Estudo das propriedades self-cleaning em substrato têxtil e magnéticas do ZnO: Ag nanoestruturado

ZnO:Ag/Ag nanostructures were synthesized at 100 °C by microwave energy in order to obtain a material with photocatalytic properties on low energy levels and magnetics. The applications of nanomagnetism are diverse ranging from geology, magnetic recording, to medicine. Thus, the material was obtaine...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Souza, Renata Priscilla de Araújo
Outros Autores: Paskocimas, Carlos Alberto
Formato: doctoralThesis
Idioma:por
Publicado em: Brasil
Assuntos:
Óxido de Zinco
Dopante
Prata
Self-cleaning
Propriedades magnéticas e têxteis funcionais
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Endereço do item:https://repositorio.ufrn.br/jspui/handle/123456789/23643
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-23643
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Óxido de Zinco
Dopante
Prata
Self-cleaning
Propriedades magnéticas e têxteis funcionais
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
spellingShingle Óxido de Zinco
Dopante
Prata
Self-cleaning
Propriedades magnéticas e têxteis funcionais
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Souza, Renata Priscilla de Araújo
Estudo das propriedades self-cleaning em substrato têxtil e magnéticas do ZnO: Ag nanoestruturado
description ZnO:Ag/Ag nanostructures were synthesized at 100 °C by microwave energy in order to obtain a material with photocatalytic properties on low energy levels and magnetics. The applications of nanomagnetism are diverse ranging from geology, magnetic recording, to medicine. Thus, the material was obtained from the precursors: zinc acetate dihydrate and silver nitrate (as dopant) in different concentrations such as ZnO1-x:Agx (x= 0, 0.01 e 0.02). Adding polyvinylpyrrolidone synthesis (as surfactant) and hexamethylene as a reducing agent/precipitating agent. For its characterization, the following techniques were performed to evaluate, Diffraction of X-Rays (XRD), Scanning Electron Microscopy and Field Effect (SEM/FEG), Transmission Electron Microscopy (TEM), analysis by isotherms Brunauer surface area Emmett and Taller (BET), Photoluminescence (PL) and Spectrophotometry. The XRD results indicated mainly crystalline phases of wurtzite ZnO for the and for face-centered cubic metallic silver nanoparticles. By undertaking spectrophotometric absorbance it was confirmed by the orange color wavelength methyl photocatalysis ZnO doped with 1 mol% silver synthesized in 10 minutes in an average time of 2 hours and 30 min. Transmittance was obtained with direct and indirect gap of the compositions. All powders obtained showed the photoluminescence property generated by structural defects. The doping of the pure material caused a shift from green to between yellow and red, thus confirming changes in the electrical properties of the same due to decrease in the gap and also showed peak regarding the metal nanoparticles silver around 390 nm. The magnetic properties of the samples were performed using the physical property measurement system (PPMS) from Quantum. Under these conditions the doping improved the photocatalytic property of ZnO. With these prior results, to prove this application the impregnation step was carried out with particles of polyamide by immersion deposition method (dip coating), for this a styrene and butyl acrylate was utilised. The characterization of nano coating ware used using the following techniques: XRD, SEM/EDS, thermal analysis (TG/DTA), Infrared Spectroscopy Fourier Transform (FTIR), atomic force microscopy (AFM) and contact angle. For evaluation of the self-cleaning for photocatalysis property was based on the color change (ΔE) using the spectrophotometer by reflectance before and after subjecting the samples to ultraviolet radiation for anthocyanins.
author2 Paskocimas, Carlos Alberto
author_facet Paskocimas, Carlos Alberto
Souza, Renata Priscilla de Araújo
format doctoralThesis
author Souza, Renata Priscilla de Araújo
author_sort Souza, Renata Priscilla de Araújo
title Estudo das propriedades self-cleaning em substrato têxtil e magnéticas do ZnO: Ag nanoestruturado
title_short Estudo das propriedades self-cleaning em substrato têxtil e magnéticas do ZnO: Ag nanoestruturado
title_full Estudo das propriedades self-cleaning em substrato têxtil e magnéticas do ZnO: Ag nanoestruturado
title_fullStr Estudo das propriedades self-cleaning em substrato têxtil e magnéticas do ZnO: Ag nanoestruturado
title_full_unstemmed Estudo das propriedades self-cleaning em substrato têxtil e magnéticas do ZnO: Ag nanoestruturado
title_sort estudo das propriedades self-cleaning em substrato têxtil e magnéticas do zno: ag nanoestruturado
publisher Brasil
publishDate 2017
url https://repositorio.ufrn.br/jspui/handle/123456789/23643
work_keys_str_mv AT souzarenatapriscilladearaujo estudodaspropriedadesselfcleaningemsubstratotextilemagneticasdoznoagnanoestruturado
_version_ 1773962251957436416
