Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC

Steel is an alloy EUROFER promising for use in nuclear reactors, or in applications where the material is subjected to temperatures up to 550 ° C due to their lower creep resistance under. One way to increase this property, so that the steel work at higher temperatures it is necessary to prevent sli...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Oliveira, Leiliane Alves de
Outros Autores: Gomes, Uilame Umbelino
Formato: doctoralThesis
Idioma:por
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
EUROFER97. Carbeto de Tântalo. Sinterização. Partículas nanométricas. CMM
EUROFER97. Tantalum carbide. Sintering. Particles Nanometrics. CMM
CNPQ::OUTROS
Endereço do item:https://repositorio.ufrn.br/jspui/handle/123456789/12826
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-12826
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic EUROFER97. Carbeto de Tântalo. Sinterização. Partículas nanométricas. CMM
EUROFER97. Tantalum carbide. Sintering. Particles Nanometrics. CMM
CNPQ::OUTROS
spellingShingle EUROFER97. Carbeto de Tântalo. Sinterização. Partículas nanométricas. CMM
EUROFER97. Tantalum carbide. Sintering. Particles Nanometrics. CMM
CNPQ::OUTROS
Oliveira, Leiliane Alves de
Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC
description Steel is an alloy EUROFER promising for use in nuclear reactors, or in applications where the material is subjected to temperatures up to 550 ° C due to their lower creep resistance under. One way to increase this property, so that the steel work at higher temperatures it is necessary to prevent sliding of its grain boundaries. Factors that influence this slip contours are the morphology of the grains, the angle and speed of the grain boundaries. This speed can be decreased in the presence of a dispersed phase in the material, provided it is fine and homogeneously distributed. In this context, this paper presents the development of a new material metal matrix composite (MMC) which has as starting materials as stainless steel EUROFER 97, and two different kinds of tantalum carbide - TaC, one with average crystallite sizes 13.78 nm synthesized in UFRN and another with 40.66 nm supplied by Aldrich. In order to improve the mechanical properties of metal matrix was added by powder metallurgy, nano-sized particles of the two types of TaC. This paper discusses the effect of dispersion of carbides in the microstructure of sintered parts. Pure steel powders with the addition of 3% TaC UFRN and 3% TaC commercial respectively, were ground in grinding times following: a) 5 hours in the planetary mill for all post b) 8 hours of grinding in the mill Planetary only for steel TaC powders of commercial and c) 24 hours in the conventional ball mill mixing the pure steel milled for 5 hours in the planetary mill with 3% TaC commercial. Each of the resulting particulate samples were cold compacted under a uniaxial pressure of 600MPa, on a cylindrical matrix of 5 mm diameter. Subsequently, the compressed were sintered in a vacuum furnace at temperatures of 1150 to 1250 ° C with an increment of 20 ° C and 10 ° C per minute and maintained at these isotherms for 30, 60 and 120 minutes and cooled to room temperature. The distribution, size and dispersion of steel and composite particles were determined by x-ray diffraction, scanning electron microscopy followed by chemical analysis (EDS). The structures of the sintered bodies were observed by optical microscopy and scanning electron accompanied by EDS beyond the x-ray diffraction. Initial studies sintering the obtained steel EUROFER 97 a positive reply in relation to improvement of the mechanical properties independent of the processing, because it is obtained with sintered microhardness values close to and even greater than 100% of the value obtained for the HV 333.2 pure steel as received in the form of a bar
author2 Gomes, Uilame Umbelino
author_facet Gomes, Uilame Umbelino
Oliveira, Leiliane Alves de
format doctoralThesis
author Oliveira, Leiliane Alves de
author_sort Oliveira, Leiliane Alves de
title Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC
title_short Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC
title_full Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC
title_fullStr Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC
title_full_unstemmed Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC
title_sort desenvolvimento e caracterização de um compósito matriz metálica (cmm): aço eurofer97 reforçado com carbeto de tântalo - tac
publisher Universidade Federal do Rio Grande do Norte
publishDate 2014
url https://repositorio.ufrn.br/jspui/handle/123456789/12826
work_keys_str_mv AT oliveiraleilianealvesde desenvolvimentoecaracterizacaodeumcompositomatrizmetalicacmmacoeurofer97reforcadocomcarbetodetantalotac
_version_ 1773963260660285440
