Estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: Poli(óxido de etileno)-tungstato de sódio

Self-sustainable polymeric films based on new solid polymer electrolyte, having the poly(ethylene oxide) (PEO) as host matrix and sodium tungstate as doping agent (Na2WO4), were obtained from different salt compositions (m = 0.20; 0.26; 0.30; 0.40; 0.50 and 1.31 mg). The films were characterized...

ver descrição completa

Na minha lista:

Detalhes bibliográficos
Autor principal:	Lima, Gilberto de
Outros Autores:	Silva, Djalma Ribeiro da
Formato:	Dissertação
Idioma:	por
Publicado em:	Brasil
Assuntos:	Poli(óxido de etileno) (POE) Tungstato de Sódio (Na2WO4) Eletrólito Polimérico Sólido (EPS) Estudo termocinético Condutividade iônica CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA
Endereço do item:	https://repositorio.ufrn.br/jspui/handle/123456789/21476
Tags:	Adicionar Tag Sem tags, seja o primeiro a adicionar uma tag!

id	ri-123456789-21476
record_format	dspace
institution	Repositório Institucional
collection	RI - UFRN
language	por
topic	Poli(óxido de etileno) (POE) Tungstato de Sódio (Na2WO4) Eletrólito Polimérico Sólido (EPS) Estudo termocinético Condutividade iônica CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA
spellingShingle	Poli(óxido de etileno) (POE) Tungstato de Sódio (Na2WO4) Eletrólito Polimérico Sólido (EPS) Estudo termocinético Condutividade iônica CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA Lima, Gilberto de Estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: Poli(óxido de etileno)-tungstato de sódio
description	Self-sustainable polymeric films based on new solid polymer electrolyte, having the poly(ethylene oxide) (PEO) as host matrix and sodium tungstate as doping agent (Na2WO4), were obtained from different salt compositions (m = 0.20; 0.26; 0.30; 0.40; 0.50 and 1.31 mg). The films were characterized through XRD, FTIR, SEM/EDS, TG/DTG, DSC and IS. X-ray diffraction showed the semi crystalline nature of the polymer and confirmed that the addition of salt induces reduction in the crystalinity of the films. FTIR data allowed the identification of the interaction between salt ions and polymer chains and confirmed that these interactions are of a physical nature. The micrographs obtained through SEM showed spherulitic morphology interleaved by interlayered bonds for all of the compositions studied. The TG/DTG study revealed that the thermal decomposition of the electrolyte almost happens at a single stage with the addition of salt, increasing the thermal stability of the films. TG/DTG data also allowed the kinetic study of the thermal decomposition of the electrolyte through Broido (BR), Coats-Redfern (CR) and Horowitz-Metzger (HM) methods, suggesting a first-order kinetic for the reaction of the thermal decomposition of the films, as well as the setting of pre-exponential factor, A, and the thermodynamic activation parameters: E, ΔH, ΔS* and ΔG*. The crystallinity degree was determined through DSC data and showed a reduction after the addition of salt to the polymer. The polymer has its conductivity increased after addition of the salt with the PEO-Na2WO4 electrolyte exhibiting maximum of ionic conductivity of 3.24x10-4 S cm-1, to room temperature, for the film with 1.31 mg of salt (F6 film). The impedance data allowed the study on relaxation on PEO chains, even as the diffusion of salt between these chains. The impedance diagrams, on Bode and Nyquist formats, enabled the adjustment of the experimental data to equivalent electric circuits, which facilitated the association of the circuit components to the physical and chemical phenomena observed for the films and revealed that, after the addition of salt to the polymer, the films have their electrical properties enhanced.
author2	Silva, Djalma Ribeiro da
author_facet	Silva, Djalma Ribeiro da Lima, Gilberto de
format	masterThesis
author	Lima, Gilberto de
author_sort	Lima, Gilberto de
title	Estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: Poli(óxido de etileno)-tungstato de sódio
title_short	Estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: Poli(óxido de etileno)-tungstato de sódio
title_full	Estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: Poli(óxido de etileno)-tungstato de sódio
title_fullStr	Estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: Poli(óxido de etileno)-tungstato de sódio
title_full_unstemmed	Estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: Poli(óxido de etileno)-tungstato de sódio
title_sort	estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: poli(óxido de etileno)-tungstato de sódio
publisher	Brasil
publishDate	2016
url	https://repositorio.ufrn.br/jspui/handle/123456789/21476
work_keys_str_mv	AT limagilbertode estudodeumnovoeletrolitopolimericosolidoemformadefilmeautossustentavelpolioxidodeetilenotungstatodesodio
_version_	1773967246272495616
