Preparação de compósitos alumina-mulita de baixo custo via sinterização reativa entre uma argila caulinítica da Paraíba e hidróxido de alumínio

This work aimed to evaluate the effects of processing on microstructure and properties of alumina-mullite composites via reactive sintering of a mixture of kaolinite clay and aluminum hydroxide. Cylindrical pellets were pressed at 40 MPa and sintered between 1300 and 1600 °C. The technological pro...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Principais autores: Martinelli, Antonio Eduardo, Medeiros, S. G., Dutra, Ricardo Peixoto Suassuna, Grilo, João Paulo de Freitas, Paskocimas, Carlos Alberto, Macedo, Daniel Araújo de
Formato: article
Idioma:pt_BR
Publicado em: ABCERAM
Assuntos:
Caulinita
Mulita
Alumina
Microestrutura
Propriedades tecnológicas
Endereço do item:https://repositorio.ufrn.br/handle/123456789/31605
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-31605
record_format dspace
spelling ri-123456789-316052021-03-29T13:55:08Z Preparação de compósitos alumina-mulita de baixo custo via sinterização reativa entre uma argila caulinítica da Paraíba e hidróxido de alumínio Preparation of low-cost alumina-mullite composites via reactive sintering between a kaolinite clay from Paraíba and aluminum hydroxide Martinelli, Antonio Eduardo Medeiros, S. G. Dutra, Ricardo Peixoto Suassuna Grilo, João Paulo de Freitas Paskocimas, Carlos Alberto Macedo, Daniel Araújo de Caulinita Mulita Alumina Microestrutura Propriedades tecnológicas This work aimed to evaluate the effects of processing on microstructure and properties of alumina-mullite composites via reactive sintering of a mixture of kaolinite clay and aluminum hydroxide. Cylindrical pellets were pressed at 40 MPa and sintered between 1300 and 1600 °C. The technological properties were determined as a function of sintering temperature. The evaluation of crystalline phases and microstructure was performed by X-ray diffraction and electron microscopy. Structural results indicate the attainment of mullite and alumina at 1300 °C. Apparent porosity below 0.8% and flexural strength higher than 40 MPa were obtained for sintering temperatures above 1450 °C. A flexural strength as high as 70 MPa was obtained after sintering at 1600 °C. This study demonstrates the possibility of preparing low cost alumina-mullite composites with technological properties compatible with those of ceramics produced by companies with large operations in the international market of refractory products Este estudo aborda os efeitos do processamento na microestrutura e nas propriedades de compósitos alumina-mulita via sinterização reativa de uma mistura argila caulinítica e hidróxido de alumínio. Amostras prensadas a 40 MPa foram sinterizadas entre 1300 e 1600 °C. As propriedades tecnológicas foram determinadas em função da temperatura de sinterização. A avaliação das fases cristalinas e da microestrutura foi realizada por difração de raios X e microscopia eletrônica. Os resultados indicaram a obtenção de mulita e alumina a partir de 1300 °C. Para sinterizações acima de 1450 °C foram obtidos valores de porosidade aparente inferiores a 0,8% e tensão de ruptura à flexão superior a 40 MPa. Amostras com morfologia bimodal (grãos equiaxiais e alongados) e resistência mecânica de 70 MPa foram obtidas após sinterização a 1600 °C. Este estudo demonstra a possibilidade de preparar compósitos alumina-mulita de baixo custo e com propriedades tecnológicas compatíveis com as de cerâmicas produzidas por companhias com grande atuação no mercado internacional de produtos refratários 2021-02-22T19:04:34Z 2021-02-22T19:04:34Z 2016-09 article MEDEIROS, S. G.; DUTRA, R. P. S.; GRILO, J. P. F.; MARTINELLI, A. E.; PASKOCIMAS, C. A.; MACEDO, D. A.. Preparação de compósitos alumina-mulita de baixo custo via sinterização reativa entre uma argila caulinítica da Paraíba e hidróxido de alumínio. Cerâmica, [S.L.], v. 62, n. 363, p. 266-271, set. 2016. FapUNIFESP (SciELO). http://dx.doi.org/10.1590/0366-69132016623631992. Disponível em: http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132016000300266&lng=pt&tlng=pt. Acesso em: 20 jan. 2021. 1678-4553 https://repositorio.ufrn.br/handle/123456789/31605 10.1590/0366-69132016623631992 pt_BR Attribution-NonCommercial 3.0 Brazil http://creativecommons.org/licenses/by-nc/3.0/br/ application/pdf ABCERAM
institution Repositório Institucional
collection RI - UFRN
language pt_BR
topic Caulinita
Mulita
Alumina
Microestrutura
Propriedades tecnológicas
spellingShingle Caulinita
Mulita
Alumina
Microestrutura
Propriedades tecnológicas
Martinelli, Antonio Eduardo
Medeiros, S. G.
