Avaliação de aço ABNT 1020 em meio salino utilizando inibidor natural de corrosão

Pipelines and their accessories, equipments, such as centrifugal pumps, among other types of devices that carry multiphase fluids (oil, water, gas and solid particulates) can suffer mechanical and corrosive damage. To monitor and prevent against these types of damage corrosion coupons and inhibit...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Silva, Fernando Nunes da
Outros Autores: Medeiros, João Telesforo Nóbrega de
Formato: doctoralThesis
Idioma:por
Publicado em: Brasil
Assuntos:
Tribologia
Tribocorrosão
Corrosão
Inibidor de corrosão
Desgaste
Textura superficial
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Endereço do item:https://repositorio.ufrn.br/jspui/handle/123456789/26509
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-26509
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Tribologia
Tribocorrosão
Corrosão
Inibidor de corrosão
Desgaste
Textura superficial
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
spellingShingle Tribologia
Tribocorrosão
Corrosão
Inibidor de corrosão
Desgaste
Textura superficial
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Silva, Fernando Nunes da
Avaliação de aço ABNT 1020 em meio salino utilizando inibidor natural de corrosão
description Pipelines and their accessories, equipments, such as centrifugal pumps, among other types of devices that carry multiphase fluids (oil, water, gas and solid particulates) can suffer mechanical and corrosive damage. To monitor and prevent against these types of damage corrosion coupons and inhibitors are widely used in various industry sectors. In this sense it is proposed a scientific investigation that consolidates a thesis focused on the development of new corrosion inhibitors and on a new method to investigate the tribocorrosive wear of a mild steel in saline aqueous medium. Thus, a corrosive cell was used for gravimetric measurements, evaluation of the tribocorrosive wear of ABNT 1020 steel coupons, and to study the efficiency of natural corrosion inhibitors, which were also characterized by physicochemical and electrochemical techniques. The mechanisms of damage to the surface and subsurface of the corrosion coupons due to corrosion and corrosion-erosion synergism were investigated, mapped and characterized. By analyzing the polarization curves for the 0.4 ppm concentration of the inhibitors, the following inhibition efficiencies were obtained: microemulsion system saline (87.06%), hydroalcoholic extract of Bixa Orellana L. (67.79%), and the microemulsion system with the solubilized extract (78.25%). In the wettability of the ABNT 1020 carbon steel surface when in contact with the saline solution (1% NaCl), and with the inhibitors in various concentrations, varying the time, they had contact angles of less than 90°. The comparison with 95% of statistical certainty, using the Fisher LSD method, showed that a cylindrical body submitted in the conditions of the proposed tests presented differentiated superficial and subsurface damages and that such damages could be perceived through microhardness, roughness and waviness.
author2 Medeiros, João Telesforo Nóbrega de
author_facet Medeiros, João Telesforo Nóbrega de
Silva, Fernando Nunes da
format doctoralThesis
author Silva, Fernando Nunes da
author_sort Silva, Fernando Nunes da
title Avaliação de aço ABNT 1020 em meio salino utilizando inibidor natural de corrosão
title_short Avaliação de aço ABNT 1020 em meio salino utilizando inibidor natural de corrosão
title_full Avaliação de aço ABNT 1020 em meio salino utilizando inibidor natural de corrosão
title_fullStr Avaliação de aço ABNT 1020 em meio salino utilizando inibidor natural de corrosão
title_full_unstemmed Avaliação de aço ABNT 1020 em meio salino utilizando inibidor natural de corrosão
title_sort avaliação de aço abnt 1020 em meio salino utilizando inibidor natural de corrosão
publisher Brasil
publishDate 2019
url https://repositorio.ufrn.br/jspui/handle/123456789/26509
work_keys_str_mv AT silvafernandonunesda avaliacaodeacoabnt1020emmeiosalinoutilizandoinibidornaturaldecorrosao
AT silvafernandonunesda evaluationofabnt1020steelinsalinemediumusingnaturalcorrosioninhibitor
_version_ 1773964247636639744
