Estudo e caracterização de compósitos de metal duro com adição de Ni (WC-Ni)

Nickel has been widely used as a substitute for cobalt in WC-Co hardmetal studies due to greater corrosion and oxidation resistance as well as mechanical properties and economic aspect. Currently, carbides and metals are added to hard metal in order to increase the sinterability of the material, and...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Oliveira, Gerlânea Silva de
Outros Autores: Gomes, Uilame Umbelino
Formato: Dissertação
Idioma:por
Publicado em: Brasil
Assuntos:
Metal duro
WC-Ni
Metalurgia do pó
Moagem de alta energia e sinterização
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Endereço do item:https://repositorio.ufrn.br/jspui/handle/123456789/22250
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-22250
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Metal duro
WC-Ni
Metalurgia do pó
Moagem de alta energia e sinterização
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
spellingShingle Metal duro
WC-Ni
Metalurgia do pó
Moagem de alta energia e sinterização
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Oliveira, Gerlânea Silva de
Estudo e caracterização de compósitos de metal duro com adição de Ni (WC-Ni)
description Nickel has been widely used as a substitute for cobalt in WC-Co hardmetal studies due to greater corrosion and oxidation resistance as well as mechanical properties and economic aspect. Currently, carbides and metals are added to hard metal in order to increase the sinterability of the material, and consequently their hardness and toughness. In this study, the effects of different amount of Ni and sintering parameters (sintering temperatures and holding time) on properties of sintered WC-Ni were studied. The sintered products were obtained via powder metallurgy processing steps, in which powders of tungsten carbide (WC) with 5 and 15 wt% Nickel (Ni) were milled in a planetary high energy ball milling for 8 hours. Then, the particulate powders were compacted into a cylindrical die with 5 mm in diameter under a uniaxial load of 300 MPa. Sintering of the green samples was carried out at 1350 and 1450ºC with holding time of 30 and 90 minutes, in resistance furnace and at 1350º C, with 30 and 90 minutes holding time in vacuum furnace. Starting (WC and Ni) and milled powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Energy Dispersive Spectroscopy (EDS). Sintered samples were also characterized by SEM, EDS and microhardness measurements. Hardness results were higher for WC-5 wt% Ni sintered in the resistance furnace at 1450 ° C with 30 and 90 minutes holding time (1078.6 and 1246.1 Hv respectively). WC-5wt% Ni Samples sintered in vacuum furnace at 1350 °C with 30 to 90 minutes holding time obtained a higher microhardness compared to ones sintered in the resistance furnace at 1350 °C with holding time of 30 and 90 minutes.
author2 Gomes, Uilame Umbelino
author_facet Gomes, Uilame Umbelino
Oliveira, Gerlânea Silva de
format masterThesis
author Oliveira, Gerlânea Silva de
author_sort Oliveira, Gerlânea Silva de
title Estudo e caracterização de compósitos de metal duro com adição de Ni (WC-Ni)
title_short Estudo e caracterização de compósitos de metal duro com adição de Ni (WC-Ni)
title_full Estudo e caracterização de compósitos de metal duro com adição de Ni (WC-Ni)
title_fullStr Estudo e caracterização de compósitos de metal duro com adição de Ni (WC-Ni)
title_full_unstemmed Estudo e caracterização de compósitos de metal duro com adição de Ni (WC-Ni)
title_sort estudo e caracterização de compósitos de metal duro com adição de ni (wc-ni)
publisher Brasil
publishDate 2017
url https://repositorio.ufrn.br/jspui/handle/123456789/22250
work_keys_str_mv AT oliveiragerlaneasilvade estudoecaracterizacaodecompositosdemetaldurocomadicaodeniwcni
_version_ 1773964765483237376
