Mesoestruturas porosas a partir de materiais naturais
The MCM-41 mesoporous synthesis was done using rice hulls ash and chrysotile as natural alternative silica sources. For the using of these sources, chemical and thermic treatments were done in both materials. After chemical and thermic treatments, these materials were employed on the MCM-41 mesoc...
Сохранить в:
| Главный автор: | |
|---|---|
| Другие авторы: | |
| Формат: | Dissertação |
| Язык: | por |
| Опубликовано: |
Universidade Federal do Rio Grande do Norte
|
| Предметы: | |
| Online-ссылка: | https://repositorio.ufrn.br/jspui/handle/123456789/12763 |
| Метки: |
Добавить метку
Нет меток, Требуется 1-ая метка записи!
|
| id |
ri-123456789-12763 |
|---|---|
| record_format |
dspace |
| institution |
Repositório Institucional |
| collection |
RI - UFRN |
| language |
por |
| topic |
MCM-41. Fontes alternativas. Materiais mesoporosos MCM-41. Natural sources. Mesoporous materials CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
| spellingShingle |
MCM-41. Fontes alternativas. Materiais mesoporosos MCM-41. Natural sources. Mesoporous materials CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA Schwanke, Anderson Joel Mesoestruturas porosas a partir de materiais naturais |
| description |
The MCM-41 mesoporous synthesis was done using rice hulls ash and chrysotile as
natural alternative silica sources. For the using of these sources, chemical and thermic
treatments were done in both materials. After chemical and thermic treatments, these
materials were employed on the MCM-41 mesoctructures synthesis. The natural materials
treated and employed in the synthesis were characterized by several techniques such as X-ray
diffraction, N2 adsorption and desorption, scanning electronic microscopy and
thermogravimetric analysis. MCM-41 standart samples synthetized with aerosil 200
commercial sílica were used to evaluation. The formed material from rice hulls ash showed
values from BET specific area about 468 m².g-1, N2 adsorption and desorption isotherms and
loss mass similar to reference materials. The silica from chrysotile calcined and leached was
employed to mesoporous materials synthesis. The BET specific area showed values about 700
m².g-1, N2 adsorption and desorption isotherms type IV and loss mass similar to mesoporous
materials. The formed material from calcined and leached chrysotile, without calcination,
applied to phenol remotion carried high performance liquid chromatography and evaluated
with organophilic clays with different treatments. By the characterization techniques were
proved that mesoporous materials with lesser order that reference samples. The material
formed from rice hulls ash without the calcination step achieved better adsorption results than
organophilic clays |
| author2 |
Pergher, Sibele Berenice Castella |
| author_facet |
Pergher, Sibele Berenice Castella Schwanke, Anderson Joel |
| format |
masterThesis |
| author |
Schwanke, Anderson Joel |
| author_sort |
Schwanke, Anderson Joel |
| title |
Mesoestruturas porosas a partir de materiais naturais |
| title_short |
Mesoestruturas porosas a partir de materiais naturais |
| title_full |
Mesoestruturas porosas a partir de materiais naturais |
| title_fullStr |
Mesoestruturas porosas a partir de materiais naturais |
| title_full_unstemmed |
Mesoestruturas porosas a partir de materiais naturais |
| title_sort |
mesoestruturas porosas a partir de materiais naturais |
| publisher |
Universidade Federal do Rio Grande do Norte |
| publishDate |
2014 |
| url |
https://repositorio.ufrn.br/jspui/handle/123456789/12763 |
| work_keys_str_mv |
AT schwankeandersonjoel mesoestruturasporosasapartirdemateriaisnaturais AT schwankeandersonjoel porousmesostructuresfromnaturalmaterials |
| _version_ |
1773959147685937152 |
| spelling |