spelling	ri-123456789-214762017-11-03T20:17:12Z Estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: Poli(óxido de etileno)-tungstato de sódio Lima, Gilberto de Silva, Djalma Ribeiro da Cavalcante, Maria Gorette Fernandes, Nedja Suely Correia, Adriana Nunes Silva, Cassia Miriam Lucas da Poli(óxido de etileno) (POE) Tungstato de Sódio (Na2WO4) Eletrólito Polimérico Sólido (EPS) Estudo termocinético Condutividade iônica CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA Self-sustainable polymeric films based on new solid polymer electrolyte, having the poly(ethylene oxide) (PEO) as host matrix and sodium tungstate as doping agent (Na2WO4), were obtained from different salt compositions (m = 0.20; 0.26; 0.30; 0.40; 0.50 and 1.31 mg). The films were characterized through XRD, FTIR, SEM/EDS, TG/DTG, DSC and IS. X-ray diffraction showed the semi crystalline nature of the polymer and confirmed that the addition of salt induces reduction in the crystalinity of the films. FTIR data allowed the identification of the interaction between salt ions and polymer chains and confirmed that these interactions are of a physical nature. The micrographs obtained through SEM showed spherulitic morphology interleaved by interlayered bonds for all of the compositions studied. The TG/DTG study revealed that the thermal decomposition of the electrolyte almost happens at a single stage with the addition of salt, increasing the thermal stability of the films. TG/DTG data also allowed the kinetic study of the thermal decomposition of the electrolyte through Broido (BR), Coats-Redfern (CR) and Horowitz-Metzger (HM) methods, suggesting a first-order kinetic for the reaction of the thermal decomposition of the films, as well as the setting of pre-exponential factor, A, and the thermodynamic activation parameters: E, ΔH, ΔS* and ΔG. The crystallinity degree was determined through DSC data and showed a reduction after the addition of salt to the polymer. The polymer has its conductivity increased after addition of the salt with the PEO-Na2WO4 electrolyte exhibiting maximum of ionic conductivity of 3.24x10-4 S cm-1, to room temperature, for the film with 1.31 mg of salt (F6 film). The impedance data allowed the study on relaxation on PEO chains, even as the diffusion of salt between these chains. The impedance diagrams, on Bode and Nyquist formats, enabled the adjustment of the experimental data to equivalent electric circuits, which facilitated the association of the circuit components to the physical and chemical phenomena observed for the films and revealed that, after the addition of salt to the polymer, the films have their electrical properties enhanced. Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Filmes poliméricos autossustentáveis baseados em um novo eletrólito polimérico sólido (EPS), tendo como matriz hospedeira o poli(óxido de etileno) (POE) e como agente dopante o tungstato de sódio (Na2WO4), foram obtidos para diferentes composições do sal (m = 0,20; 0,26; 0,30; 0,40; 0,50 e 1,31 mg). Os filmes foram caracterizados por DRX, FTIR, MEV/EDS, TG/DTG, DSC e EI. Os difratogramas de raios X confirmaram a natureza semicristalina do polímero e sugeriram que a adição do sal provoca uma redução na cristalinidade dos filmes. Os dados de FTIR permitiram a análise da interação entre os íons do sal e as cadeias poliméricas. As micrografias obtidas por MEV demonstraram morfologia esferulítica intercaladas por ligações interlamelares para todas as composições estudadas. O estudo de TG/DTG mostrou que a decomposição térmica do eletrólito ocorre em uma única etapa com a adição do sal aumentando a estabilidade térmica dos filmes. Os dados de TG/DTG permitiram, ainda, o estudo cinético da decomposição térmica do eletrólito por meio dos métodos de Briodo (BR), Coats-Redfern (CR) e Horowitz-Metzger (HM) sugerindo uma cinética de 1ª ordem para a reação de decomposição térmica dos filmes, assim como, a determinação dos parâmetros termodinâmicos de ativação: E, ∆H, ∆S e ∆G*. O grau de cristalinidade foi determinado através dos dados de DSC e mostrou uma redução após a adição do sal ao polímero. O eletrólito POE/Na2WO4 exibiu um máximo de condutividade iônica de 3,24x10-4 S.cm-1, a temperatura ambiente, para o filme com 1,31 mg do sal. Através dos dados de impedância foi possível o estudo de relaxação das cadeias do POE, assim como, a difusão do sal entre estas cadeias. Os diagramas de impedância, nos formatos Bode e Nyquist, permitiram o ajuste dos dados experimentais à circuitos elétricos equivalentes o que facilitou a associação dos componentes dos circuitos aos fenômenos físicos e químicos observados para os filmes e revelaram que, após a adição do sal ao polímero, os filmes têm suas propriedades elétricas melhoradas. 2016-12-16T20:13:09Z 2016-12-16T20:13:09Z 2016-02-05 masterThesis LIMA, Gilberto de. Estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: Poli(óxido de etileno)-tungstato de sódio. 2016. 139f. Dissertação (Mestrado em Química) - Centro de Ciências Exatas e da Terra, Universidade Federal do Rio Grande do Norte, Natal, 2016. https://repositorio.ufrn.br/jspui/handle/123456789/21476 por Acesso Aberto application/pdf Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM QUÍMICA

Estudo de um novo eletrólito polimérico sólido em forma de filme autossustentável: Poli(óxido de etileno)-tungstato de sódio

Registros relacionados