spelling ri-123456789-222502019-01-30T03:39:28Z Estudo e caracterização de compósitos de metal duro com adição de Ni (WC-Ni) Oliveira, Gerlânea Silva de Gomes, Uilame Umbelino http://lattes.cnpq.br/9501673264848557 http://lattes.cnpq.br/9858094266525225 Souza, Carlson Pereira de http://lattes.cnpq.br/1030834608582624 Silva, Ariadne de Souza http://lattes.cnpq.br/5623381698478389 Lopes, Francisco Wendell Bezerra http://lattes.cnpq.br/8791819081924591 Oliveira, Leiliane Alves de http://lattes.cnpq.br/7082478793734403 Metal duro WC-Ni Metalurgia do pó Moagem de alta energia e sinterização CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA Nickel has been widely used as a substitute for cobalt in WC-Co hardmetal studies due to greater corrosion and oxidation resistance as well as mechanical properties and economic aspect. Currently, carbides and metals are added to hard metal in order to increase the sinterability of the material, and consequently their hardness and toughness. In this study, the effects of different amount of Ni and sintering parameters (sintering temperatures and holding time) on properties of sintered WC-Ni were studied. The sintered products were obtained via powder metallurgy processing steps, in which powders of tungsten carbide (WC) with 5 and 15 wt% Nickel (Ni) were milled in a planetary high energy ball milling for 8 hours. Then, the particulate powders were compacted into a cylindrical die with 5 mm in diameter under a uniaxial load of 300 MPa. Sintering of the green samples was carried out at 1350 and 1450ºC with holding time of 30 and 90 minutes, in resistance furnace and at 1350º C, with 30 and 90 minutes holding time in vacuum furnace. Starting (WC and Ni) and milled powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Energy Dispersive Spectroscopy (EDS). Sintered samples were also characterized by SEM, EDS and microhardness measurements. Hardness results were higher for WC-5 wt% Ni sintered in the resistance furnace at 1450 ° C with 30 and 90 minutes holding time (1078.6 and 1246.1 Hv respectively). WC-5wt% Ni Samples sintered in vacuum furnace at 1350 °C with 30 to 90 minutes holding time obtained a higher microhardness compared to ones sintered in the resistance furnace at 1350 °C with holding time of 30 and 90 minutes. Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) O níquel tem sido bastante utilizado, em estudos, como substituto do cobalto no metal duro - WC-Co, devido apresentar maior resistência à corrosão e à oxidação, além das propriedades mecânicas e de aspectos econômicos. Atualmente, carbetos e metais são adicionados ao metal duro, para aumentar a sinterabilidade do material, e, consequentemente, as suas propriedades de dureza e tenacidade. Neste trabalho, foram estudados os efeitos da variação percentual de Ni e dos parâmetros de sinterização (temperaturas de sinterização e isotermas) nas propriedades do sinterizado WC-Ni. Os produtos sinterizados foram obtidos através das etapas de processamento da metalurgia do pó, no qual pós de carbeto de tungstênio – WC com adição de 5 e 15%p. de Níquel – Ni foram moídos em um moinho planetário de alta energia durante 8 horas. Em seguida, os pós particulados foram compactados em uma prensa uniaxial sob carga de 300 Mpa numa matriz cilíndrica de 5 mm de diâmetro. A sinterização dos compactados a verde foi realizada nas temperaturas de 1350 ºC e 1450ºC, com isotermas de 30 e 90 minutos, no dilatômetro; e, na temperatura de 1350º C, com isotermas de 30 e 90 minutos, em forno á vácuo. Os pós de partida (WC e Ni) e os moídos foram caracterizados por difração de raios – X (DRX), microscopia eletrônica de varredura (MEV) e espectroscopia de energia dispersiva (EDS); e as amostras sinterizadas foram caracterizadas por MEV, EDS e medidas de microdureza. Os valores de microdureza Vickers foram maiores para as amostras de WC-5%p.Ni sinterizadas a 1450°C, com isotermas de 30 e 90 minutos no dilatômetro (1078,6 HV e 1246,1 HV, respectivemente). No forno a vácuo, o melhor resultado de microdureza, também, foi para as amostras WC-5%p.Ni sinterizadas a 1350ºC com isoterma de 30 e 90 minutos (849,6 HV e 914,7 HV, respectivemente). As amostras de WC-5%p.Ni sinterizadas no forno a vácuo a 1350°C com isotermas de 30 e 90 minutos mostraram maiores valores de microdureza comparados aos das amostras WC-5%pNi sinterizadas no dilatômetro a 1350°C com isoterma de 30 e 90 minutos. 2017-03-15T20:06:06Z 2017-03-15T20:06:06Z 2016-07-29 masterThesis OLIVEIRA, Gerlânea Silva de. Estudo e caracterização de compósitos de metal duro com adição de Ni (WC-Ni). 2016. 100f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Centro de Ciências Exatas e da Terra, Universidade Federal do Rio Grande do Norte, Natal, 2016. https://repositorio.ufrn.br/jspui/handle/123456789/22250 por Acesso Aberto application/pdf Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS

Registros relacionados