ri-123456789-127632019-01-29T21:47:04Z Mesoestruturas porosas a partir de materiais naturais Porous mesostructures from natural materials Schwanke, Anderson Joel Pergher, Sibele Berenice Castella http://lattes.cnpq.br/5184076681745031 http://lattes.cnpq.br/5249001430287414 Araújo, Antônio Souza de http://lattes.cnpq.br/9770622597949866 Nascimento, Rubens Maribondo do http://lattes.cnpq.br/8671649752936793 Gusmão, Katia Bernardo http://lattes.cnpq.br/8664708384378316 MCM-41. Fontes alternativas. Materiais mesoporosos MCM-41. Natural sources. Mesoporous materials CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA The MCM-41 mesoporous synthesis was done using rice hulls ash and chrysotile as natural alternative silica sources. For the using of these sources, chemical and thermic treatments were done in both materials. After chemical and thermic treatments, these materials were employed on the MCM-41 mesoctructures synthesis. The natural materials treated and employed in the synthesis were characterized by several techniques such as X-ray diffraction, N2 adsorption and desorption, scanning electronic microscopy and thermogravimetric analysis. MCM-41 standart samples synthetized with aerosil 200 commercial sílica were used to evaluation. The formed material from rice hulls ash showed values from BET specific area about 468 m².g-1, N2 adsorption and desorption isotherms and loss mass similar to reference materials. The silica from chrysotile calcined and leached was employed to mesoporous materials synthesis. The BET specific area showed values about 700 m².g-1, N2 adsorption and desorption isotherms type IV and loss mass similar to mesoporous materials. The formed material from calcined and leached chrysotile, without calcination, applied to phenol remotion carried high performance liquid chromatography and evaluated with organophilic clays with different treatments. By the characterization techniques were proved that mesoporous materials with lesser order that reference samples. The material formed from rice hulls ash without the calcination step achieved better adsorption results than organophilic clays Coordenação de Aperfeiçoamento de Pessoal de Nível Superior A síntese dos mesoporosos do tipo MCM-41 foram realizadas empregando materiais naturais como cinza da casca de arroz e crisotila como fontes alternativas de sílica. Para a utilização destas fontes, tratamentos térmicos e químicos foram realizados em ambos os materiais. Os materiais naturais, após tratamento térmico e químico, foram empregados na formação de mesoestruturas do tipo MCM-41. Os materiais naturais, tratados e empregados na síntese foram caracterizados por diversas técnicas, como difração de raios-X, adsorção e dessorção de N2, microscopia eletrônica de varredura e análise termogravimétrica. Amostras padrões de MCM-41 sintetizadas com sílica comercial pirolisada aerosil 200 foram utilizadas como critério de comparação. O material formado a partir da cinza da casca de arroz calcinada e lixiviada apresentou área específica de 468 m².g-1, isotermas de adsorção e dessorção de N2 típicas de materiais mesoporosos e eventos de perda de massa semelhantes a amostra de referência. A sílica derivada da crisotila calcinada e lixiviada foram utilizadas para a síntese de materiais mesoporosos. O material apresentou valores de área específica BET de 700 m².g-1, isotermas de adsorção e dessorção de N2 do tipo IV e perdas de massa características de materiais mesoporosos. O material formado a partir da cinza da casca de arroz, sem a etapa de calcinação foi aplicado na adsorção de fenol acompanhado por cromatografia líquida de alta eficiência (CLAE) e comparado com argilas organofílicas com diversos tratamentos. Pelas técnicas de caracterização comprova-se que os materiais são do possuem menor ordenação que a amostra de referência. O material formado a partir da cinza da casca de arroz, e sem a etapa de calcinação, obteve melhores resultados de adsorção de fenol, se comparado às argilas organofílicas 2014-12-17T14:07:04Z 2013-04-30 2014-12-17T14:07:04Z 2012-12-17 masterThesis SCHWANKE, Anderson Joel. Porous mesostructures from natural materials. 2012. 90 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2012. https://repositorio.ufrn.br/jspui/handle/123456789/12763 por Acesso Aberto application/pdf application/pdf Universidade Federal do Rio Grande do Norte BR UFRN Programa de Pós-Graduação em Ciência e Engenharia de Materiais Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part |