Estudo da sinterização do compósito WC-316L

Mostrar outras versões (1)

The hard metal is a metal matrix composite composed hard phase carbide and a ductile phase, which can be cobalt, nickel or iron, which plays the role of a hard phase and binder gives the material an adequate toughness. The main binder used in composite based on WC is cobalt. Cobalt however is a scar...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Santos, Alessandra Agna Araújo dos
Outros Autores: Gomes, Uilame Umbelino
Formato: Dissertação
Idioma:pt_BR
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
Compósito WC-316L
Metalurgia do pó
Aço inoxidável 316L
Sinterização
Obtaining composite WC-316L
Use of powder metallurgy
CNPQ::ENGENHARIAS
Acesso em linha:https://repositorio.ufrn.br/jspui/handle/123456789/27203
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-27203
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language pt_BR
topic Compósito WC-316L
Metalurgia do pó
Aço inoxidável 316L
Sinterização
Obtaining composite WC-316L
Use of powder metallurgy
CNPQ::ENGENHARIAS
spellingShingle Compósito WC-316L
Metalurgia do pó
Aço inoxidável 316L
Sinterização
Obtaining composite WC-316L
Use of powder metallurgy
CNPQ::ENGENHARIAS
Santos, Alessandra Agna Araújo dos
Estudo da sinterização do compósito WC-316L
description The hard metal is a metal matrix composite composed hard phase carbide and a ductile phase, which can be cobalt, nickel or iron, which plays the role of a hard phase and binder gives the material an adequate toughness. The main binder used in composite based on WC is cobalt. Cobalt however is a scarce material having high processing costs and is toxic. This study analyzed the influence of 316L stainless steel sinter WC, analyzing the possibility of replace cobalt by 316L stainless steel. The 316L stainless steel has similar physical characteristics to cobalt and is more economical and non-toxic processing. The composite WC-316L was processed by powder metallurgy following steps: preparing starting powders, milling (grinding balls ratio 7:1) to damp presence of cyclohexane for 5 hours, compaction of 200 MPa, sintering at different temperatures: 1200oC , 1300oC and 1400oC with rate 20oC/min isotherm 60 minutes in vacuum atmosphere. The starting powders WC and 316L were characterized by X-RD diffraction, particle size testing and scanning electron microscopy (SEM). The composite sintered WC- 316L was characterized by SEM and micro vickers hardness test. The samples processed at temperatures of 1200oC and 1300oC showed high porosity heterogeneity microstructural, low relative density, 58 % and 66 % respectively, and low hardness, 300 HV and 700 HV, respectively. The samples sintered at temperature 1400oC showed higher homogeneity microstructural compared to the samples sintered at temperatures of 1200oC and 1300oC , relative density of 86 %, and micro hardness value of 1890 HV.
author2 Gomes, Uilame Umbelino
author_facet Gomes, Uilame Umbelino
Santos, Alessandra Agna Araújo dos
format masterThesis
author Santos, Alessandra Agna Araújo dos
author_sort Santos, Alessandra Agna Araújo dos
title Estudo da sinterização do compósito WC-316L
title_short Estudo da sinterização do compósito WC-316L
title_full Estudo da sinterização do compósito WC-316L
title_fullStr Estudo da sinterização do compósito WC-316L
title_full_unstemmed Estudo da sinterização do compósito WC-316L
title_sort estudo da sinterização do compósito wc-316l
publisher Universidade Federal do Rio Grande do Norte
publishDate 2019
url https://repositorio.ufrn.br/jspui/handle/123456789/27203
work_keys_str_mv AT santosalessandraagnaaraujodos estudodasinterizacaodocompositowc316l
_version_ 1773963514857127936
