Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa
In industrial processes that use high temperatures, greater fire great can reduce the cost of production and increase productivity. The use of faster and more efficient fire cycles has been little investigated by the structural ceramic industry in Brazil. As clay materials are submitted to high temp...
Na minha lista:
Principais autores: | , , , , , |
---|---|
Formato: | article |
Idioma: | pt_BR |
Publicado em: |
ABCERAM
|
Assuntos: | |
Endereço do item: | https://repositorio.ufrn.br/handle/123456789/32027 |
Tags: |
Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
|
id |
ri-123456789-32027 |
---|---|
record_format |
dspace |
institution |
Repositório Institucional |
collection |
RI - UFRN |
language |
pt_BR |
topic |
Argilas Cerâmica estrutural Ciclo de queima Energia Propriedades tecnológicas |
spellingShingle |
Argilas Cerâmica estrutural Ciclo de queima Energia Propriedades tecnológicas Dutra, Ricardo Peixoto Suassuna Varela, Marcio Luiz Nascimento, Rubens Maribondo do Gomes, Uílame Umbelino Martinelli, Antonio Eduardo Paskocimas, Carlos Alberto Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa |
description |
In industrial processes that use high temperatures, greater fire great can reduce the cost of production and increase productivity. The use of faster and more efficient fire cycles has been little investigated by the structural ceramic industry in Brazil. As clay materials are submitted to high temperatures, pores are sealed by mass transport mechanisms and a series of thermally activated processes involving the initial constituents. The reactions that take place during firing depend on the nature and composition of the clay materials used.
The firing cycle must be tuned to assure the technological performance required for each product, but at the same time minimize the consumption of energy. Samples were pressed under 25 MPa, dried and fired in an electric furnace. The heating rates selected were 2 oC/min (slow cycle) and 20 oC/min (fast firing). The holding time at the sintering temperatures (950 °C and 1050 oC) were null. This paper presents for the first time the use of a fast fire rate for raw materials using a traditional slow cycle and fast cycle were tested from physical and mechanical properties of the burned pieces were measured, with emphasis on water absorption and linear
shrinkage tests. Microstructural analysis was performed using X-ray diffraction. The results show that is possible to obtain products with equivalent water absorption values and in enhanced mechanic properties when is used the fast firing |
format |
article |
author |
Dutra, Ricardo Peixoto Suassuna Varela, Marcio Luiz Nascimento, Rubens Maribondo do Gomes, Uílame Umbelino Martinelli, Antonio Eduardo Paskocimas, Carlos Alberto |
author_facet |
Dutra, Ricardo Peixoto Suassuna Varela, Marcio Luiz Nascimento, Rubens Maribondo do Gomes, Uílame Umbelino Martinelli, Antonio Eduardo Paskocimas, Carlos Alberto |
author_sort |
Dutra, Ricardo Peixoto Suassuna |
title |
Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa |
title_short |
Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa |
title_full |
Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa |
title_fullStr |
Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa |
title_full_unstemmed |
Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa |
title_sort |
estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa |
publisher |
ABCERAM |
publishDate |
2021 |
url |
https://repositorio.ufrn.br/handle/123456789/32027 |
work_keys_str_mv |
AT dutraricardopeixotosuassuna estudocomparativodaqueimarapidacomaqueimatradicionalnaspropriedadesdemateriaisceramicosdebaseargilosa AT varelamarcioluiz estudocomparativodaqueimarapidacomaqueimatradicionalnaspropriedadesdemateriaisceramicosdebaseargilosa AT nascimentorubensmaribondodo estudocomparativodaqueimarapidacomaqueimatradicionalnaspropriedadesdemateriaisceramicosdebaseargilosa AT gomesuilameumbelino estudocomparativodaqueimarapidacomaqueimatradicionalnaspropriedadesdemateriaisceramicosdebaseargilosa AT martinelliantonioeduardo estudocomparativodaqueimarapidacomaqueimatradicionalnaspropriedadesdemateriaisceramicosdebaseargilosa AT paskocimascarlosalberto estudocomparativodaqueimarapidacomaqueimatradicionalnaspropriedadesdemateriaisceramicosdebaseargilosa AT dutraricardopeixotosuassuna comparativestudyoffastfiringwithtraditionalfiringonthepropertiesofceramicclayrawmaterials AT varelamarcioluiz comparativestudyoffastfiringwithtraditionalfiringonthepropertiesofceramicclayrawmaterials AT nascimentorubensmaribondodo comparativestudyoffastfiringwithtraditionalfiringonthepropertiesofceramicclayrawmaterials AT gomesuilameumbelino comparativestudyoffastfiringwithtraditionalfiringonthepropertiesofceramicclayrawmaterials AT martinelliantonioeduardo comparativestudyoffastfiringwithtraditionalfiringonthepropertiesofceramicclayrawmaterials AT paskocimascarlosalberto comparativestudyoffastfiringwithtraditionalfiringonthepropertiesofceramicclayrawmaterials |
