Estudo da influência da adição de níquel em alumina pela rota da metalurgia do pó
Ceramic materials alumina basis have been widely used in structural components, mainly because owning properties such as high hardness, chemical inertness and good wear resistance, however, the low toughness is a factor that compromises its use in many other applications, featuring the addition of n...
Na minha lista:
| Autor principal: | |
|---|---|
| Outros Autores: | |
| Formato: | Dissertação |
| Idioma: | por |
| Publicado em: |
Universidade Federal do Rio Grande do Norte
|
| Assuntos: | |
| Endereço do item: | https://repositorio.ufrn.br/jspui/handle/123456789/21025 |
| Tags: |
Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
|
| Resumo: | Ceramic materials alumina basis have been widely used in structural components, mainly because owning properties such as high hardness, chemical inertness and good wear resistance, however, the low toughness is a factor that compromises its use in many other applications, featuring the addition of nickel as a possible solution to this problem, in this context, this work aims to study the addition of nickel alumina using the route of powder metallurgy processing of the material. The percentage of nickel were added 2, 4 and 6 wt%; and each composition to high energy milling in a planetary mill was performed for 2, 4, 9 and 16h. Subsequently, the samples were compacted at 300 MPa and sintered in a vacuum oven at 1400⁰C for 2h. The samples were characterized as the physical and mechanical properties, observing, in general, an improvement in sinterability of the material with increasing grinding time and nickel content, and mixing with a decrease of porosity and increase of hardness, density values above 80% of theoretical were obtained. The milling time of 4 hours and addition of 2% nickel, particularly if achieved higher hardness (HV 1068.7 +/- 32.6) and density of about 99% theoretical density. |
|---|