spelling ri-123456789-272032022-12-28T15:34:17Z Estudo da sinterização do compósito WC-316L Santos, Alessandra Agna Araújo dos Gomes, Uilame Umbelino http://lattes.cnpq.br/8930639182241765 http://lattes.cnpq.br/9858094266525225 Costa, Francine Alves da http://lattes.cnpq.br/8698567925323942 Silva, Gilson Garcia da http://lattes.cnpq.br/8681275097040450 Furakava, Marciano Compósito WC-316L Metalurgia do pó Aço inoxidável 316L Sinterização Obtaining composite WC-316L Use of powder metallurgy CNPQ::ENGENHARIAS The hard metal is a metal matrix composite composed hard phase carbide and a ductile phase, which can be cobalt, nickel or iron, which plays the role of a hard phase and binder gives the material an adequate toughness. The main binder used in composite based on WC is cobalt. Cobalt however is a scarce material having high processing costs and is toxic. This study analyzed the influence of 316L stainless steel sinter WC, analyzing the possibility of replace cobalt by 316L stainless steel. The 316L stainless steel has similar physical characteristics to cobalt and is more economical and non-toxic processing. The composite WC-316L was processed by powder metallurgy following steps: preparing starting powders, milling (grinding balls ratio 7:1) to damp presence of cyclohexane for 5 hours, compaction of 200 MPa, sintering at different temperatures: 1200oC , 1300oC and 1400oC with rate 20oC/min isotherm 60 minutes in vacuum atmosphere. The starting powders WC and 316L were characterized by X-RD diffraction, particle size testing and scanning electron microscopy (SEM). The composite sintered WC- 316L was characterized by SEM and micro vickers hardness test. The samples processed at temperatures of 1200oC and 1300oC showed high porosity heterogeneity microstructural, low relative density, 58 % and 66 % respectively, and low hardness, 300 HV and 700 HV, respectively. The samples sintered at temperature 1400oC showed higher homogeneity microstructural compared to the samples sintered at temperatures of 1200oC and 1300oC , relative density of 86 %, and micro hardness value of 1890 HV. Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) O metal duro é um compósito de matriz metálica composto por uma fase dura, os carbetos, e uma fase dúctil, podendo ser cobalto, níquel ou ferro, que exerce o papel de ligante da fase dura e confere a tenacidade adequada ao material. O principal ligante utilizado em compósitos a base de WC é o cobalto. O cobalto, no entanto, é um material escasso, que possui alto custo de processamento e é tóxico. Este trabalho analisou a influência do aço inoxidável 316L na sinterização do WC, avaliando assim a possibilidade de substituição do cobalto pelo aço inoxidável 316L. O aço inox 316L possui características físicas similares ao cobalto é de processamento mais econômico e não tóxico. O compósito WC-316L foi processado via metalurgia do pó pelas seguintes etapas: preparação dos pós iniciais, moagem (relação de bolas 7:1) á úmido, na presença de cicloexano, durante 5 horas, compactação de 200 MPa, sinterização em diferentes temperaturas: 1200oC, 1300oC e 1400oC com taxa de 20oC/min e isoterma de 60 minutos em atmosfera de vácuo. Os pós de partida WC e 316L foram caracterizados por difração de raios-x (DRX), ensaio granulométrico e microscopia eletrônica de varredura (MEV). O compósito sinterizado WC-316L foi caracterizado por MEV e ensaio de microdureza vickers. As amostras processadas nas temperaturas de 1200oC e 1300oC apresentaram alta porosidade, heterogeneidade microestrutural, densidade relativa baixa, 58% e 66% respectivamente, e baixa microdureza, 300 HV e 700 HV, respectivamente. As amostras sinterizadas a temperatura de 1400oC apresentaram maior homogeneidade microestrutural comparadas as amostras sinterizadas a temperaturas de 1200oC e 1300oC, densidade relativa de 86%, e valor de microdureza de 1890 HV. 2019-06-17T11:17:10Z 2019-06-17T11:17:10Z 2013-09-02 masterThesis SANTOS, Alessandra Agna Araújo. Estudo da sinterização do compósito WC-316L. 2013. 66f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Centro de Ciências Exatas e da Terra, Universidade Federal do Rio Grande do Norte, Natal, 2013. https://repositorio.ufrn.br/jspui/handle/123456789/27203 pt_BR Attribution 3.0 https://creativecommons.org/licenses/by/3.0/ application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN Programa de Pós-Graduação em Ciência e Engenharia de Materiais Centro de Ciências Exatas e da Terra

Registos relacionados