Comportamento mecânico de materiais compósitos submetidos a impacto de baixa velocidade na presença de concentradores de tensão

Composites have been widely used in various engineering sectors due to specific high strength and high specific modulus. With the increasing application of composites, it is increasingly important to understand, predict and control their flaws in which defects can play a key role. Defects are imp...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Neto, José Lira Braga
Outros Autores: Freire Junior, Raimundo Carlos Silverio
Formato: doctoralThesis
Idioma:pt_BR
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
Materiais compósitos; Impacto drop test; Flexão após impacto (FAI); Resistência Residual; Dano por impacto.
Endereço do item:https://repositorio.ufrn.br/handle/123456789/30750
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-30750
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language pt_BR
topic Materiais compósitos; Impacto drop test; Flexão após impacto (FAI); Resistência Residual; Dano por impacto.
spellingShingle Materiais compósitos; Impacto drop test; Flexão após impacto (FAI); Resistência Residual; Dano por impacto.
Neto, José Lira Braga
Comportamento mecânico de materiais compósitos submetidos a impacto de baixa velocidade na presença de concentradores de tensão
description Composites have been widely used in various engineering sectors due to specific high strength and high specific modulus. With the increasing application of composites, it is increasingly important to understand, predict and control their flaws in which defects can play a key role. Defects are imperfections of materials generated in manufacturing or during prolonged service. One of the most common defects in composite processing refers to the formation of voids. Voids cause the reduction of mechanical properties and therefore it is important to evaluate the behavior of the material in the presence of this type of defect. Another factor that can lead to a reduction in properties is the damage caused by low-speed impacts, generating internal damage to the material compromising its integrity. This work aims to evaluate the behavior due to the low velocity impact on polymeric composites considering stress concentrators (two side holes at the point of impact) and find the residual mechanical properties of these materials through fai (Flexural After Impact). In the analysis of residual properties, the effects of damage and stress concentrators will be dismembered by evaluating their individual influences on the increase of the stress concentration factor (K). This dismemberment will be carried out through tests considering the isolated effects of each case and a formulation that relates them. In addition, it will also evaluate the influence of the percentage of voids on impact and residual resistance by developing two composites based on fiberglass-E fabric with different void percentages. From the tests performed, it was found that the damage caused by the impact increased by 18% the concentration factor of the material, but in the samples tested with lateral holes the damage had an influence of only 5% in the reduction of the residual resistance
author2 Freire Junior, Raimundo Carlos Silverio
author_facet Freire Junior, Raimundo Carlos Silverio
Neto, José Lira Braga
format doctoralThesis
author Neto, José Lira Braga
author_sort Neto, José Lira Braga
title Comportamento mecânico de materiais compósitos submetidos a impacto de baixa velocidade na presença de concentradores de tensão
title_short Comportamento mecânico de materiais compósitos submetidos a impacto de baixa velocidade na presença de concentradores de tensão
title_full Comportamento mecânico de materiais compósitos submetidos a impacto de baixa velocidade na presença de concentradores de tensão
title_fullStr Comportamento mecânico de materiais compósitos submetidos a impacto de baixa velocidade na presença de concentradores de tensão
title_full_unstemmed Comportamento mecânico de materiais compósitos submetidos a impacto de baixa velocidade na presença de concentradores de tensão
title_sort comportamento mecânico de materiais compósitos submetidos a impacto de baixa velocidade na presença de concentradores de tensão
publisher Universidade Federal do Rio Grande do Norte
publishDate 2020
url https://repositorio.ufrn.br/handle/123456789/30750
work_keys_str_mv AT netojoselirabraga comportamentomecanicodemateriaiscompositossubmetidosaimpactodebaixavelocidadenapresencadeconcentradoresdetensao
_version_ 1773967377987272704
