Uso da palha de carnaúba em revestimento de dutos
In this work, the plant species Copernicia prunifera (Miller) H. E. Moore (carnauba), naturally occurring which prevails in the northeast region of Brazil was the subject of studies aiming its use as external coating of pipelines used in petroleum industry. The part of the plant worked were the leav...
Na minha lista:
| Autor principal: | |
|---|---|
| Outros Autores: | |
| Formato: | Dissertação |
| Idioma: | por |
| Publicado em: |
Universidade Federal do Rio Grande do Norte
|
| Assuntos: | |
| Endereço do item: | https://repositorio.ufrn.br/jspui/handle/123456789/17648 |
| Tags: |
Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
|
| id |
ri-123456789-17648 |
|---|---|
| record_format |
dspace |
| institution |
Repositório Institucional |
| collection |
RI - UFRN |
| language |
por |
| topic |
Palha de carnaúba Tratamento químico Revestimento Resina acrílica Argila. Carnauba straw Chemical treatment Coating Acrylic resin Clay. CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA |
| spellingShingle |
Palha de carnaúba Tratamento químico Revestimento Resina acrílica Argila. Carnauba straw Chemical treatment Coating Acrylic resin Clay. CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA Fernandes, Jéssica Emanuela de Araújo Uso da palha de carnaúba em revestimento de dutos |
| description |
In this work, the plant species Copernicia prunifera (Miller) H. E. Moore (carnauba),
naturally occurring which prevails in the northeast region of Brazil was the subject of studies
aiming its use as external coating of pipelines used in petroleum industry. The part of the
plant worked were the leaves, also called straw, which were coated with resinous material.
For this purpose, it was necessary to evaluate the effectiveness of the use of acrylic resins in
the straw carnauba coating. The properties of the untreated carnauba straw and chemically
treated with sodium hydroxide, hexane and carbon tetrachloride were investigated by ATRFTIR,
SEM and thermal analysis. The first two techniques showed that treatment with
solvents has caused major changes in the straw surface, while the thermal analysis indicated
that the sodium hydroxide caused variations in thermal stability of straw constituents. Water
absorption measurements showed that treatments have accelerated the absorption process and
the reduction of contact angle values for treated samples with solvents indicated higher
hidrophilicity of straw. The tensile tests showed lower values of elastic modulus and tensile
strength for treated samples. Furthermore, coatings using pure commercial resins A and B
as well as the formulations with clay were applied in straw and they were examined once
again through thermal analysis, water absorption measurements, contact angle and mechanical
tests. To analyze the effect of heat ageing, samples were subjected to tensile tests again in
order to assess its resistance. The results showed that the resins/clay formulations increased
thermal stability of straw, they promoted a good impermeabilization and caused significant
decrease in the values of elastic modulus and tensile strength. Evaluating the ageing effect on
the mechanical properties, it has been showed good recovery to the coated straw with the
formulations A 60 and A 80% in modulus and tensile strength values and elongation at break
values have remained very close. It is thus concluded that the carnauba straw can be used as a
coating of pipelines with significant cost savings, since there is no need for pretreatment for
its use and shows itself as a viable biotechnology alternative, contributing to the quality of
coatings material and environment preservation. |
| author2 |
Pereira, Márcia Rodrigues |
| author_facet |
Pereira, Márcia Rodrigues Fernandes, Jéssica Emanuela de Araújo |
| format |
masterThesis |
| author |
Fernandes, Jéssica Emanuela de Araújo |
| author_sort |
Fernandes, Jéssica Emanuela de Araújo |
| title |
Uso da palha de carnaúba em revestimento de dutos |
| title_short |
Uso da palha de carnaúba em revestimento de dutos |
| title_full |
Uso da palha de carnaúba em revestimento de dutos |
| title_fullStr |
Uso da palha de carnaúba em revestimento de dutos |
| title_full_unstemmed |
Uso da palha de carnaúba em revestimento de dutos |
| title_sort |
uso da palha de carnaúba em revestimento de dutos |
| publisher |
Universidade Federal do Rio Grande do Norte |
| publishDate |
2014 |
| url |
https://repositorio.ufrn.br/jspui/handle/123456789/17648 |
| work_keys_str_mv |
AT fernandesjessicaemanueladearaujo usodapalhadecarnaubaemrevestimentodedutos |
| _version_ |
1773958032527458304 |
| spelling |