spelling ri-123456789-236432019-01-30T01:59:52Z Estudo das propriedades self-cleaning em substrato têxtil e magnéticas do ZnO: Ag nanoestruturado Souza, Renata Priscilla de Araújo Paskocimas, Carlos Alberto http://lattes.cnpq.br/2667915577777121 http://lattes.cnpq.br/2365059843175411 Motta, Fabiana Villela da http://lattes.cnpq.br/9918299069511517 Bohn, Felipe http://lattes.cnpq.br/9522788035526763 Borges, Filipe Martel de Magalhães http://lattes.cnpq.br/3125652251177322 Nascimento, José Heriberto Oliveira do http://lattes.cnpq.br/7033735079037677 Godinho Júnior, Mário http://lattes.cnpq.br/8364676654739392 Melo, Maxymme Mendes de http://lattes.cnpq.br/3779445657082353 Óxido de Zinco Dopante Prata Self-cleaning Propriedades magnéticas e têxteis funcionais CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA ZnO:Ag/Ag nanostructures were synthesized at 100 °C by microwave energy in order to obtain a material with photocatalytic properties on low energy levels and magnetics. The applications of nanomagnetism are diverse ranging from geology, magnetic recording, to medicine. Thus, the material was obtained from the precursors: zinc acetate dihydrate and silver nitrate (as dopant) in different concentrations such as ZnO1-x:Agx (x= 0, 0.01 e 0.02). Adding polyvinylpyrrolidone synthesis (as surfactant) and hexamethylene as a reducing agent/precipitating agent. For its characterization, the following techniques were performed to evaluate, Diffraction of X-Rays (XRD), Scanning Electron Microscopy and Field Effect (SEM/FEG), Transmission Electron Microscopy (TEM), analysis by isotherms Brunauer surface area Emmett and Taller (BET), Photoluminescence (PL) and Spectrophotometry. The XRD results indicated mainly crystalline phases of wurtzite ZnO for the and for face-centered cubic metallic silver nanoparticles. By undertaking spectrophotometric absorbance it was confirmed by the orange color wavelength methyl photocatalysis ZnO doped with 1 mol% silver synthesized in 10 minutes in an average time of 2 hours and 30 min. Transmittance was obtained with direct and indirect gap of the compositions. All powders obtained showed the photoluminescence property generated by structural defects. The doping of the pure material caused a shift from green to between yellow and red, thus confirming changes in the electrical properties of the same due to decrease in the gap and also showed peak regarding the metal nanoparticles silver around 390 nm. The magnetic properties of the samples were performed using the physical property measurement system (PPMS) from Quantum. Under these conditions the doping improved the photocatalytic property of ZnO. With these prior results, to prove this application the impregnation step was carried out with particles of polyamide by immersion deposition method (dip coating), for this a styrene and butyl acrylate was utilised. The characterization of nano coating ware used using the following techniques: XRD, SEM/EDS, thermal analysis (TG/DTA), Infrared Spectroscopy Fourier Transform (FTIR), atomic force microscopy (AFM) and contact angle. For evaluation of the self-cleaning for photocatalysis property was based on the color change (ΔE) using the spectrophotometer by reflectance before and after subjecting the samples to ultraviolet radiation for anthocyanins. Foram sintetizadas nanoestruturas de ZnO:Ag com nanopartículas (NPs) de prata a 100 °C através de energia micro-ondas com o objetivo de obter um material com propriedades fotocatalíticas (self-cleaning) em baixos níveis de energia e magnéticas. As aplicações práticas do nanomagnetismo são diversas que vão da geologia, da gravação magnética, até a medicina. Desse modo, o material foi obtido a partir dos precursores: acetato de zinco di-hidratado e nitrato de prata em diferentes concentrações tais como ZnO1-x:Agx (x= 0, 0.01 e 0.02). Adicionando a síntese polivinilpirrolidona (como agente surfactante) e hexametilenotetramina como agente redutor/agente de precipitação. Para sua caracterização foram realizadas Difrações de Raios-X (DRX), Microscopia Eletrônica de Varredura e por Efeito de Campo (MEV/FEG), Microscopia Eletrônica de Transmissão (TEM), análises de área de específica por isortermas Brunauer, Emmett e Taller (BET), Fotoluminescência (PL) e Espectrofotometria. Os resultados de DRX apontaram principalmente fases cristalinas de Wurtzita para o ZnO e cúbica de face centrada para nanopartículas de prata metálica. Através da espectrofotometria foi possível confirmar por absorbância no comprimento de onda do corante alaranjado de metila a fotocatálise do ZnO dopado com 1 mol% de prata, sintetizado em 10 min no tempo médio de 2 horas e 30 min. Por transmitância foi obtido o gap direto e indireto das composições estudadas. Todas as composições obtidas apresentaram a propriedade de fotoluminescência gerada por defeitos estruturais. A dopagem ocasionou para o material puro um deslocamento do verde para o amarelo e o vermelho em consequência da diminuição do gap. Apresentou também pico referente às nanopartículas metálicas de prata em torno de 390 nm. As propriedades magnéticas foram investigadas através da análise das curvas de magnetização em temperaturas específicas e da magnetização em função da temperatura, obtidas utilizando-se um sistema PPMS. Com estes resultados, foi realizada a etapa de impregnação das nanopartículas em poliamida pelo método de deposição por imersão, para isso foi utilizado estireno e acrilato de butila. A caracterização do nanorevestimento foi realizada através das análises de DRX, MEV/EDS, análise térmica (TG/DTA), Espectroscopia no Infravermelho com Transformada de Fourier (FTIR), Microscopia de Força Atômica (AFM) e ângulo de contato. A avaliação da propriedade self-cleaning foi baseada na alteração da cor (ΔE) usando o espectrofotômetro por reflectância. 2017-07-17T15:04:44Z 2017-07-17T15:04:44Z 2016-08-05 doctoralThesis SOUZA, Renata Priscilla de Araújo. Estudo das propriedades self-cleaning em substrato têxtil e magnéticas do ZnO: Ag nanoestruturado. 2016. 157f. Tese (Doutorado em Ciência e Engenharia de Materiais) - Centro de Ciências Exatas e da Terra, Universidade Federal do Rio Grande do Norte, Natal, 2016. https://repositorio.ufrn.br/jspui/handle/123456789/23643 por Acesso Aberto application/pdf Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS

Registros relacionados