Síntese, caracterização estrutural e magnética de hexaferritas de bário dopadas com La3+ e Co2+

The barium hexaferrite, an iron oxide of hexagonal geometry, currently plays an important technological role in applications such as permanent magnets, microwave devices and magnetic recording. In this work, we investigated the e ects of doping with La3+ and Co2+ ions on the magnetic and structur...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Silva, Lucas Marques da
Outros Autores: Araújo, José Humberto de
Formato: Dissertação
Idioma:por
Publicado em: Brasil
Assuntos:
Hexaferritas dopadas
Nanopartículas
Terra rara
Quitosana
Propriedades magnéticas
Efeito Hopkinson
CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA
Endereço do item:https://repositorio.ufrn.br/jspui/handle/123456789/25686
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-25686
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Hexaferritas dopadas
Nanopartículas
Terra rara
Quitosana
Propriedades magnéticas
Efeito Hopkinson
CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA
spellingShingle Hexaferritas dopadas
Nanopartículas
Terra rara
Quitosana
Propriedades magnéticas
Efeito Hopkinson
CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA
Silva, Lucas Marques da
Síntese, caracterização estrutural e magnética de hexaferritas de bário dopadas com La3+ e Co2+
description The barium hexaferrite, an iron oxide of hexagonal geometry, currently plays an important technological role in applications such as permanent magnets, microwave devices and magnetic recording. In this work, we investigated the e ects of doping with La3+ and Co2+ ions on the magnetic and structural properties of barium hexaferrite. Two series of samples were produced, Ba1−αLaαFe12−xCoxO19 with α=0.30, x=(0.0, 0.25, 0.50, 0.75 and 1.0) and α=0.10, x=(0.25 and 0.50). The samples were synthesized by the Ionic Coordination Reaction technical in chitosan polymer matrix and calcined in air 900 ◦C/4 h. The characterization was performed by X ray di ractometry, scanning electron microscopy, vibrating sample magnetometry, Mössbauer spectroscopy and the physical properties measurement system. The X ray di ractograms revealed the presence of the BaFe12O19 type crystalline phase in all samples, with mean particle size ranging from 71 - 58 nm, decreasing with doping. The electron micrographs presented a particle morphology in the form of nanorods, with lengths and diameters around 190 nm and 70 nm, respectively. The analysis detected impurities of α-Fe2O3 and γ-Fe2O3, for the series with α=0.30. The results of the M x H curves showed a dependence of saturation magnetization and coercivity with doping, ranging from 62.9 - 68.8 emu/g, and 5.78 - 2.79 kOe, respectively. A signi- cant improvement (∼10%) at saturation magnetization and an increase in the coercive eld was observed in sample Ba0,9La0,1Fe11,75Co0,25O19. Investigations using Mössbauer spectroscopy demonstrated that the substitution of the Fe3+ by Co2+ ions occurred more strongly in 4f1 and 2a sites of barium hexaferrite. In the M x T measurements, was detected the Hopkinson e ect, an increase in magnetization near the Curie temperature.
author2 Araújo, José Humberto de
author_facet Araújo, José Humberto de
Silva, Lucas Marques da
format masterThesis
author Silva, Lucas Marques da
author_sort Silva, Lucas Marques da
title Síntese, caracterização estrutural e magnética de hexaferritas de bário dopadas com La3+ e Co2+
title_short Síntese, caracterização estrutural e magnética de hexaferritas de bário dopadas com La3+ e Co2+
title_full Síntese, caracterização estrutural e magnética de hexaferritas de bário dopadas com La3+ e Co2+
title_fullStr Síntese, caracterização estrutural e magnética de hexaferritas de bário dopadas com La3+ e Co2+
title_full_unstemmed Síntese, caracterização estrutural e magnética de hexaferritas de bário dopadas com La3+ e Co2+
title_sort síntese, caracterização estrutural e magnética de hexaferritas de bário dopadas com la3+ e co2+
publisher Brasil
publishDate 2018
url https://repositorio.ufrn.br/jspui/handle/123456789/25686
work_keys_str_mv AT silvalucasmarquesda sintesecaracterizacaoestruturalemagneticadehexaferritasdebariodopadascomla3eco2
AT silvalucasmarquesda synthesisstructuralandmagneticcharacterizationofbariumhexaferritesdopedwithla3andco2
_version_ 1773966670956593152
