Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina

Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In th...

Πλήρης περιγραφή

Αποθηκεύτηκε σε:
Λεπτομέρειες βιβλιογραφικής εγγραφής
Κύριος συγγραφέας: Azevedo, Heytor Vitor Souza Bezerra de
Άλλοι συγγραφείς: Gomes, Uilame Umbelino
Μορφή: Dissertação
Γλώσσα:por
Έκδοση: Universidade Federal do Rio Grande do Norte
Θέματα:
Compósitos
Alumina
Carbeto de tungstênio
Cobalto
Moagem de alta energia
Sinterização
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Διαθέσιμο Online:https://repositorio.ufrn.br/jspui/handle/123456789/21026
Ετικέτες: Προσθήκη ετικέτας
Δεν υπάρχουν, Καταχωρήστε ετικέτα πρώτοι!
id ri-123456789-21026
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Compósitos
Alumina
Carbeto de tungstênio
Cobalto
Moagem de alta energia
Sinterização
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
spellingShingle Compósitos
Alumina
Carbeto de tungstênio
Cobalto
Moagem de alta energia
Sinterização
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Azevedo, Heytor Vitor Souza Bezerra de
Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina
description Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 – WC – Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 °C for 1 hour with a heating rate of 10 °C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 °C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 °C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X – ray diffraction (XRD), X – ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness.
author2 Gomes, Uilame Umbelino
author_facet Gomes, Uilame Umbelino
Azevedo, Heytor Vitor Souza Bezerra de
format masterThesis
author Azevedo, Heytor Vitor Souza Bezerra de
author_sort Azevedo, Heytor Vitor Souza Bezerra de
title Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina
title_short Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina
title_full Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina
title_fullStr Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina
title_full_unstemmed Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina
title_sort efeito da adição de wc e co na sinterização e propriedades mecânicas da alumina
publisher Universidade Federal do Rio Grande do Norte
publishDate 2016
url https://repositorio.ufrn.br/jspui/handle/123456789/21026
work_keys_str_mv AT azevedoheytorvitorsouzabezerrade efeitodaadicaodewceconasinterizacaoepropriedadesmecanicasdaalumina
_version_ 1773967462585335808
spelling ri-123456789-210262019-01-30T10:14:51Z Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina Azevedo, Heytor Vitor Souza Bezerra de Gomes, Uilame Umbelino http://lattes.cnpq.br/9849935320577564 http://lattes.cnpq.br/9858094266525225 Costa, Francine Alves da http://lattes.cnpq.br/8698567925323942 Silva, Ariadne de Souza http://lattes.cnpq.br/5623381698478389 Tavares, Elcio Correia de Souza http://lattes.cnpq.br/4400396552273448 Compósitos Alumina Carbeto de tungstênio Cobalto Moagem de alta energia Sinterização CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 – WC – Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 °C for 1 hour with a heating rate of 10 °C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 °C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 °C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X – ray diffraction (XRD), X – ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness. Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Compósitos à base de alumina (Al2O3), carbeto de tungstênio (WC) e cobalto (Co) apresentam propriedades específicas como baixa densidade, alta resistência à oxidação, alto ponto de fusão e elevada inércia química. Esse compósito revela ser um material promissor para ser aplicado em diversos campos da engenharia. Este trabalho tem como objetivo avaliar algumas propriedades mecânicas durante a confecção e, após a sinterização do compósito (Al2O3 - WC - Co). Pós compósitos com a composição de 80%.p de Al2O3, 18%.p de WC e 2%.p de Co foram processados pela rota de moagem de alta energia (MAE), em moinho planetário por 50 horas, bem como por mistura manual em um recipiente de vidro, seguindo a mesma proporção em peso. Amostras foram coletadas (2, 10, 20, 30, 40 e 50 horas) durante o processo de moagem. Em seguida, os pós foram prensados no formato de amostra circular com diâmetro de 5 mm em uma prensa uniaxial com pressões de 200 e 400 MPa. A sinterização ocorreu de duas maneiras: a primeira sinterização via fase sólida foi realizada à 1300 °C e à 1126 °C durante 1h com taxa de aquecimento de 10°C/min em forno resistivo sob atmosfera de argônio as pressões de compactação utilizadas foram de 200 e 400 MPa, a segunda sinterização foi realizada em dilatômetro via fase sólida à 1300 °C com pressão de compactação de 200 MPa, também foi realizada em dilatômetro outra sinterização, desta vez por fase líquida à 1550 °C com pressões de compactação de 200 e 400 MPa, obedecendo os mesmos parâmetros utilizados no forno resistivo. As matérias-primas foram caracterizadas por difração de raios X - (DRX), fluorescência de raios X - (FRX), microscopia eletrônica de varredura (MEV), espectroscopia por dispersão de energia (EDS) e particulometria a laser. As amostras sinterizadas foram submetidas a ensaios de microdureza. Os resultados mostraram que a moagem de alta energia atingiu os objetivos quanto ao tamanho de partícula e a densificação do compósito. Entretanto, a microdureza não alcançou resultados significativos, isso é um indício que o compósito possui baixa tenacidade à fratura. 2016-07-26T22:08:45Z 2016-07-26T22:08:45Z 2016-01-29 masterThesis AZEVEDO, Heytor Vitor Souza Bezerra de. Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina. 2016. 91f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Centro de Ciências Exatas e da Terra, Universidade Federal do Rio Grande do Norte, Natal, 2016. https://repositorio.ufrn.br/jspui/handle/123456789/21026 por Acesso Aberto application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS

Παρόμοια τεκμήρια