spelling ri-123456789-265092019-01-30T15:05:12Z Avaliação de aço ABNT 1020 em meio salino utilizando inibidor natural de corrosão Evaluation of ABNT 1020 steel in saline medium using natural corrosion inhibitor Silva, Fernando Nunes da Medeiros, João Telesforo Nóbrega de Silva, Djalma Ribeiro da Oliveira, Adelci Menezes de Rossi, Cátia Guaraciara Fernandes Teixeira Cunha, Jardel Dantas da Tribologia Tribocorrosão Corrosão Inibidor de corrosão Desgaste Textura superficial CNPQ::ENGENHARIAS::ENGENHARIA MECANICA Pipelines and their accessories, equipments, such as centrifugal pumps, among other types of devices that carry multiphase fluids (oil, water, gas and solid particulates) can suffer mechanical and corrosive damage. To monitor and prevent against these types of damage corrosion coupons and inhibitors are widely used in various industry sectors. In this sense it is proposed a scientific investigation that consolidates a thesis focused on the development of new corrosion inhibitors and on a new method to investigate the tribocorrosive wear of a mild steel in saline aqueous medium. Thus, a corrosive cell was used for gravimetric measurements, evaluation of the tribocorrosive wear of ABNT 1020 steel coupons, and to study the efficiency of natural corrosion inhibitors, which were also characterized by physicochemical and electrochemical techniques. The mechanisms of damage to the surface and subsurface of the corrosion coupons due to corrosion and corrosion-erosion synergism were investigated, mapped and characterized. By analyzing the polarization curves for the 0.4 ppm concentration of the inhibitors, the following inhibition efficiencies were obtained: microemulsion system saline (87.06%), hydroalcoholic extract of Bixa Orellana L. (67.79%), and the microemulsion system with the solubilized extract (78.25%). In the wettability of the ABNT 1020 carbon steel surface when in contact with the saline solution (1% NaCl), and with the inhibitors in various concentrations, varying the time, they had contact angles of less than 90°. The comparison with 95% of statistical certainty, using the Fisher LSD method, showed that a cylindrical body submitted in the conditions of the proposed tests presented differentiated superficial and subsurface damages and that such damages could be perceived through microhardness, roughness and waviness. Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Tubulações e seus acessórios, equipamentos, como bombas centrífugas, entre outros tipos de dispositivos que operam transportando fluidos multifásicos (óleo, água, gás e particulados sólidos) podem sofrer danos tanto mecânicos quanto corrosivos. Para monitorar e prevenir contra esses tipos de danos cupons de corrosão e inibidores são amplamente utilizados em diversos setores da indústria. Neste sentido propõe-se uma investigação científica que consolide uma tese concentrada no desenvolvimento de novos inibidores de corrosão e em um novo método para investigar o desgaste tribocorrosivo de uma liga ferro-carbono em meio aquoso salino. Sendo assim, foi utilizada uma célula corrosiva para medições gravimétricas, avaliação do desgaste tribocorrosivo de cupons de aço ABNT 1020, e estudar a eficiência de inibidores naturais de corrosão, que, também foram caracterizados através de técnicas físicoquímicas e eletroquímica. Os mecanismos de danos ocorridos na superfície e na subsuperfície dos cupons de corrosão, em decorrência da corrosão e do sinergismo corrosão-desgaste, foram investigados, mapeados e caracterizados. Através da análise das curvas de polarização para a concentração de 0,4 ppm dos inibidores foi possível obter as seguintes eficiências de inibição: sistema microemulsionado salino (87,06%), extrato hidroalcoólico da Bixa Orellana L. (67,79%), e o sistema microemulsionado com o extrato solubilizado (78,25%). Na molhabilidade da superfície do aço carbono ABNT 1020 quando em contato com a solução salina (NaCl 1%), e com os inibidores em várias concentrações, variando o tempo, apresentaram ângulos de contato menor que 90°. A comparação com 95% de certeza estatística, usando o método de Fisher LSD, mostrou que um corpo cilíndrico submetido nas condições de ensaios propostas, apresentou danos superficiais e subsuperficiais diferenciados no seu entorno e que tais danos puderam ser perceptíveis através das técnicas de microdureza, rugosidade e ondulação superficial. 2019-01-15T19:22:36Z 2019-01-15T19:22:36Z 2018-08-27 doctoralThesis SILVA, Fernando Nunes da. Avaliação de aço ABNT 1020 em meio salino utilizando inibidor natural de corrosão. 2018. 117f. Tese (Doutorado em Engenharia Mecânica) - Centro de Tecnologia, Universidade Federal do Rio Grande do Norte, Natal, 2018. https://repositorio.ufrn.br/jspui/handle/123456789/26509 por Acesso Aberto application/pdf Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA

Registros relacionados