Otimização da síntese do AlSBA-15 para produção de biodiesel por transesteri-ficação do óleo de coco
Stimulus encouraging the production and consumption of biodiesel favors the policy of pre-serving the environment, contributing to the reduction of greenhouse gas reducing climate change. The current trend of research in this field focuses on improving these processes with the use of heterogeneous c...
Na minha lista:
| Autor principal: | |
|---|---|
| Outros Autores: | |
| Formato: | doctoralThesis |
| Idioma: | por |
| Publicado em: |
Universidade Federal do Rio Grande do Norte
|
| Assuntos: | |
| Endereço do item: | https://repositorio.ufrn.br/jspui/handle/123456789/19398 |
| Tags: |
Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
|
| Resumo: | Stimulus encouraging the production and consumption of biodiesel favors the policy of pre-serving the environment, contributing to the reduction of greenhouse gas reducing climate change. The current trend of research in this field focuses on improving these processes with the use of heterogeneous catalysts, seeing has significant advantages such as: low contamination of products, ease of separation of the catalyst from the reaction medium, possibili-ty of reuse of the catalyst, decreased corrosion problems. The objective of this research was to optimize the synthesis of AlSBA-15 for the production of biodiesel through transesterification process via ethyl route. For the optimization of hydrothermal synthesis of type AlSBA-15 catalyst has assembled a 23 factorial experimental matrix with eleven trials. The stoichiometric amounts of starting materials were varied according to different ratios Si / Al which is a factor in the experimental design, in addition to the time and temperature of aging of the synthesis gel. The material showed the best results of characterization (SBET = 591.7 (m2 / g), Vp = 0.83 (cm3 / g), Dp = 5.59 (nm), w = 6.48 (nm) was synthesized at 100 ° C for 24 hours, with a ratio Si / Al = 10.This material was applied as a heterogeneous catalyst in the reaction of ethyl transesterification as raw coconut oil in natura. Coconut oil presented suitable for obtaining biodiesel via ethyl route.The visual aspects and physical-chemical characteristics of the reaction products show that AlSBA-15 catalyst favored the reaction. According to physical-chemical analysis the order of oxidative stability of the product of the transesterification reaction was: catalytic reaction at 1500 ° C> non-catalytic reaction at 100 ° C> 100 ° C catalytic> catalytic reaction at 200 ° C Reaction. The results of oxidative stability and kinematic viscosity shows that the biodiesel produced in the catalytic sandblasting held at 150 ° C which was maintained within the ABNT NBR 7148, ABNT NBR 10441 and EN 14112. |
|---|