Visualização microscópica da dinâmica de reação do poli (etileno-co-ácido-metacrílico) (EMAA) sinterizado sobre resina epóxi

The addition of thermoplastics to the thermosetting matrix of composites as an intrinsic self-healing agent aims to reduce maintenance costs and extend the durability of the material overcoming limitations such as mechanical failures and defects arising mainly from the appearance of microcracks d...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Potêncio, Diego José Cavalcanti
Outros Autores: Nascimento, Maria Carolina Burgos Costa do
Formato: bachelorThesis
Idioma:pt_BR
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
Poli (etileno-co-ácido-metacrílico) (EMAA)
Sinterização
Auto-reparo
Compósitos
Resina epóxi
Endereço do item:https://repositorio.ufrn.br/handle/123456789/40348
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-40348
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language pt_BR
topic Poli (etileno-co-ácido-metacrílico) (EMAA)
Sinterização
Auto-reparo
Compósitos
Resina epóxi
spellingShingle Poli (etileno-co-ácido-metacrílico) (EMAA)
Sinterização
Auto-reparo
Compósitos
Resina epóxi
Potêncio, Diego José Cavalcanti
Visualização microscópica da dinâmica de reação do poli (etileno-co-ácido-metacrílico) (EMAA) sinterizado sobre resina epóxi
description The addition of thermoplastics to the thermosetting matrix of composites as an intrinsic self-healing agent aims to reduce maintenance costs and extend the durability of the material overcoming limitations such as mechanical failures and defects arising mainly from the appearance of microcracks during service. One of the limiting challenges for using this mechanism is the lack of knowledge about the efficiency of external stimuli and the detailing of intermolecular interactions that occur internally. In this work, a visualization technique with optical microscopy of hot stage was utilized to analyze the interactions that occur between the thermoplastic poly (ethylene-co-methacrylic acid) (EMAA) and the epoxy resin, focusing on the investigation of the appearance of bubbles. Analyzes of heating of EMMA powder on the epoxy and glass substrate were performed, for temperatures of 130, 150, and 180 °C and EMAA particle sizes of 125 and 355 µm. The data obtained from microscopic images resulted in higher amounts of bubbles for the experiments using the smallest EMAA particle size. The larger grain size of this thermoplastic, 355 µm, contributed to the formation of larger size bubbles. The sintering temperature changes the size of the bubbles although and influence in the growth and decay rates of bubbles number. The comparison between the two utilized substrates proves the formation of water bubbles providing from condensation reactions when the EMAA was sintered on the epoxy resin since it was evident the large increase in total bubbles number at the end of the process when compared to the decay of this number in the sintering done on the glass substrate. The results obtained from this study evidence the reaction dynamics and the bubble formation mechanism, which can be utilized as a tool for planning optimized conditions for repair cycles.
author2 Nascimento, Maria Carolina Burgos Costa do
author_facet Nascimento, Maria Carolina Burgos Costa do
Potêncio, Diego José Cavalcanti
format bachelorThesis
author Potêncio, Diego José Cavalcanti
author_sort Potêncio, Diego José Cavalcanti
title Visualização microscópica da dinâmica de reação do poli (etileno-co-ácido-metacrílico) (EMAA) sinterizado sobre resina epóxi
title_short Visualização microscópica da dinâmica de reação do poli (etileno-co-ácido-metacrílico) (EMAA) sinterizado sobre resina epóxi
title_full Visualização microscópica da dinâmica de reação do poli (etileno-co-ácido-metacrílico) (EMAA) sinterizado sobre resina epóxi
title_fullStr Visualização microscópica da dinâmica de reação do poli (etileno-co-ácido-metacrílico) (EMAA) sinterizado sobre resina epóxi
title_full_unstemmed Visualização microscópica da dinâmica de reação do poli (etileno-co-ácido-metacrílico) (EMAA) sinterizado sobre resina epóxi
title_sort visualização microscópica da dinâmica de reação do poli (etileno-co-ácido-metacrílico) (emaa) sinterizado sobre resina epóxi
publisher Universidade Federal do Rio Grande do Norte
publishDate 2020
url https://repositorio.ufrn.br/handle/123456789/40348
work_keys_str_mv AT potenciodiegojosecavalcanti visualizacaomicroscopicadadinamicadereacaodopolietilenocoacidometacrilicoemaasinterizadosobreresinaepoxi
_version_ 1773959756529008640
