Estudo dos processos TIG alimentado e MIG-P CC+ aplicados ao passe de raiz na liga AA5052

In many cases the root pass is a critical step of welding, since its execution is affected by several factors, such as variation of joint opening, chamfer angle, dimensions of the face (nose) root, torch inclination, welding speed and feed speed. Moreover, the choice of the welding process is a key...

Fuld beskrivelse

Na minha lista:
Bibliografiske detaljer
Hovedforfatter: Costa, Pedro Henrique Sales da
Andre forfattere: Nascimento, Rubens Maribondo do
Format: Dissertação
Sprog:por
Udgivet: Universidade Federal do Rio Grande do Norte
Fag:
Soldagem
MIG
TIG Alimentado
Passe de raiz
Alumínio
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Online adgang:https://repositorio.ufrn.br/jspui/handle/123456789/20413
Tags: Tilføj Tag
Ingen Tags, Vær først til at tagge denne postø!
id ri-123456789-20413
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Soldagem
MIG
TIG Alimentado
Passe de raiz
Alumínio
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
spellingShingle Soldagem
MIG
TIG Alimentado
Passe de raiz
Alumínio
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Costa, Pedro Henrique Sales da
Estudo dos processos TIG alimentado e MIG-P CC+ aplicados ao passe de raiz na liga AA5052
description In many cases the root pass is a critical step of welding, since its execution is affected by several factors, such as variation of joint opening, chamfer angle, dimensions of the face (nose) root, torch inclination, welding speed and feed speed. Moreover, the choice of the welding process is a key factor to ensure the execution of a root pass with adequate mechanical and metallurgical properties. In this context, this work aimed to study the feasibility of MIG-P CC+ and TIG-A welding processes applied to the root pass in plates of 200 x 200 x 12,75 mm of the AA 5052 aluminum alloy. For this, different configurations of welding were analyzed: chamfer type(V and collar with L=1,0 and 3,00 mm) and two types of addition metals (ER 4043 and 5356). As compared methodology, It was determined the same current 150 A and the deposition rate of addition metal Va/Vs = 14, they were proposed 12combinations of parameters, each with 3repetitions, totaling 36 tests, stressing that It was used only the most appropriate chamfer setting for TIG-A. Results of micrograph and microhardness of fusion and heat affected zones and dilution levels for welded joints with diferente addition metals, beyond radiography. At the established conditions in this work, it can be said that the TIG-A process showed better results in relation to MIG-P CC+. About the chamfer configuration, which was more appropriate was V chamfer, for both addition metals and process. There were no defects such as lack of fusion, bites and roughness. Relative to dilution levels, higher values were observed when used the MIG-P CC+ process for the ER 4043, as well as TIG-A in the V chamfer configuration. ER 4043 addition metal showed a larger amount of pores in relation to the ER 5356, in both process. It was observed the presence of a grain refining, beyond higher hardness levels in all welds made with the ER 5356 addition metal.
author2 Nascimento, Rubens Maribondo do
author_facet Nascimento, Rubens Maribondo do
Costa, Pedro Henrique Sales da
format masterThesis
author Costa, Pedro Henrique Sales da
author_sort Costa, Pedro Henrique Sales da
title Estudo dos processos TIG alimentado e MIG-P CC+ aplicados ao passe de raiz na liga AA5052
title_short Estudo dos processos TIG alimentado e MIG-P CC+ aplicados ao passe de raiz na liga AA5052
title_full Estudo dos processos TIG alimentado e MIG-P CC+ aplicados ao passe de raiz na liga AA5052
title_fullStr Estudo dos processos TIG alimentado e MIG-P CC+ aplicados ao passe de raiz na liga AA5052
title_full_unstemmed Estudo dos processos TIG alimentado e MIG-P CC+ aplicados ao passe de raiz na liga AA5052
title_sort estudo dos processos tig alimentado e mig-p cc+ aplicados ao passe de raiz na liga aa5052
publisher Universidade Federal do Rio Grande do Norte
publishDate 2016
url https://repositorio.ufrn.br/jspui/handle/123456789/20413
work_keys_str_mv AT costapedrohenriquesalesda estudodosprocessostigalimentadoemigpccaplicadosaopassederaiznaligaaa5052
_version_ 1773967245018398720
