Fadiga e fratura da superliga à base de níquel, Inconel 625, submetida a razão de carga R = -1
The fatigue process in materials is the failure mechanism with the presence of cyclic stresses. Surface flaws and stress concentrators may lead to nucleation of cracks during this process. The cracks propagate and cause component fracture after a sufficient number of cycles. This failure mechanis...