spelling ri-123456789-403482023-03-10T19:15:43Z Visualização microscópica da dinâmica de reação do poli (etileno-co-ácido-metacrílico) (EMAA) sinterizado sobre resina epóxi Potêncio, Diego José Cavalcanti Nascimento, Maria Carolina Burgos Costa do Felipe Pedro da Costa Gomes Andrade Neto, Nivaldo Freire de Poli (etileno-co-ácido-metacrílico) (EMAA) Sinterização Auto-reparo Compósitos Resina epóxi The addition of thermoplastics to the thermosetting matrix of composites as an intrinsic self-healing agent aims to reduce maintenance costs and extend the durability of the material overcoming limitations such as mechanical failures and defects arising mainly from the appearance of microcracks during service. One of the limiting challenges for using this mechanism is the lack of knowledge about the efficiency of external stimuli and the detailing of intermolecular interactions that occur internally. In this work, a visualization technique with optical microscopy of hot stage was utilized to analyze the interactions that occur between the thermoplastic poly (ethylene-co-methacrylic acid) (EMAA) and the epoxy resin, focusing on the investigation of the appearance of bubbles. Analyzes of heating of EMMA powder on the epoxy and glass substrate were performed, for temperatures of 130, 150, and 180 °C and EMAA particle sizes of 125 and 355 µm. The data obtained from microscopic images resulted in higher amounts of bubbles for the experiments using the smallest EMAA particle size. The larger grain size of this thermoplastic, 355 µm, contributed to the formation of larger size bubbles. The sintering temperature changes the size of the bubbles although and influence in the growth and decay rates of bubbles number. The comparison between the two utilized substrates proves the formation of water bubbles providing from condensation reactions when the EMAA was sintered on the epoxy resin since it was evident the large increase in total bubbles number at the end of the process when compared to the decay of this number in the sintering done on the glass substrate. The results obtained from this study evidence the reaction dynamics and the bubble formation mechanism, which can be utilized as a tool for planning optimized conditions for repair cycles. A adição de termoplásticos à matriz termofixa de compósitos como agente intrínseco de auto-reparo tem como objetivo reduzir os custos de manutenção e prolongar a vida útil do material superando limitações como falhas mecânicas e defeitos decorrentes principalmente do surgimento de microtrincas durante o serviço. Um dos desafios limitantes para o uso desse mecanismo é a falta de conhecimento sobre a eficiência dos estímulos externos e o detalhamento de interações intermoleculares que ocorrem internamente. Neste trabalho, utilizou-se uma técnica de visualização com microscopia óptica de estágio quente para analisar as interações que ocorrem entre o termoplástico poli (etileno-co-ácido-metacrílico) (EMAA) e a resina epóxi, com foco na investigação do surgimento de bolhas. Foram realizadas análises do aquecimento do pó de EMMA sobre o substrato de epóxi e de vidro para as temperaturas de 130, 150 e 180 °C e granulometrias do EMAA de 125 e 355 µm. Os dados obtidos das imagens microscópicas resultaram em maiores quantidades de bolhas para os experimentos empregando a menor granulometria do EMAA. O maior tamanho de grão deste termoplástico, 355 µm, contribuiu para a formação de bolhas de tamanhos maiores. A temperatura de sinterização altera o tamanho das bolhas e também influencia bastante nas taxas de crescimento e decaimento do número de bolhas. A comparação entre os dois substratos utilizados, comprova a formação de bolhas de água provenientes de reações de condensação quando o EMAA foi sinterizado sobre a resina epóxi, visto que foi evidente o grande crescimento do número total de bolhas ao final do processo quando comparado ao decaimento deste número na sinterização feita sobre o substrato de vidro. Os resultados obtidos a partir deste estudo evidenciam a dinâmica da reação e o mecanismo de formação de bolhas, podendo ser utilizado como ferramenta para o planejamento de condições otimizadas para ciclos de reparo. 2020-12-31T10:53:14Z 2021-09-29T13:22:21Z 2020-12-31T10:53:14Z 2021-09-29T13:22:21Z 2020-12-10 bachelorThesis 20180155705 POTÊNCIO, Diego José Cavalcanti. Visualização microscópica da dinâmica de reação do poli (etileno-co-ácido-metacrílico) (EMAA) sinterizado sobre resina epóxi. 2020. 63 f. Trabalho de Conclusão de Curso (Graduação em Engenharia de Materiais) - Centro de Tecnologia, Departamento de Engenharia de Materiais, Universidade Federal do Rio Grande do Norte, Natal, 2020. https://repositorio.ufrn.br/handle/123456789/40348 pt_BR application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN Engenharia de Materiais

Registros relacionados