Estudo da temperatura de fusão alcalina na síntese de zeólita-A utilizando pó de vidro residual como fonte alternativa

Zeolites are microporous materials due to their structural organization that allow the separation of molecules because of their sizes. For this reason, zeolites are also known as molecular sieves. This group of materials has many industrial applications, such as adsorption, ion exchange of detergent...

ver descrição completa

Na minha lista:

Detalhes bibliográficos
Autor principal:	Dantas, Ercília Regina Silva
Outros Autores:	Melo, Marcus Antônio de Freitas
Formato:	bachelorThesis
Idioma:	pt_BR
Publicado em:	Universidade Federal do Rio Grande do Norte
Assuntos:	Zeólita-A Pó de Vidro Residual Síntese Hidrotérmica Fonte Alternativa Zeolite-A. Synthesis Hydrothermal. Residual Glass Powder Alternative Source Engenharias.
Endereço do item:	https://repositorio.ufrn.br/handle/123456789/38766
Tags:	Adicionar Tag Sem tags, seja o primeiro a adicionar uma tag!

id	ri-123456789-38766
record_format	dspace
institution	Repositório Institucional
collection	RI - UFRN
language	pt_BR
topic	Zeólita-A Pó de Vidro Residual Síntese Hidrotérmica Fonte Alternativa Zeolite-A. Synthesis Hydrothermal. Residual Glass Powder Alternative Source Engenharias.
spellingShingle	Zeólita-A Pó de Vidro Residual Síntese Hidrotérmica Fonte Alternativa Zeolite-A. Synthesis Hydrothermal. Residual Glass Powder Alternative Source Engenharias. Dantas, Ercília Regina Silva Estudo da temperatura de fusão alcalina na síntese de zeólita-A utilizando pó de vidro residual como fonte alternativa
description	Zeolites are microporous materials due to their structural organization that allow the separation of molecules because of their sizes. For this reason, zeolites are also known as molecular sieves. This group of materials has many industrial applications, such as adsorption, ion exchange of detergents, catalysis and so on. The study of zeolites has undergone accelerated growth in the last 60 years, and the development and analysis of different synthesis methods had decisive role. In this work, zeolite A was obtained using alkaline fusion followed by a hydrothermal treatment where the residual glass powder (RGP) was used as source of SiO2 and AlO2. During the synthesis, the parameter evaluated was the alkaline fusion temperature which varied from 250°C to 500°C. The synthesized materials and residual glass powder (RGP) were characterized by chemical analysis using energy dispersive X-ray analysis (EDX), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Based on the EDX result, the RGP was identified as a silica rich material (about 70%). In addition, the diffractograms and micrographs showed an amorphous nature for the RGP. Also, the formation of zeolite-A was observed at 350˚C and 500˚C by the characterization of the synthesized materials. In fact, an secondary formation (zeolite-X) was verified, because the rise in alkaline fusion temperature caused an increase in the solubility of the species. The results showed the importance of the studied parameter that has direct influence on the formed structural network and the efficiency of the residual glass powder as an alternative source.
author2	Melo, Marcus Antônio de Freitas
author_facet	Melo, Marcus Antônio de Freitas Dantas, Ercília Regina Silva
format	bachelorThesis
author	Dantas, Ercília Regina Silva
author_sort	Dantas, Ercília Regina Silva
title	Estudo da temperatura de fusão alcalina na síntese de zeólita-A utilizando pó de vidro residual como fonte alternativa
title_short	Estudo da temperatura de fusão alcalina na síntese de zeólita-A utilizando pó de vidro residual como fonte alternativa
title_full	Estudo da temperatura de fusão alcalina na síntese de zeólita-A utilizando pó de vidro residual como fonte alternativa
title_fullStr	Estudo da temperatura de fusão alcalina na síntese de zeólita-A utilizando pó de vidro residual como fonte alternativa
title_full_unstemmed	Estudo da temperatura de fusão alcalina na síntese de zeólita-A utilizando pó de vidro residual como fonte alternativa
title_sort	estudo da temperatura de fusão alcalina na síntese de zeólita-a utilizando pó de vidro residual como fonte alternativa
publisher	Universidade Federal do Rio Grande do Norte
publishDate	2016
url	https://repositorio.ufrn.br/handle/123456789/38766
work_keys_str_mv	AT dantaserciliareginasilva estudodatemperaturadefusaoalcalinanasintesedezeolitaautilizandopodevidroresidualcomofontealternativa
_version_	1773966288847110144