Dutra, Ricardo Peixoto Suassuna
Grilo, João Paulo de Freitas
Paskocimas, Carlos Alberto
Macedo, Daniel Araújo de
Preparação de compósitos alumina-mulita de baixo custo via sinterização reativa entre uma argila caulinítica da Paraíba e hidróxido de alumínio
description This work aimed to evaluate the effects of processing on microstructure and properties of alumina-mullite composites via reactive sintering of a mixture of kaolinite clay and aluminum hydroxide. Cylindrical pellets were pressed at 40 MPa and sintered between 1300 and 1600 °C. The technological properties were determined as a function of sintering temperature. The evaluation of crystalline phases and microstructure was performed by X-ray diffraction and electron microscopy. Structural results indicate the attainment of mullite and alumina at 1300 °C. Apparent porosity below 0.8% and flexural strength higher than 40 MPa were obtained for sintering temperatures above 1450 °C. A flexural strength as high as 70 MPa was obtained after sintering at 1600 °C. This study demonstrates the possibility of preparing low cost alumina-mullite composites with technological properties compatible with those of ceramics produced by companies with large operations in the international market of refractory products
format article
author Martinelli, Antonio Eduardo
Medeiros, S. G.
Dutra, Ricardo Peixoto Suassuna
Grilo, João Paulo de Freitas
Paskocimas, Carlos Alberto
Macedo, Daniel Araújo de
author_facet Martinelli, Antonio Eduardo
Medeiros, S. G.
Dutra, Ricardo Peixoto Suassuna
Grilo, João Paulo de Freitas
Paskocimas, Carlos Alberto
Macedo, Daniel Araújo de
author_sort Martinelli, Antonio Eduardo
title Preparação de compósitos alumina-mulita de baixo custo via sinterização reativa entre uma argila caulinítica da Paraíba e hidróxido de alumínio
title_short Preparação de compósitos alumina-mulita de baixo custo via sinterização reativa entre uma argila caulinítica da Paraíba e hidróxido de alumínio
title_full Preparação de compósitos alumina-mulita de baixo custo via sinterização reativa entre uma argila caulinítica da Paraíba e hidróxido de alumínio
title_fullStr Preparação de compósitos alumina-mulita de baixo custo via sinterização reativa entre uma argila caulinítica da Paraíba e hidróxido de alumínio
title_full_unstemmed Preparação de compósitos alumina-mulita de baixo custo via sinterização reativa entre uma argila caulinítica da Paraíba e hidróxido de alumínio
title_sort preparação de compósitos alumina-mulita de baixo custo via sinterização reativa entre uma argila caulinítica da paraíba e hidróxido de alumínio
publisher ABCERAM
publishDate 2021
url https://repositorio.ufrn.br/handle/123456789/31605
work_keys_str_mv AT martinelliantonioeduardo preparacaodecompositosaluminamulitadebaixocustoviasinterizacaoreativaentreumaargilacauliniticadaparaibaehidroxidodealuminio
AT medeirossg preparacaodecompositosaluminamulitadebaixocustoviasinterizacaoreativaentreumaargilacauliniticadaparaibaehidroxidodealuminio
AT dutraricardopeixotosuassuna preparacaodecompositosaluminamulitadebaixocustoviasinterizacaoreativaentreumaargilacauliniticadaparaibaehidroxidodealuminio
AT grilojoaopaulodefreitas preparacaodecompositosaluminamulitadebaixocustoviasinterizacaoreativaentreumaargilacauliniticadaparaibaehidroxidodealuminio
AT paskocimascarlosalberto preparacaodecompositosaluminamulitadebaixocustoviasinterizacaoreativaentreumaargilacauliniticadaparaibaehidroxidodealuminio
AT macedodanielaraujode preparacaodecompositosaluminamulitadebaixocustoviasinterizacaoreativaentreumaargilacauliniticadaparaibaehidroxidodealuminio
AT martinelliantonioeduardo preparationoflowcostaluminamullitecompositesviareactivesinteringbetweenakaoliniteclayfromparaibaandaluminumhydroxide
AT medeirossg preparationoflowcostaluminamullitecompositesviareactivesinteringbetweenakaoliniteclayfromparaibaandaluminumhydroxide
AT dutraricardopeixotosuassuna preparationoflowcostaluminamullitecompositesviareactivesinteringbetweenakaoliniteclayfromparaibaandaluminumhydroxide
AT grilojoaopaulodefreitas preparationoflowcostaluminamullitecompositesviareactivesinteringbetweenakaoliniteclayfromparaibaandaluminumhydroxide
AT paskocimascarlosalberto preparationoflowcostaluminamullitecompositesviareactivesinteringbetweenakaoliniteclayfromparaibaandaluminumhydroxide
AT macedodanielaraujode preparationoflowcostaluminamullitecompositesviareactivesinteringbetweenakaoliniteclayfromparaibaandaluminumhydroxide
_version_ 1773965551255683072

Registros relacionados