Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato

In States of Paraíba (PB) and Rio Grande do Norte (RN), northeast of Brazil, the most significant deposits of non-metallic industrial minerals are pegmatites, quartzites and granites, which are located in Seridó region. Extraction of clay, quartz, micas and feldspars occurs mainly in the cities o...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Souza, Marcondes Mendes de
Outros Autores: Costa, Franciné Alves da
Formato: doctoralThesis
Idioma:por
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
Cerâmica
Grés porcelanato
Resíduos de quartzitos
Revestimentos
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Endereço do item:https://repositorio.ufrn.br/jspui/handle/123456789/20228
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-20228
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Cerâmica
Grés porcelanato
Resíduos de quartzitos
Revestimentos
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
spellingShingle Cerâmica
Grés porcelanato
Resíduos de quartzitos
Revestimentos
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Souza, Marcondes Mendes de
Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato
description In States of Paraíba (PB) and Rio Grande do Norte (RN), northeast of Brazil, the most significant deposits of non-metallic industrial minerals are pegmatites, quartzites and granites, which are located in Seridó region. Extraction of clay, quartz, micas and feldspars occurs mainly in the cities of Várzea (PB), OuroBranco (RN) and Parelhas (RN). Mining companies working in the extraction and processing of quartzite generate large volumes of waste containing about 90% SiO2 in their chemical composition coming from quartz that is one of the basic constituents of ceramic mass for the production of ceramic coating. Therefore, this work evaluates the utilization of these wastes on fabrication of high-quality ceramic products, such as porcelain stoneware, in industrial scale. Characterization of raw materials was based on XRF, XRD, GA, TGA and DSC analysis, on samples composed by 57% of feldspar, 37% of argil and 6% of quartzite residues, with 5 different colors (white, gold, pink, green and black). Samples were synthesized in three temperatures, 1150°C, 1200°C and 1250°C, with one hour isotherm and warming-up tax of 10°C/min. After synthesizing, the specimens were submit to physical characterization tests of water absorption, linear shrinkage, apparently porosity, density, flexural strain at three points. The addition of 6% of quartzite residue to ceramic mass provided a final product with technological properties attending technical norms for the production of porcelain stoneware; best results were observed at a temperature of 1200°C. According to the results there was a high iron oxide on black quartzite, being their use in porcelain stoneware discarded by ethic and structural question, because the material fused at 1250°C. All quartzite formulations had low water absorption when synthesized at 1200°C, getting 0.1% to 0.36% without having gone through the atomization process. Besides, flexural strain tests overcame 27 MPa reaching the acceptance limits of the European Directive EN 100, at 1200°C synthesizing. Thus, the use of quartzite residues in ceramic masses poses as great potential for the production of porcelain stoneware.
author2 Costa, Franciné Alves da
author_facet Costa, Franciné Alves da
Souza, Marcondes Mendes de
format doctoralThesis
author Souza, Marcondes Mendes de
author_sort Souza, Marcondes Mendes de
title Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato
title_short Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato
title_full Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato
title_fullStr Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato
title_full_unstemmed Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato
title_sort estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato
publisher Universidade Federal do Rio Grande do Norte
publishDate 2016
url https://repositorio.ufrn.br/jspui/handle/123456789/20228
work_keys_str_mv AT souzamarcondesmendesde estudodaadicaoderesiduosdequartzitosparaobtencaodegresporcelanato
_version_ 1773965071650652160
spelling ri-123456789-202282017-11-03T12:41:53Z Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato Souza, Marcondes Mendes de Costa, Franciné Alves da http://lattes.cnpq.br/7908961729654856 http://lattes.cnpq.br/8698567925323942 Gomes, Uílame Umbelino http://lattes.cnpq.br/9858094266525225 Silva, Angelus Giuseppe Pereira da http://lattes.cnpq.br/1435330862718379 Tavares, Elcio Correia de Souza http://lattes.cnpq.br/4400396552273448 Silva, Gilson Garcia da http://lattes.cnpq.br/8681275097040450 Cerâmica Grés porcelanato Resíduos de quartzitos Revestimentos CNPQ::ENGENHARIAS::ENGENHARIA MECANICA In States of Paraíba (PB) and Rio Grande do Norte (RN), northeast of Brazil, the most significant deposits of non-metallic industrial minerals are