Estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos

In recent years ceramic materials have been studied and are evolving rapidly, mainly the advanced ceramics. The various properties involving these materials, such as photoluminescence and photocatalysis justify the increasing need for better understanding of the influence of the addition of doping i...

ver descrição completa

Na minha lista:

Detalhes bibliográficos
Autor principal:	Nascimento, Girlene Gonçalves do
Outros Autores:	Paskocimas, Carlos Alberto
Formato:	Dissertação
Idioma:	por
Publicado em:	Brasil
Assuntos:	Zn2TiO4 Fotocatálise Fotoluminescência Precursores poliméricos CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Endereço do item:	https://repositorio.ufrn.br/jspui/handle/123456789/22848
Tags:	Adicionar Tag Sem tags, seja o primeiro a adicionar uma tag!

id	ri-123456789-22848
record_format	dspace
institution	Repositório Institucional
collection	RI - UFRN
language	por
topic	Zn2TiO4 Fotocatálise Fotoluminescência Precursores poliméricos CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
spellingShingle	Zn2TiO4 Fotocatálise Fotoluminescência Precursores poliméricos CNPQ::ENGENHARIAS::ENGENHARIA MECANICA Nascimento, Girlene Gonçalves do Estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos
description	In recent years ceramic materials have been studied and are evolving rapidly, mainly the advanced ceramics. The various properties involving these materials, such as photoluminescence and photocatalysis justify the increasing need for better understanding of the influence of the addition of doping in the final properties. In this work the polymeric precursor method was used to obtain Zn2TiO4 doped with Eu3+ using Zn2EuxTi1-xO4 and Zn2-xEuxTiO4 systems where (X = 1%, 2% and 3%). The powders were calcined at 800°C and 1000°C for 4 hours with a heating rate of 5°C/min. The characterization was made by means of Thermal Analysis (TG/DSC), X-ray diffraction, scanning electron microscopy (SEM), Photocatalytic Activity Assay and Photoluminescence measurements (PL). The powders showed a variation in network parameters, such variation is probably a consequence of vacancies formation within the host network, driven by the entrance of the ion Eu3+ that has greater ionic radius than Ti4+. We obtained better results in the degradation tests in Zn2-xEuxTiO4 sample with 3%, that caused by defects in the crystal lattice due to doping and the withdrawal of zinc favoring the photocatalytic activity of titanium.. The photoluminescence spectra showed no characteristic peaks of Eu3+ due to the overlapping of the matrix, but increased significantly in intensity with increasing doping. The results show the potential of the polymeric precursor methods for obtaining Zn2TiO4 doped with Eu3+.
author2	Paskocimas, Carlos Alberto
author_facet	Paskocimas, Carlos Alberto Nascimento, Girlene Gonçalves do
format	masterThesis
author	Nascimento, Girlene Gonçalves do
author_sort	Nascimento, Girlene Gonçalves do
title	Estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos
title_short	Estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos
title_full	Estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos
title_fullStr	Estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos
title_full_unstemmed	Estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos
title_sort	estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos
publisher	Brasil
publishDate	2017
url	https://repositorio.ufrn.br/jspui/handle/123456789/22848
work_keys_str_mv	AT nascimentogirlenegoncalvesdo estudodaatividadefotocataliticaefotoluminescentedotitanatodezincodopadocomeuropiosintetizadopelometododosprecursorespolimericos
_version_	1773966849033109504
spelling	ri-123456789-228482017-11-04T22:25:50Z Estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos Nascimento, Girlene Gonçalves do Paskocimas, Carlos Alberto Nascimento, Rubens Maribondo do Silva, Gilson Garcia da Zn2TiO4 Fotocatálise Fotoluminescência Precursores poliméricos CNPQ::ENGENHARIAS::ENGENHARIA MECANICA In recent years ceramic materials have been studied and are evolving rapidly, mainly the advanced ceramics. The various properties involving these materials, such as photoluminescence and photocatalysis justify the increasing need for better understanding of the influence of the addition of doping in the final properties. In this work the polymeric precursor method was used to obtain Zn2TiO4 doped with Eu3+ using Zn2EuxTi1-xO4 and Zn2-xEuxTiO4 systems where (X = 1%, 2% and 3%). The powders were calcined at 800°C and 1000°C for 4 hours with a heating rate of 5°C/min. The characterization was made by means of Thermal Analysis (TG/DSC), X-ray diffraction, scanning electron microscopy (SEM), Photocatalytic Activity Assay and Photoluminescence measurements (PL). The powders showed a variation in network parameters, such variation is probably a consequence of vacancies formation within the host network, driven by the entrance of the ion Eu3+ that has greater ionic radius than Ti4+. We obtained better results in the degradation tests in Zn2-xEuxTiO4 sample with 3%, that caused by defects in the crystal lattice due to doping and the withdrawal of zinc favoring the photocatalytic activity of titanium.. The photoluminescence spectra showed no characteristic peaks of Eu3+ due to the overlapping of the matrix, but increased significantly in intensity with increasing doping. The results show the potential of the polymeric precursor methods for obtaining Zn2TiO4 doped with Eu3+. Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Nos últimos anos os materiais cerâmicos vêm sendo estudados e estão evoluindo rapidamente, principalmente as cerâmicas avançadas. As diversas propriedades envolvendo estes materiais, tais como fotocatálise e fotoluminescência, justificam cada vez mais a necessidade de uma melhor compreensão da influência da adição de dopantes nas propriedades finais. Neste trabalho o método dos precursores poliméricos foi utilizado para obter Zn2TiO4 dopado com Eu3+, utilizando os sistemas Zn2EuxTi1-xO4 e Zn2-xEuxTiO4 onde (X=1%, 2% e 3%). Os pós foram calcinados a 800°C e 1000°C durante 4h com taxa de aquecimento de 5°C/min. A caracterização do composto foi feita por meio de Análises Térmicas (TG/DSC), Difração de Raios X, Microscopia Eletrônica de Varredura (MEV), Ensaio de Atividade Fotocatalítica e medidas de Fotoluminescência (FL). Os pós apresentaram uma variação nos parâmetros de rede, tal variação é provavelmente uma consequência da formação de vacâncias dentro da rede hospedeira, motivada pela entrada do íon Eu3+ que possui maior raio iônico que o Ti4+. Foram obtidos melhores resultados nos testes de degradação na amostra Zn2-xEuxTiO4 com 3%, isto causado pelos defeitos na rede cristalina devido a dopagem e pela retirada do zinco favorecendo a atividade fotocatalítica do titânio. Os espectros de fotoluminescência não mostraram picos característicos de Eu3+ devido a sobreposição da matriz, porém aumentou de forma significativa a intensidade de acordo com o aumento da dopagem. Os resultados obtidos mostram o potencial do método dos precursores poliméricos para obtenção do Zn2TiO4 dopado com Eu3+. 2017-05-09T19:38:25Z 2017-05-09T19:38:25Z 2015-01-28 masterThesis NASCIMENTO, Girlene Gonçalves do. Estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos. 2015. 84f. Dissertação (Mestrado em Engenharia Mecânica) - Centro de Tecnologia, Universidade Federal do Rio Grande do Norte, Natal, 2015. https://repositorio.ufrn.br/jspui/handle/123456789/22848 por Acesso Aberto application/pdf Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA

Estudo da atividade fotocatalítica e fotoluminescente do titanato de zinco dopado com európio sintetizado pelo método dos precursores poliméricos

Registros relacionados