Obtenção e caracterização de um compósito de matriz de resina poliester e resíduos de madeira produzidos em marcenarias

The use of industrial waste is nowadays evident, especially in the environmental issue. In recent years, the results have been obtained with the use of waste and vegetable fibers, the dismemberment of the concept of a material can be called composite. A polyester resin composite (orthophthalic and t...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Oliveira, Luan Carvalho Santana de
Outros Autores: Souza, Luiz Guilherme Meira de
Formato: Dissertação
Idioma:por
Publicado em: Brasil
Assuntos:
Compósito
Resina poliéster
Resíduos
Formulações
Caracterização
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Endereço do item:https://repositorio.ufrn.br/jspui/handle/123456789/22398
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-22398
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Compósito
Resina poliéster
Resíduos
Formulações
Caracterização
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
spellingShingle Compósito
Resina poliéster
Resíduos
Formulações
Caracterização
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Oliveira, Luan Carvalho Santana de
Obtenção e caracterização de um compósito de matriz de resina poliester e resíduos de madeira produzidos em marcenarias
description The use of industrial waste is nowadays evident, especially in the environmental issue. In recent years, the results have been obtained with the use of waste and vegetable fibers, the dismemberment of the concept of a material can be called composite. A polyester resin composite (orthophthalic and terephthalic) composite and filler of wood produced in woodworking was obtained and studied. The processes of obtaining composites and a characterization of mechanical, thermal and physical properties in composite samples with a more specific fraction of 10, 20 and 30% were studied for three different granulometries, totaling six formulations for percentages. However, a formulation with 20% was chosen, because with that percentage already had a saturation of the mixture. The tests carried out for tensile, flexural, thermal, water absorption, density, biodegradation, environmental degradation and MEV tests. The composites obtained in all the studied formulations had lower mechanical resistance than the matrix, however it did not make it impossible to use them in applications where no significant efforts are required. In terms of thermal resistance or composite proposed to competitive with a resin matrix, having somewhat lower behavior. As expected the composites presented higher water absorption indices when compared to the polymer matrices. The apparent density of the composites does not present significant variation in relation to the used dimensions. It has been demonstrated, therefore, that the residues aggregated to the resin have a filling charge function. The composite was used for the manufacture of seat tops, demonstrating its feasibility of application in the fabrication of structures for low mechanical stresses.
author2 Souza, Luiz Guilherme Meira de
author_facet Souza, Luiz Guilherme Meira de
Oliveira, Luan Carvalho Santana de
format masterThesis
author Oliveira, Luan Carvalho Santana de
author_sort Oliveira, Luan Carvalho Santana de
title Obtenção e caracterização de um compósito de matriz de resina poliester e resíduos de madeira produzidos em marcenarias
title_short Obtenção e caracterização de um compósito de matriz de resina poliester e resíduos de madeira produzidos em marcenarias
title_full Obtenção e caracterização de um compósito de matriz de resina poliester e resíduos de madeira produzidos em marcenarias
title_fullStr Obtenção e caracterização de um compósito de matriz de resina poliester e resíduos de madeira produzidos em marcenarias
title_full_unstemmed Obtenção e caracterização de um compósito de matriz de resina poliester e resíduos de madeira produzidos em marcenarias
title_sort obtenção e caracterização de um compósito de matriz de resina poliester e resíduos de madeira produzidos em marcenarias
publisher Brasil
publishDate 2017
url https://repositorio.ufrn.br/jspui/handle/123456789/22398
work_keys_str_mv AT oliveiraluancarvalhosantanade obtencaoecaracterizacaodeumcompositodematrizderesinapoliestereresiduosdemadeiraproduzidosemmarcenarias
_version_ 1773963621727993856
