análises via EBSD de um aço TRIP laminado a frio
title_sort estudo sobre a influência do tempo de polimento por imersão em sílica coloidal nas análises via ebsd de um aço trip laminado a frio
publisher Universidade Federal do Rio Grande do Norte
publishDate 2021
url https://repositorio.ufrn.br/handle/123456789/40383
work_keys_str_mv AT carvalhocassiacarlade estudosobreainfluenciadotempodepolimentoporimersaoemsilicacoloidalnasanalisesviaebsddeumacotriplaminadoafrio
_version_ 1797696597695397888
spelling ri-123456789-403832024-03-19T04:04:20Z Estudo sobre a influência do tempo de polimento por imersão em sílica coloidal nas análises via EBSD de um aço TRIP laminado a frio Carvalho, Cássia Carla de Castro, Nicolau Apoena Flávio José Saraiva Rodrigues Ferreira, Jetson Lemos Lima, Lindolpho Sales Dantas da Costa Aço TRIP EBSD Austenita retida Polimento fino Steels assisted by the TRIP effect have stood out due to their multiphase microstructure, which offers a combination of properties that enables the development of automotive parts with excellent mechanical properties. This improvement in properties occurs through the transformation of austenite retained in martensite during plastic deformation. Therefore, the fraction of austenite retained in the steel directly influences its properties, making the microstructural analysis of the steel become one of the most important steps for the development of automotive steels and one of the techniques widely used for the quantification of phases is the EBSD (Electron Backscattering Diffraction). This technique requires well-polished samples for an effective removal of the hardened layer during the preparation steps, thus avoiding obtaining false values in the quantification of the phases. A technique that is efficient in removing the hardened layer is fine polishing on colloidal silica. Therefore, this work aims to study the influence of the polishing time by immersion in colloidal silica on the results of analyzes via EBSD of a cold-rolled TRIP steel. To carry out this work, a TRIP 780 steel was used, in which, after the initial sample preparation steps, polishing was performed on colloidal silica for different times, between 1 and 12 hours. Analyzes were performed via EBSD, in order to follow the evolution of the results obtained with the increase of the polishing time. The results obtained were represented by means of phase maps and crystallographic orientations and by the parameters IQ (Image Quality), KAM (Kernel Average Misorientation) and percentage of phases. Analyzing the behavior of the maps, the IQ and the phase quantification, an increase in the percentage of austenite and the average IQ is noted with the increase in the polishing time. The values obtained in the KAM show a decrease as the polishing time increases. With the T-Student test, it was possible to affirm with 95% of significance that the polishing time presents a significant difference in the mean values of IQ and KAM only up to 4 hours of polishing, so that for longer times there is no more influence on the results evaluated, indicating that this polishing time is sufficient to remove the superficial layers of the samples that have undergone transformations due to the metallographic preparation steps that preceded the final polishing in colloidal silica. Aços assistidos pelo efeito TRIP têm se destacado devido a sua microestrutura multifásica, a qual oferece uma combinação de propriedades que possibilita o desenvolvimento de peças automotivas com ótimas propriedades mecânicas. Essa melhoria das propriedades ocorre por meio da transformação da austenita retida em martensita durante a deformação plástica. Logo, a fração de austenita retida no aço influencia diretamente nas propriedades do mesmo, fazendo com que a análise microestrutural do aço se torne uma das etapas mais importantes para o desenvolvimento dos aços automotivos e umas das técnicas bastante utilizadas para a quantificação de fases é o EBSD (Electron Backscattering Diffraction). Esta técnica requer amostras bem polidas para uma efetiva remoção da camada encruada durante as etapas da preparação, evitando assim a obtenção de falsos valores na quantificação das fases. Uma técnica que se mostra eficiente na remoção da camada encruada é o polimento fino em sílica coloidal. Logo, este trabalho tem como objetivo estudar a influência do tempo polimento por imersão em sílica coloidal nos resultados das análises via EBSD de um aço TRIP laminado a frio. Para realização deste trabalho, foi utilizado um aço TRIP 780, no qual, após as etapas iniciais de preparação de amostra, foi realizado polimento em sílica coloidal por diferentes tempos, entre 1 e 12 horas. Foram realizadas análises via EBSD, de modo a acompanhar a evolução dos resultados obtidos com o aumento do tempo de polimento. Os resultados obtidos foram representados por meio de mapas de fases e orientações cristalográficas e pelos parâmetros IQ (Image Quality), KAM (Kernel Average Misorientation) e porcentagem de fases. Analisando o comportamento dos mapas, do IQ e da quantificação de fases, nota-se um aumento da porcentagem de austenita e do IQ médio com o aumento do tempo de polimento. Os valores obtidos no KAM apresentam uma diminuição à medida que aumenta o tempo de polimento. Com o teste T-Student, foi possível afirmar com 95% de significância que o tempo de polimento apresenta diferença significativa nos valores médios de IQ e de KAM somente até 4 horas de polimento, de modo que para tempos mais longos não há mais influência nos resultados avaliados, indicando que esse tempo de polimento é suficiente para remover as camadas superficiais das amostras que sofreram transformações devido às etapas de preparação metalográfica que antecederam o polimento final em sílica coloidal. 2023-06-30 2021-04-30T20:08:40Z 2021-09-29T13:23:34Z 2021-04-30T20:08:40Z 2021-03-18 bachelorThesis 20180155803 CARVALHO, Cássia Carla. Estudo sobre a influência do tempo de polimento por imersão em sílica coloidal nas análises via EBSD de um aço TRIP laminado a frio. 2021. 42f. Trabalho de Conclusão de Curso (Graduação em Engenharia de Materiais) - Centro de Tecnologia, Universidade Federal do Rio Grande do Norte, Natal, 2021. https://repositorio.ufrn.br/handle/123456789/40383 pt_BR Attribution-NonCommercial-NoDerivs 3.0 Brazil http://creativecommons.org/licenses/by-nc-nd/3.0/br/ application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN Engenharia de Materiais

Registros relacionados