Determinação do perfil térmico em amostras de aço AISI M35 imersas em plasma

Mostrar outras versões (1)

The heat transfer between plasma and a solid occurs mostly due the radiation and the collision of the particles on the material surface, heating the material from the surface to the bulk. The thermal gradient inside the sample depends of the rate of particles collisions and thermal conductivity of t...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Galvão, Nierlly Karinni de Almeida Maribondo
Outros Autores: Alves Júnior, Clodomiro
Formato: Dissertação
Idioma:por
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
Gradiente térmico
Cátodo oco
Aço M35
Plasma
Thermal gradient
Hollow cathode
M35 steel
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Endereço do item:https://repositorio.ufrn.br/jspui/handle/123456789/12856
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-12856
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Gradiente térmico
Cátodo oco
Aço M35
Plasma
Thermal gradient
Hollow cathode
M35 steel
Plasma
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
spellingShingle Gradiente térmico
Cátodo oco
Aço M35
Plasma
Thermal gradient
Hollow cathode
M35 steel
Plasma
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Galvão, Nierlly Karinni de Almeida Maribondo
Determinação do perfil térmico em amostras de aço AISI M35 imersas em plasma
description The heat transfer between plasma and a solid occurs mostly due the radiation and the collision of the particles on the material surface, heating the material from the surface to the bulk. The thermal gradient inside the sample depends of the rate of particles collisions and thermal conductivity of the solid. In order to study that effect, samples of AISI M35 steel, with 9,5 mm X 3,0 mm (diameter X thickness) were quenched in resistive furnace and tempereds in plasma using the plane configuration and hollow cathode, working with pressures of 4 and 10 mbar respectively. Analyzing the samples microstructure and measuring the hardness along the transversal profile, it was possible to associate the tempered temperature evaluating indirectly the thermal profile. This relation was obtained by microstructural analyzes and through the hardness curve x tempered sample temperature in resistive furnace, using temperatures of 500, 550, 600, 650 and 700°C. The microstructural characterization of the samples was obtained by the scanning electron microscopy, optic microscopy and X-ray diffraction. It was verified that all samples treated in plasma presented a superficial layer, denominated affected shelling zone, wich was not present in the samples treated in resistive furnace. Moreover, the samples that presented larger thermal gradient were treated in hollow cathode with pressure of 4 mbar
author2 Alves Júnior, Clodomiro
author_facet Alves Júnior, Clodomiro
Galvão, Nierlly Karinni de Almeida Maribondo
format masterThesis
author Galvão, Nierlly Karinni de Almeida Maribondo
author_sort Galvão, Nierlly Karinni de Almeida Maribondo
title Determinação do perfil térmico em amostras de aço AISI M35 imersas em plasma
title_short Determinação do perfil térmico em amostras de aço AISI M35 imersas em plasma
title_full Determinação do perfil térmico em amostras de aço AISI M35 imersas em plasma
title_fullStr Determinação do perfil térmico em amostras de aço AISI M35 imersas em plasma
title_full_unstemmed Determinação do perfil térmico em amostras de aço AISI M35 imersas em plasma
title_sort determinação do perfil térmico em amostras de aço aisi m35 imersas em plasma
publisher Universidade Federal do Rio Grande do Norte
publishDate 2014
url https://repositorio.ufrn.br/jspui/handle/123456789/12856
work_keys_str_mv AT galvaonierllykarinnidealmeidamaribondo determinacaodoperfiltermicoemamostrasdeacoaisim35imersasemplasma
_version_ 1773959697404002304
spelling ri-123456789-128562019-01-29T21:52:59Z Determinação do perfil térmico em amostras de aço AISI M35 imersas em plasma Galvão, Nierlly Karinni de Almeida Maribondo Alves Júnior, Clodomiro http://lattes.cnpq.br/8212974625271765 http://lattes.cnpq.br/7441669258580942 Souza Júnior, Caubi Ferreira http://lattes.cnpq.br/5346630547885521 Lima, João Alves de http://lattes.cnpq.br/2699729486137957 Goldenstein, Hélio http://lattes.cnpq.br/7081512949222824 Gradiente térmico Cátodo oco Aço M35 Plasma Thermal gradient Hollow cathode M35 steel Plasma CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA The heat transfer between plasma and a solid occurs mostly due the radiation and the collision of the particles on the material surface, heating the material from the surface to the bulk. The thermal gradient inside the sample depends of the rate of particles collisions and thermal conductivity of the solid. In order to study that effect, samples of AISI M35 steel, with 9,5 mm X 3,0 mm (diameter X thickness) were quenched in resistive furnace and tempereds in plasma using the plane configuration and hollow cathode, working with pressures of 4 and 10 mbar respectively. Analyzing the samples microstructure and measuring the hardness along the transversal profile, it was possible to associate the tempered temperature evaluating indirectly the thermal profile. This relation was obtained by microstructural analyzes and through the hardness curve x tempered sample temperature in resistive furnace, using temperatures of 500, 550, 600, 650 and 700°C. The microstructural characterization of the samples was obtained by the scanning electron microscopy, optic microscopy and X-ray diffraction. It was verified that all samples treated in plasma presented a superficial layer, denominated affected shelling zone, wich was not present in the samples treated in resistive furnace. Moreover, the samples that presented larger thermal gradient were treated in hollow cathode with pressure of 4 mbar Coordenação de Aperfeiçoamento de Pessoal de Nível Superior A transferência de calor entre o plasma e um sólido ocorre principalmente através da radiação e colisão das partículas sobre a superfície do material, o que faz com que o aquecimento do material aconteça da superfície para seu interior. Dependendo da taxa de colisões das partículas e da condutividade térmica do sólido, haverá gradientes térmicos no interior das amostras. A fim de estudar esse efeito, amostras de aço AISI M35, com 9,5 mm X 3,0 mm (diâmetro X espessura) foram temperadas em forno resistivo e revenidas em plasma, nas configurações cátodo planar e cátodo oco, com pressões de trabalho de 4 e 10 mbar, para ambas as configurações. Analisando a microestrutura das amostras e medindo as durezas ao longo do perfil transversal pode-se associar à temperatura de revenido avaliando indiretamente o perfil térmico. Essa relação foi obtida através de análise microestrutural e da curva dureza x temperatura de amostras revenidas em forno resistivo, utilizando temperaturas de 500, 550, 600, 650 e 700°C. A caracterização microestrutural das amostras foi realizada através da microscopia eletrônica de varredura (MEV), microscopia óptica (MO) e difração de raios-X (DRX). Verificou-se que todas as amostras tratadas em plasma apresentaram uma camada superficial, denominada de zona afetada por bombardeamento, que não se encontra presente nas amostras tratadas em forno resistivo. Além disso, verificou-se que as amostras que apresentaram maior gradiente térmico foram as tratadas em cátodo oco com pressão de 4 mbar 2014-12-17T14:07:19Z 2007-08-22 2014-12-17T14:07:19Z 2007-03-22 masterThesis GALVÃO, Nierlly Karinni de Almeida Maribondo. Determinação do perfil térmico em amostras de aço AISI M35 imersas em plasma. 2007. 106 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2007. https://repositorio.ufrn.br/jspui/handle/123456789/12856 por Acesso Aberto application/pdf application/pdf Universidade Federal do Rio Grande do Norte BR UFRN Programa de Pós-Graduação em Ciência e Engenharia de Materiais Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part

Registros relacionados