spelling ri-123456789-223982017-11-04T00:53:37Z Obtenção e caracterização de um compósito de matriz de resina poliester e resíduos de madeira produzidos em marcenarias Oliveira, Luan Carvalho Santana de Souza, Luiz Guilherme Meira de http://lattes.cnpq.br/4872074585274757 http://lattes.cnpq.br/0801747108308706 Mota, Maria Kalionara de Freitas http://lattes.cnpq.br/6791276267509274 Santos, Natanaeyfle Randemberg Gomes dos http://lattes.cnpq.br/0174046631340409 Compósito Resina poliéster Resíduos Formulações Caracterização CNPQ::ENGENHARIAS::ENGENHARIA MECANICA The use of industrial waste is nowadays evident, especially in the environmental issue. In recent years, the results have been obtained with the use of waste and vegetable fibers, the dismemberment of the concept of a material can be called composite. A polyester resin composite (orthophthalic and terephthalic) composite and filler of wood produced in woodworking was obtained and studied. The processes of obtaining composites and a characterization of mechanical, thermal and physical properties in composite samples with a more specific fraction of 10, 20 and 30% were studied for three different granulometries, totaling six formulations for percentages. However, a formulation with 20% was chosen, because with that percentage already had a saturation of the mixture. The tests carried out for tensile, flexural, thermal, water absorption, density, biodegradation, environmental degradation and MEV tests. The composites obtained in all the studied formulations had lower mechanical resistance than the matrix, however it did not make it impossible to use them in applications where no significant efforts are required. In terms of thermal resistance or composite proposed to competitive with a resin matrix, having somewhat lower behavior. As expected the composites presented higher water absorption indices when compared to the polymer matrices. The apparent density of the composites does not present significant variation in relation to the used dimensions. It has been demonstrated, therefore, that the residues aggregated to the resin have a filling charge function. The composite was used for the manufacture of seat tops, demonstrating its feasibility of application in the fabrication of structures for low mechanical stresses. Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) A utilização de resíduos industriais está em evidência na atualidade, principalmente em função da questão ambiental. Nos últimos anos inúmeros compósitos foram obtidos e estudados, com a utilização de resíduos e fibras vegetais, desmistificando o conceito de que um material só pode ser chamado de compósito se a carga for de reforço. Obteve e estudou-se um compósito de matriz de resina poliéster (ortoftálica e tereftálica) e carga de enchimento de raspa de madeira produzida em marcenarias. Foram estudados os processos de obtenção dos compósitos e a caracterização de propriedades mecânicas, térmicas e físicas nas amostras dos compósitos com fração mássica de 10, 20 e 30%, para três diferentes granulometrias, totalizando seis formulações para porcentagens. Porém, foi escolhida a formulação com 20%, pois com essa porcentagem já tinha atingido a saturação da mistura. Os ensaios realizados foram de tração, flexão, térmico, absorção de água, densidade, biodegradação, degradação ambiental e MEV. Os compósitos obtidos, em todas as formulações estudadas, apresentaram resistência mecânica inferior a da matriz, porém não inviabilizou sua utilização para aplicações onde não são requeridos significativos esforços. Em termos de resistência térmica o compósito proposto foi competitivo com a resina matriz, tendo comportamento um pouco inferior. Como esperado os compósitos apresentaram maiores índices de absorção de água quando comparados às matrizes poliméricas. A densidade aparente dos compósitos não apresentou variação significativa em relação às matrizes utilizadas. Demonstrou-se, portanto, que os resíduos agregados à resina têm a função de carga de enchimento. O compósito foi utilizado para a fabricação de tampos de bancos, demonstrando-se sua viabilidade de aplicação na fabricação de estruturas apara baixas solicitações mecânicas. 2017-03-22T20:17:43Z 2017-03-22T20:17:43Z 2017-01-20 masterThesis OLIVEIRA, Luan Carvalho Santana de. Obtenção e caracterização de um compósito de matriz de resina poliester e resíduos de madeira produzidos em marcenarias. 2017. 88f. Dissertação (Mestrado em Engenharia Mecânica) - Centro de Tecnologia, Universidade Federal do Rio Grande do Norte, Natal, 2017. https://repositorio.ufrn.br/jspui/handle/123456789/22398 por Acesso Aberto application/pdf Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA

Registros relacionados