spelling ri-123456789-128262019-01-29T21:39:07Z Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC Oliveira, Leiliane Alves de Gomes, Uilame Umbelino http://lattes.cnpq.br/7082478793734403 http://lattes.cnpq.br/9858094266525225 Silva, Ariadne de Souza http://lattes.cnpq.br/5623381698478389 Souza, Carlson Pereira de http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4781094H3 Costa, Franciné Alves da http://lattes.cnpq.br/8698567925323942 Soares, Sérgio Renato da Silva Lima, Severino Jackson Guedes de http://lattes.cnpq.br/1045652409149134 EUROFER97. Carbeto de Tântalo. Sinterização. Partículas nanométricas. CMM EUROFER97. Tantalum carbide. Sintering. Particles Nanometrics. CMM CNPQ::OUTROS Steel is an alloy EUROFER promising for use in nuclear reactors, or in applications where the material is subjected to temperatures up to 550 ° C due to their lower creep resistance under. One way to increase this property, so that the steel work at higher temperatures it is necessary to prevent sliding of its grain boundaries. Factors that influence this slip contours are the morphology of the grains, the angle and speed of the grain boundaries. This speed can be decreased in the presence of a dispersed phase in the material, provided it is fine and homogeneously distributed. In this context, this paper presents the development of a new material metal matrix composite (MMC) which has as starting materials as stainless steel EUROFER 97, and two different kinds of tantalum carbide - TaC, one with average crystallite sizes 13.78 nm synthesized in UFRN and another with 40.66 nm supplied by Aldrich. In order to improve the mechanical properties of metal matrix was added by powder metallurgy, nano-sized particles of the two types of TaC. This paper discusses the effect of dispersion of carbides in the microstructure of sintered parts. Pure steel powders with the addition of 3% TaC UFRN and 3% TaC commercial respectively, were ground in grinding times following: a) 5 hours in the planetary mill for all post b) 8 hours of grinding in the mill Planetary only for steel TaC powders of commercial and c) 24 hours in the conventional ball mill mixing the pure steel milled for 5 hours in the planetary mill with 3% TaC commercial. Each of the resulting particulate samples were cold compacted under a uniaxial pressure of 600MPa, on a cylindrical matrix of 5 mm diameter. Subsequently, the compressed were sintered in a vacuum furnace at temperatures of 1150 to 1250 ° C with an increment of 20 ° C and 10 ° C per minute and maintained at these isotherms for 30, 60 and 120 minutes and cooled to room temperature. The distribution, size and dispersion of steel and composite particles were determined by x-ray diffraction, scanning electron microscopy followed by chemical analysis (EDS). The structures of the sintered bodies were observed by optical microscopy and scanning electron accompanied by EDS beyond the x-ray diffraction. Initial studies sintering the obtained steel EUROFER 97 a positive reply in relation to improvement of the mechanical properties independent of the processing, because it is obtained with sintered microhardness values close to and even greater than 100% of the value obtained for the HV 333.2 pure steel as received in the form of a bar Conselho Nacional de Desenvolvimento Científico e Tecnológico O aço EUROFER é uma liga promissora para utilização em reatores nucleares, ou em aplicações onde o material é submetido a temperaturas de serviço até 550°C devido sua menor resistência sob fluência. Uma forma de aumentar essa propriedade, para que o aço trabalhe a temperaturas mais altas é necessário impedir o deslizamento de seus contornos de grão. Fatores que influenciam nesse deslizamento dos contornos são a morfologia dos grãos, o ângulo e a velocidade dos contornos de grão. Esta velocidade pode ser diminuída com a presença de uma fase dispersa no material, desde que seja fina e distribuída de forma homogênea. Neste contexto, este trabalho apresenta o desenvolvimento de um novo material Compósito de Matriz Metálica (CMM), que tem como materiais de partida o aço inoxidável EUROFER 97; e dois tipos diferentes de Carbeto de Tântalo TaC, um com tamanhos médios de cristalitos de 13,78 nm sintetizado na UFRN e outro com 40,66 nm fornecido pela Aldrich. Objetivando melhorar as propriedades mecânicas da matriz metálica foi adicionado, através da metalurgia do pó, partículas nanométricas desses dois tipos de TaC. Este trabalho discute o efeito da dispersão desses carbetos na microestrutura das peças sinterizadas. Pós de aço puro, com adição de 3% de TaC UFRN e 3% de TaC comercial respectivamente, foram moídos nos seguintes tempos de moagem: a) 5 horas, no moinho planetário para todos os pós; b) 8 horas de moagem no moinho planetário somente para os pós de aço com TaC comercial; e c) 24 horas no moinho convencional de bolas da mistura do aço puro moído durante 5 horas no moinho planetário com 3% de TaC comercial. Cada uma das amostras particuladas resultantes foram compactadas a frio sob uma pressão uniaxial de 600MPa, em uma matriz cilíndrica de 5 mm de diâmetro. Posteriormente, os compactados foram sinterizadas em forno a vácuo, em temperaturas de 1150 e 1250° C com incremento de 20 °C e 10°C por minuto, sendo mantidas nestas isotermas por 30, 60 e 120 minutos e resfriadas à temperatura ambiente. A distribuição, tamanho e dispersão dos aços e compósitos particulados foram determinadas por difração de raios x, microscopia eletrônica de varredura seguida de uma análise química (EDS). As estruturas dos corpos sinterizados foram observadas por microscopia ótica e eletrônica de varredura acompanhada de EDS além da difração de raios x. Os estudos iniciais de sinterização com o aço EUROFER 97 obteve uma resposta positiva em relação a melhoria das propriedades mecânicas independente do processamento, pois se obteve sinterizados com valores de microdureza próximo e até maior que 100% do valor de 333,2 HV obtidos para o aço puro como recebido, em forma de barra 2014-12-17T14:07:16Z 2013-09-04 2014-12-17T14:07:16Z 2013-05-17 doctoralThesis OLIVEIRA, Leiliane Alves de. Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC. 2013. 154 f. Tese (Doutorado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2013. https://repositorio.ufrn.br/jspui/handle/123456789/12826 por Acesso Aberto application/pdf application/pdf Universidade Federal do Rio Grande do Norte BR UFRN Programa de Pós-Graduação em Ciência e Engenharia de Materiais Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part

Registros relacionados