pegmatites, quartzites and granites, which are located in Seridó region. Extraction of clay, quartz, micas and feldspars occurs mainly in the cities of Várzea (PB), OuroBranco (RN) and Parelhas (RN). Mining companies working in the extraction and processing of quartzite generate large volumes of waste containing about 90% SiO2 in their chemical composition coming from quartz that is one of the basic constituents of ceramic mass for the production of ceramic coating. Therefore, this work evaluates the utilization of these wastes on fabrication of high-quality ceramic products, such as porcelain stoneware, in industrial scale. Characterization of raw materials was based on XRF, XRD, GA, TGA and DSC analysis, on samples composed by 57% of feldspar, 37% of argil and 6% of quartzite residues, with 5 different colors (white, gold, pink, green and black). Samples were synthesized in three temperatures, 1150°C, 1200°C and 1250°C, with one hour isotherm and warming-up tax of 10°C/min. After synthesizing, the specimens were submit to physical characterization tests of water absorption, linear shrinkage, apparently porosity, density, flexural strain at three points. The addition of 6% of quartzite residue to ceramic mass provided a final product with technological properties attending technical norms for the production of porcelain stoneware; best results were observed at a temperature of 1200°C. According to the results there was a high iron oxide on black quartzite, being their use in porcelain stoneware discarded by ethic and structural question, because the material fused at 1250°C. All quartzite formulations had low water absorption when synthesized at 1200°C, getting 0.1% to 0.36% without having gone through the atomization process. Besides, flexural strain tests overcame 27 MPa reaching the acceptance limits of the European Directive EN 100, at 1200°C synthesizing. Thus, the use of quartzite residues in ceramic masses poses as great potential for the production of porcelain stoneware. Nos estados da Paraíba e Rio Grande do Norte, no Brasil, as jazidas mais expressivas na produção de minerais industriais não-metálicos são as dos pegmatitos, quartzitos e granitos, que estão localizadas na região do Seridó. Os municípios de Várzea - PB, Ouro Branco - RN e Parelhas - RN são os principais responsáveis pela extração de argila, quartzo, micas e feldspato. As empresas de mineração que atuam na extração e beneficiamento dos quartzitos geram grandes volumes de resíduos, constituindo cerca de 90% de SiO2 na sua composição química proveniente do quartzo, que é um dos constituintes básicos nas formulações das massas cerâmicas para a produção de revestimento cerâmicos. Para tanto, este trabalho avalia o estudo da adição de resíduos de quartzito para obtenção do grés porcelanato através da caracterização das matérias-primas por FRX, DRX, MEV, AG, ATG e DSC, utilizando cinco formulações contendo 57% de feldspato, 37% de argila e 6% de resíduos de quartzitos com colorações diferentes (branco, dourado, rosa, verde e preto), que foram sinterizadas em três temperaturas: 1150°C, 1200°C e 1250°C, com isoterma de 1 hora e taxa de aquecimento de 10° C/min. Após a sinterização, os corpos-de-prova foram submetidos a ensaios de caracterização física como: absorção de água, retração linear, porosidade aparente, massa específica aparente, resistência à flexão em três pontos. Os resultados obtidos apontavam para a possibilidade da utilização do resíduo de quartzito em um percentual de 6% de adição na massa cerâmica. A utilização de resíduos de quartzito em massa cerâmica proporcionou um produto final com propriedades tecnológicas que atendem às normas técnicas para a produção de grés porcelanato, sendo a temperatura de 1200°Ca que apresentou melhores resultados. De acordo com os resultados obtidos verificou-se um alto teor de óxido de ferro no quartzito preto, sendo descartada a utilização do mesmo em grés porcelanato por questão estrutural, pois o material fundiu a 1250°C. Todas as formulações dos quartzitos obtiveram baixa absorção de água quando sinterizadas a 1200°C, obtendo AA entre 0,1% a 0,36% sem terem passado pelo processo de atomização. Nos ensaios de resistência à flexão todos os quartzitos encontram-se nos limites de aceitação, segundo a norma europeia EN 100, superando 27 MPa na sinterização a 1200°C. Com isso, o uso de resíduo de quartzito em massas cerâmicas se apresenta como excelente potencial para a produção de grés porcelanato. 2016-04-11T23:07:06Z 2016-04-11T23:07:06Z 2015-04-17 doctoralThesis SOUZA, Marcondes Mendes de. Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato. 2015. 114f. Tese (Doutorado em Engenharia Mecânica) - Centro de Tecnologia, Universidade Federal do Rio Grande do Norte, Natal, 2015. https://repositorio.ufrn.br/jspui/handle/123456789/20228 por Acesso Aberto application/pdf Universidade Federal do Rio Grande do Norte Brasil UFRN PROGRAMA DE PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA

Registros relacionados