spelling ri-123456789-307502020-11-29T07:44:48Z Comportamento mecânico de materiais compósitos submetidos a impacto de baixa velocidade na presença de concentradores de tensão Neto, José Lira Braga Freire Junior, Raimundo Carlos Silverio Amorim Júnior, Wanderley Ferreira de Barbosa, Joelton Fonseca Alves, Salete Martins Amico, Sandro Campos Materiais compósitos; Impacto drop test; Flexão após impacto (FAI); Resistência Residual; Dano por impacto. Composites have been widely used in various engineering sectors due to specific high strength and high specific modulus. With the increasing application of composites, it is increasingly important to understand, predict and control their flaws in which defects can play a key role. Defects are imperfections of materials generated in manufacturing or during prolonged service. One of the most common defects in composite processing refers to the formation of voids. Voids cause the reduction of mechanical properties and therefore it is important to evaluate the behavior of the material in the presence of this type of defect. Another factor that can lead to a reduction in properties is the damage caused by low-speed impacts, generating internal damage to the material compromising its integrity. This work aims to evaluate the behavior due to the low velocity impact on polymeric composites considering stress concentrators (two side holes at the point of impact) and find the residual mechanical properties of these materials through fai (Flexural After Impact). In the analysis of residual properties, the effects of damage and stress concentrators will be dismembered by evaluating their individual influences on the increase of the stress concentration factor (K). This dismemberment will be carried out through tests considering the isolated effects of each case and a formulation that relates them. In addition, it will also evaluate the influence of the percentage of voids on impact and residual resistance by developing two composites based on fiberglass-E fabric with different void percentages. From the tests performed, it was found that the damage caused by the impact increased by 18% the concentration factor of the material, but in the samples tested with lateral holes the damage had an influence of only 5% in the reduction of the residual resistance Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Os compósitos vêm sendo amplamente utilizados em diversos setores da engenhariam devido alta resistência específica e alto módulo específico. Com a crescente aplicação de compósitos, é cada vez mais importante entender, prever e controlar suas falhas nas quais os defeitos podem desempenhar um papel fundamental. Defeitos são imperfeições de materiais gerados na fabricação ou durante serviços prolongados. Um dos defeitos mais comuns ao processamento de compósitos refere-se à formação de vazios. Os vazios causam a redução das propriedades mecânicas e por isso, torna-se importante avaliar o comportamento do material na presença deste tipo de defeito. Outro fator que pode levar a uma redução nas propriedades são os danos causados por impactos de baixa velocidade, gerando danos internos no material comprometendo sua integridade. Este trabalho tem objetivo é avaliar o comportamento devido ao impacto de baixa velocidade em compósitos poliméricos considerando concentradores de tensão (dois furos laterais ao ponto de impacto) e encontrar as propriedades mecânicas residuais destes materiais por meio do FAI (Flexural After Impact). Na análise das propriedades residuais se desmembrará os efeitos do dano e dos concentradores de tensão avaliando suas influências individuais no aumento do fator de concentração de tensão (K). Este desmembramento será realizado através de ensaios que considerem os efeitos isolados de cada caso e uma formulação que os relaciona. Além disso, também avaliará a influência do percentual de vazios no impacto e na resistência residual desenvolvendo-se dois compósitos a base de tecido de fibra de vidro-E com percentuais de vazios diferentes. Pelos ensaios realizados, verificou-se que o dano causado pelo impacto aumentou em 18% o fator de concentração do material, porém nas amostras ensaiadas com furos laterais o dano possuiu uma influência de somente 5% na diminuição da resistência residual 2020-11-28T17:11:56Z 2020-11-28T17:11:56Z 2020-03-27 doctoralThesis BRAGA NETO, José Lira. Comportamento mecânico de materiais compósitos submetidos a impacto de baixa velocidade na presença de concentradores de tensão . 2020. 99f. Tese (Doutorado Em Engenharia Mecânica) - Centro de Tecnologia, Universidade Federal do Rio Grande do Norte, Natal, 2020. https://repositorio.ufrn.br/handle/123456789/30750 pt_BR Acesso Aberto application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA

Registros relacionados