spelling ri-123456789-256862019-01-30T10:10:17Z Síntese, caracterização estrutural e magnética de hexaferritas de bário dopadas com La3+ e Co2+ Synthesis, structural and magnetic characterization of barium hexaferrites doped with La3+ and Co2+ Silva, Lucas Marques da Araújo, José Humberto de Medeiros, Suzana Nóbrega de Soares, João Maria Hexaferritas dopadas Nanopartículas Terra rara Quitosana Propriedades magnéticas Efeito Hopkinson CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA The barium hexaferrite, an iron oxide of hexagonal geometry, currently plays an important technological role in applications such as permanent magnets, microwave devices and magnetic recording. In this work, we investigated the e ects of doping with La3+ and Co2+ ions on the magnetic and structural properties of barium hexaferrite. Two series of samples were produced, Ba1−αLaαFe12−xCoxO19 with α=0.30, x=(0.0, 0.25, 0.50, 0.75 and 1.0) and α=0.10, x=(0.25 and 0.50). The samples were synthesized by the Ionic Coordination Reaction technical in chitosan polymer matrix and calcined in air 900 ◦C/4 h. The characterization was performed by X ray di ractometry, scanning electron microscopy, vibrating sample magnetometry, Mössbauer spectroscopy and the physical properties measurement system. The X ray di ractograms revealed the presence of the BaFe12O19 type crystalline phase in all samples, with mean particle size ranging from 71 - 58 nm, decreasing with doping. The electron micrographs presented a particle morphology in the form of nanorods, with lengths and diameters around 190 nm and 70 nm, respectively. The analysis detected impurities of α-Fe2O3 and γ-Fe2O3, for the series with α=0.30. The results of the M x H curves showed a dependence of saturation magnetization and coercivity with doping, ranging from 62.9 - 68.8 emu/g, and 5.78 - 2.79 kOe, respectively. A signi- cant improvement (∼10%) at saturation magnetization and an increase in the coercive eld was observed in sample Ba0,9La0,1Fe11,75Co0,25O19. Investigations using Mössbauer spectroscopy demonstrated that the substitution of the Fe3+ by Co2+ ions occurred more strongly in 4f1 and 2a sites of barium hexaferrite. In the M x T measurements, was detected the Hopkinson e ect, an increase in magnetization near the Curie temperature. Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Conselho Nacional de Desenvolvimento Científico e Tecnológico - CNPq A hexaferrita de bário, um óxido de ferro de geometria hexagonal, desempenha atualmente um importante papel tecnológico em aplicalções como ímãs permanente, dispositivos de microondas e gravação magnética. Neste trabalho, investigamos os efeitos da dopagem com íons de La3+ e Co2+ sobre as propriedades magnéticas e estruturais da hexaferrita de bário. Duas séries de amostras foram produzidas, Ba1−αLaαFe12−xCoxO19 com α=0,30, x=(0,0; 0,25; 0,50; 0,75; e 1,0) e α=0,10, x=(0,25 e 0,50). As amostras foram sintetizadas através do método de Reação por Coordenação Iônica em matriz polimérica de quitosana e calcinados ao ar em 900 ◦C/4 h. A caracterização foi realizada por difratometria de raios X, microscopia eletrônica de varredura, magnetometria de amostra vibrante, espectroscopia Mössbauer e o sistema de medição de propriedades físicas. Os difratogramas de raios X revelaram a presença da fase cristalina do tipo BaFe12O19 em todas as amostras, com tamanho médio de partícula variando entre 58 - 71 nm, diminuindo com a dopagem. As microgra as eletrônicas apresentaram uma morfologia de partícula na forma de nanobastões, com comprimentos e diâmetros em torno de 190 nm e 70 nm, respectivamente. As análises detectaram impurezas de α-Fe2O3 e γ-Fe2O3, para a série com α=0,30. Os resultados das curvas M x H mostraram uma dependência da magnetização de saturação e coercividade com a dopagem, variando entre 62,9 - 68,8 emu/g, e 5,78 - 2,79 kOe, respectivamente. Uma melhora signi cativa (∼10%) na magnetização de saturação e um incremento no campo coercitivo foi observada na amostra Ba0,9La0,1Fe11,75Co0,25O19. As investigações através da espectroscopia Mössbauer demonstraram que a substituição do íon de Fe3+ por íons de Co2+ ocorreram com maior preferência nos sítios 4f1 e 2a da hexaferrita de bário. Nas medidas M x T foi detectado o efeito Hopkinson, um aumento da magnetização nas proximidades da temperatura de Curie. 2018-08-06T19:11:53Z 2018-08-06T19:11:53Z 2018-04-06 masterThesis SILVA, Lucas Marques da. Síntese, caracterização estrutural e magnética de hexaferritas de bário dopadas com La3+ e Co2+. 2018. 97f. Dissertação (Mestrado em Física) - Centro de Ciências Exatas e da Terra, Universidade Federal do Rio Grande do Norte, Natal, 2018. https://repositorio.ufrn.br/jspui/handle/123456789/25686 por Acesso Aberto application/pdf Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM FÍSICA

Registros relacionados