spelling	ri-123456789-387662021-09-27T12:20:42Z Estudo da temperatura de fusão alcalina na síntese de zeólita-A utilizando pó de vidro residual como fonte alternativa Dantas, Ercília Regina Silva Melo, Marcus Antônio de Freitas Melo, Marcus Antônio de Freitas Alves, José Antônio Barros Leal Reis Braga, Renata Martins Zeólita-A Pó de Vidro Residual Síntese Hidrotérmica Fonte Alternativa Zeolite-A. Synthesis Hydrothermal. Residual Glass Powder Alternative Source Engenharias. Zeolites are microporous materials due to their structural organization that allow the separation of molecules because of their sizes. For this reason, zeolites are also known as molecular sieves. This group of materials has many industrial applications, such as adsorption, ion exchange of detergents, catalysis and so on. The study of zeolites has undergone accelerated growth in the last 60 years, and the development and analysis of different synthesis methods had decisive role. In this work, zeolite A was obtained using alkaline fusion followed by a hydrothermal treatment where the residual glass powder (RGP) was used as source of SiO2 and AlO2. During the synthesis, the parameter evaluated was the alkaline fusion temperature which varied from 250°C to 500°C. The synthesized materials and residual glass powder (RGP) were characterized by chemical analysis using energy dispersive X-ray analysis (EDX), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Based on the EDX result, the RGP was identified as a silica rich material (about 70%). In addition, the diffractograms and micrographs showed an amorphous nature for the RGP. Also, the formation of zeolite-A was observed at 350˚C and 500˚C by the characterization of the synthesized materials. In fact, an secondary formation (zeolite-X) was verified, because the rise in alkaline fusion temperature caused an increase in the solubility of the species. The results showed the importance of the studied parameter that has direct influence on the formed structural network and the efficiency of the residual glass powder as an alternative source. As zeólitas são materiais microporosos que, devido à organização de sua rede estrutural, possibilita a separação de moléculas em virtude de seus tamanhos. Por esse motivo, as zeólitas também são conhecidas como peneiras moleculares. Esse grupo de materiais apresenta inúmeras aplicações industriais em adsorção, troca iônica de detergentes, catálise, entre outras. O estudo sobre zeólitas sofreu acelerado crescimento nos últimos 60 anos onde o desenvolvimento e análise de diferentes métodos de sínteses teve papel determinante. Neste trabalho, a zeólita do tipo A foi sintetizada pelo método de fusão alcalina seguida por tratamento hidrotérmico no qual pó de vidro residual (PVR) foi utilizado como fonte de SiO2 e AlO2. Durante a síntese, o parâmetro avaliado foi à temperatura de fusão alcalina que sofreu variações de 250°C a 500°C. As amostras sintetizadas e o resíduo foram caracterizados por espectrometria de energia dispersiva de raios X (EDX), difração de raios X (DRX) e microscopia eletrônica de varredura (MEV). De acordo com o EDX, o PVR foi identificado como uma material rico em sílica (cerca de 70%). Além disso, os difratogramas de raios X e imagens de MEV mostram que o PVR apresenta uma natureza amorfa. Através das caracterizações dos materiais sintetizados foi observado a formação de zeólita-A à 350˚C e 500˚C. Na verdade, verificou-se a formação secundária de zeólita-X também devido ao aumento da solubilidade das espécies causada pelas aumento da temperatura de fusão alcalina. Portanto, os resultados obtidos evidenciaram a importância do parâmetro estudado que apresenta influência direta sobre a rede estrutural formada e a eficiência do pó de vidro residual como fonte alternativa. 2016-03-17T14:35:33Z 2021-09-27T12:20:42Z 2016-03-17T14:35:33Z 2021-09-27T12:20:42Z 2015-12-15 bachelorThesis 2010050720 DANTAS, Ercília Regina Silva. Estudo da temperatura de fusão alcalina na síntese de zeólita-A utilizando pó de vidro residual como fonte alternativa. 2015. 58f. Trabalho de Conclusão de Curso (Graduação em Engenharia Química), Departamento de Engenharia Química, Universidade Federal do Rio Grande do Norte, Natal, 2015. https://repositorio.ufrn.br/handle/123456789/38766 pt_BR openAccess application/octet-stream Universidade Federal do Rio Grande do Norte Brasil UFRN Engenharia Química

Estudo da temperatura de fusão alcalina na síntese de zeólita-A utilizando pó de vidro residual como fonte alternativa

Registros relacionados