ri-123456789-176482017-11-04T14:35:59Z Uso da palha de carnaúba em revestimento de dutos Fernandes, Jéssica Emanuela de Araújo Pereira, Márcia Rodrigues http://lattes.cnpq.br/6114636932635634 http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4788568T8 Maciel, Maria Aparecida Medeiros http://lattes.cnpq.br/5360188002708095 Sousa, Emanuel Alves de http://lattes.cnpq.br/8566005165321301 Palha de carnaúba Tratamento químico Revestimento Resina acrílica Argila. Carnauba straw Chemical treatment Coating Acrylic resin Clay. CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA In this work, the plant species Copernicia prunifera (Miller) H. E. Moore (carnauba), naturally occurring which prevails in the northeast region of Brazil was the subject of studies aiming its use as external coating of pipelines used in petroleum industry. The part of the plant worked were the leaves, also called straw, which were coated with resinous material. For this purpose, it was necessary to evaluate the effectiveness of the use of acrylic resins in the straw carnauba coating. The properties of the untreated carnauba straw and chemically treated with sodium hydroxide, hexane and carbon tetrachloride were investigated by ATRFTIR, SEM and thermal analysis. The first two techniques showed that treatment with solvents has caused major changes in the straw surface, while the thermal analysis indicated that the sodium hydroxide caused variations in thermal stability of straw constituents. Water absorption measurements showed that treatments have accelerated the absorption process and the reduction of contact angle values for treated samples with solvents indicated higher hidrophilicity of straw. The tensile tests showed lower values of elastic modulus and tensile strength for treated samples. Furthermore, coatings using pure commercial resins A and B as well as the formulations with clay were applied in straw and they were examined once again through thermal analysis, water absorption measurements, contact angle and mechanical tests. To analyze the effect of heat ageing, samples were subjected to tensile tests again in order to assess its resistance. The results showed that the resins/clay formulations increased thermal stability of straw, they promoted a good impermeabilization and caused significant decrease in the values of elastic modulus and tensile strength. Evaluating the ageing effect on the mechanical properties, it has been showed good recovery to the coated straw with the formulations A 60 and A 80% in modulus and tensile strength values and elongation at break values have remained very close. It is thus concluded that the carnauba straw can be used as a coating of pipelines with significant cost savings, since there is no need for pretreatment for its use and shows itself as a viable biotechnology alternative, contributing to the quality of coatings material and environment preservation. Conselho Nacional de Desenvolvimento Científico e Tecnológico Neste trabalho, a espécie vegetal Copernicia prunifera (Miller) H. E. Moore (carnaúba), de ocorrência natural predominante da região Nordeste do Brasil, foi alvo de estudos objetivando sua utilização como revestimento externo de dutos da indústria do petróleo. A parte da planta trabalhada foram as folhas, também chamadas de palhas, que receberam um revestimento resinoso. Para tanto, foi necessário avaliar a eficácia do uso de resinas acrílicas no revestimento da palha de carnaúba. As propriedades da palha não-tratada e tratada quimicamente com hidróxido de sódio, hexano e tetracloreto de carbono foram investigadas por FTIR-ATR, MEV e TG. As duas primeiras técnicas mostraram que os tratamentos com os solventes provocaram maiores modificações na superfície da palha, enquanto o estudo termogravimétrico indicou que o hidróxido de sódio causou variações na estabilidade térmica dos constituintes da palha. Medidas de absorção de água mostraram que os tratamentos aceleraram o processo de absorção e a redução dos valores de ângulo de contato para as amostras tratadas com os solventes indicou aumento da hidrofilicidade das palhas. Os ensaios mecânicos apresentaram menores valores de módulo elástico e tensão de ruptura para as amostras tratadas. Além disso, revestimentos com resinas comerciais puras A e B assim como composições com argila foram aplicados nas palhas e estas foram analisadas novamente através da termogravimetria, medidas de absorção de água, ângulo de contato e resistência mecânica. Para analisar o efeito do envelhecimento térmico realizado, as amostras foram submetidas mais uma vez aos ensaios mecânicos, a fim de avaliar sua resistência. Os resultados mostraram que as formulações resinas/argila aumentaram a estabilidade térmica da palha, promoveram uma boa impermeabilização e causaram significativa redução nos valores de módulo elástico e tensão de ruptura. Ao avaliar o efeito do envelhecimento nas propriedades mecânicas, percebeu-se boa recuperação nos valores de módulo e tensão para a palha revestida com as formulações A 60 e A 80%. Já os resultados de deformação mostraram que os valores permaneceram bem próximos. Dessa forma, conclui-se que a palha de carnaúba pode vir a ser utilizada como revestimento de dutos com significante redução de custos, já que não há a necessidade de tratamento prévio para seu uso e mostra-se como uma alternativa biotecnológica viável, contribuindo com a qualidade de material de revestimentos e a preservação do meio ambiente. 2014-12-17T15:41:55Z 2012-03-20 2014-12-17T15:41:55Z 2011-02-28 masterThesis FERNANDES, Jéssica Emanuela de Araújo. Uso da palha de carnaúba em revestimento de dutos. 2011. 102 f. Dissertação (Mestrado em Físico-Química; Química) - Universidade Federal do Rio Grande do Norte, Natal, 2011. https://repositorio.ufrn.br/jspui/handle/123456789/17648 por Acesso Aberto application/pdf application/pdf Universidade Federal do Rio Grande do Norte BR UFRN Programa de Pós-Graduação em Química Físico-Química; Química |