_version_ |
1773959613601808384 |
spelling |
ri-123456789-320272021-04-04T08:37:20Z Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa Comparative study of fast firing with traditional firing on the properties of ceramic clay raw materials Dutra, Ricardo Peixoto Suassuna Varela, Marcio Luiz Nascimento, Rubens Maribondo do Gomes, Uílame Umbelino Martinelli, Antonio Eduardo Paskocimas, Carlos Alberto Argilas Cerâmica estrutural Ciclo de queima Energia Propriedades tecnológicas In industrial processes that use high temperatures, greater fire great can reduce the cost of production and increase productivity. The use of faster and more efficient fire cycles has been little investigated by the structural ceramic industry in Brazil. As clay materials are submitted to high temperatures, pores are sealed by mass transport mechanisms and a series of thermally activated processes involving the initial constituents. The reactions that take place during firing depend on the nature and composition of the clay materials used. The firing cycle must be tuned to assure the technological performance required for each product, but at the same time minimize the consumption of energy. Samples were pressed under 25 MPa, dried and fired in an electric furnace. The heating rates selected were 2 oC/min (slow cycle) and 20 oC/min (fast firing). The holding time at the sintering temperatures (950 °C and 1050 oC) were null. This paper presents for the first time the use of a fast fire rate for raw materials using a traditional slow cycle and fast cycle were tested from physical and mechanical properties of the burned pieces were measured, with emphasis on water absorption and linear shrinkage tests. Microstructural analysis was performed using X-ray diffraction. The results show that is possible to obtain products with equivalent water absorption values and in enhanced mechanic properties when is used the fast firing O estudo do ciclo de queima de materiais cerâmicos tradicionais é de grande interesse industrial, visto que são processos que utilizam grande quantidade de energia. Com um ciclo de queima adequado é possível obter um produto de melhor qualidade e com menor consumo de energia térmica, aumentando a produtividade e diminuindo os custos de produção. No Brasil, atualmente, a maioria dos ciclos de queima dos produtos da cerâmica estrutural tem duração em torno de 24 h, sendo normal, em alguns casos, ciclos que chegam a durar mais de 30 h. A inclusão de ciclos de queima mais curtos é atualmente o mais importante processo de inovação em estudo para otimização do processo de queima da indústria de cerâmica estrutural. Este trabalho faz um estudo comparativo das propriedades tecnológicas de materiais cerâmicos de base argilosa queimados por um ciclo de queima tradicional (queima lenta) e um ciclo de queima rápida. Foram utilizadas neste trabalho matérias-primas argilosas procedentes de indústrias de cerâmica estrutural. As taxas de queima utilizadas foram de 1 oC/min (ciclo lento) e 20 oC/min (ciclo rápido) e as temperaturas máximas para as duas taxas de queima foram de 850 oC, 950 oC e 1050 oC. Os resultados obtidos possibilitam uma melhor compreensão dos efeitos do ciclo de queima nas propriedades tecnológicas dos produtos da cerâmica estrutural, permitindo incluir ciclos de queima rápida dependendo das características iniciais das materiais primas e do processamento utilizado 2021-03-30T19:23:31Z 2021-03-30T19:23:31Z 2009 article DUTRA, R. P. S. ; VARELA, M. L. ; NASCIMENTO, R. M. ; GOMES, U. U. ; MARTINELLI, A. E. ; PASKOCIMAS, C. A.. Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa. Cerâmica (São Paulo. Impresso), v. 55, p. 100-106, 2009. Disponível em: http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132009000100014&lng=pt&tlng=pt Acesso em: 16 nov. 2020. https://doi.org/10.1590/S0366-69132009000100014. 1678-4553 0366-6913 https://repositorio.ufrn.br/handle/123456789/32027 10.1590/S0366-69132009000100014 pt_BR Attribution-NonCommercial 3.0 Brazil http://creativecommons.org/licenses/by-nc/3.0/br/ application/pdf ABCERAM |