spelling ri-123456789-204132017-11-02T13:06:57Z Estudo dos processos TIG alimentado e MIG-P CC+ aplicados ao passe de raiz na liga AA5052 Costa, Pedro Henrique Sales da Nascimento, Rubens Maribondo do http://lattes.cnpq.br/2019291698805066 http://lattes.cnpq.br/8671649752936793 Buschinelli, Augusto José de Almeida http://lattes.cnpq.br/9684649153800847 Silva, Celina Leal Mendes da http://lattes.cnpq.br/0940685473373951 Lourenço, Jorge Magner http://lattes.cnpq.br/0636102944565252 Soldagem MIG TIG Alimentado Passe de raiz Alumínio CNPQ::ENGENHARIAS::ENGENHARIA MECANICA In many cases the root pass is a critical step of welding, since its execution is affected by several factors, such as variation of joint opening, chamfer angle, dimensions of the face (nose) root, torch inclination, welding speed and feed speed. Moreover, the choice of the welding process is a key factor to ensure the execution of a root pass with adequate mechanical and metallurgical properties. In this context, this work aimed to study the feasibility of MIG-P CC+ and TIG-A welding processes applied to the root pass in plates of 200 x 200 x 12,75 mm of the AA 5052 aluminum alloy. For this, different configurations of welding were analyzed: chamfer type(V and collar with L=1,0 and 3,00 mm) and two types of addition metals (ER 4043 and 5356). As compared methodology, It was determined the same current 150 A and the deposition rate of addition metal Va/Vs = 14, they were proposed 12combinations of parameters, each with 3repetitions, totaling 36 tests, stressing that It was used only the most appropriate chamfer setting for TIG-A. Results of micrograph and microhardness of fusion and heat affected zones and dilution levels for welded joints with diferente addition metals, beyond radiography. At the established conditions in this work, it can be said that the TIG-A process showed better results in relation to MIG-P CC+. About the chamfer configuration, which was more appropriate was V chamfer, for both addition metals and process. There were no defects such as lack of fusion, bites and roughness. Relative to dilution levels, higher values were observed when used the MIG-P CC+ process for the ER 4043, as well as TIG-A in the V chamfer configuration. ER 4043 addition metal showed a larger amount of pores in relation to the ER 5356, in both process. It was observed the presence of a grain refining, beyond higher hardness levels in all welds made with the ER 5356 addition metal. Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Em muitos casos o passe de raiz é uma etapa crítica da soldagem, uma vez que sua execução é afetada por diversos fatores, tais como variação da abertura da junta, ângulo do chanfro, dimensões da face (nariz) da raiz, inclinação da tocha, velocidade de soldagem e velocidade de alimentação. Além disso, a escolha do processo de soldagem é um fator primordial para garantir a execução de um passe de raiz com adequadas propriedades mecânicas e metalúrgicas. Nesse contexto, este trabalho teve como objetivo estudar a viabilidade dos processos de soldagem MIG-P CC+ e TIG-A aplicado ao passe de raiz em chapas de 200 x 200 x 12,75 mm da liga de alumínio AA 5052. Para tal, foram analisadas configurações diferentes de soldagem: o tipo de chanfro (em V e em gola com L=2,00 e 3,00 mm) e dois tipos de metais de adição (ER 4043 e 5356). Como metodologia de comparação, foi determinada a mesma corrente de 150 A e taxa de deposição do metal de adição Va/Vs = 14, foram realizadas 8 combinações de parâmetros, cada uma com 3 repetições, totalizando 24 testes, salientando que foi usada apenas a configuração de chanfro mais adequada para o TIG-A. São apresentados resultados da micrografia e microdureza das zonas fundida e termicamente afetada e níveis de diluição para as juntas soldadas com os distintos metais de adição, além da radiografia. Nas condições estabelecidas neste trabalho, pode-se afirmar que o processo TIG-A apresentou melhores resultados em relação ao MIG-P CC+. Em relação à configuração do chanfro, o que se mostrou mais adequado foi o chanfro em V, para ambos os metais de adição e processos. Não ocorreram defeitos como falta de fusão, mordeduras e rugosidades. Em relação aos níveis de diluição, foram constatados maiores valores quando utilizado o processo MIG-P CC+ para o ER 4043, assim como o processo TIG-A na configuração de chanfro em V. O metal de adição ER 4043 apresentou uma quantidade de poros maior em relação ao ER 5356, em ambos os processos. Foi observada à presença de um refino de grão, além de maiores níveis de dureza em todas as soldas realizadas com o metal de adição ER 5356. 2016-05-09T20:11:14Z 2016-05-09T20:11:14Z 2015-08-28 masterThesis COSTA, Pedro Henrique Sales da. Estudo dos processos TIG alimentado e MIG-P CC+ aplicados ao passe de raiz na liga AA5052. 2015. 77f. Dissertação (Mestrado em Engenharia Mecânica) - Centro de Tecnologia, Universidade Federal do Rio Grande do Norte, Natal, 2015. https://repositorio.ufrn.br/jspui/handle/123456789/20413 por Acesso Aberto application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA

Lignende værker