Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita

Mostrar outras versões (1)

Nickel alloys are frequently used in applications that require resistance at high temperatures associated with resistance to corrosion. Alloys of Ni-Si-C can be obtained by means of powder metallurgy in which powder mixtures are made of metallic nickel powders with additions of various alloying carr...

全面介紹

Na minha lista:
書目詳細資料
主要作者: Nicodemo, Juliana Pivotto
其他作者: Martinelli, Antônio Eduardo
格式: Dissertação
語言:por
出版: Universidade Federal do Rio Grande do Norte
主題:
Metalurgia do pó. Níquel. Portadores de liga. Carbeto de silício e nitreto de silício
Powder metallurgy. Nickel. Alloy carrier. Silicon carbide and silicon nitride
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
在線閱讀:https://repositorio.ufrn.br/jspui/handle/123456789/12758
標簽: 添加標簽
沒有標簽, 成為第一個標記此記錄!
id ri-123456789-12758
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Metalurgia do pó. Níquel. Portadores de liga. Carbeto de silício e nitreto de silício
Powder metallurgy. Nickel. Alloy carrier. Silicon carbide and silicon nitride
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
spellingShingle Metalurgia do pó. Níquel. Portadores de liga. Carbeto de silício e nitreto de silício
Powder metallurgy. Nickel. Alloy carrier. Silicon carbide and silicon nitride
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Nicodemo, Juliana Pivotto
Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita
description Nickel alloys are frequently used in applications that require resistance at high temperatures associated with resistance to corrosion. Alloys of Ni-Si-C can be obtained by means of powder metallurgy in which powder mixtures are made of metallic nickel powders with additions of various alloying carriers for such were used in this study SiC, Si3N4 or Si metal with graphite. Carbonyl Ni powder with mean particle size of 11 mM were mixed with 3 wt% of SiC powders with an average particle size of 15, 30 and 50 μm and further samples were obtained containing 4 to 5% by mass of SiC with average particle size of 15 μm. Samples were also obtained by varying the carrier alloy, these being Si3N4 powder with graphite, with average particle size of 1.5 and 5 μm, respectively. As a metallic Si graphite with average particle size of 12.5 and 5 μm, respectively. The reference material used was nickel carbonyl sintered without adding carriers. Microstructural characterization of the alloys was made by optical microscopy and scanning electron microscopy with semi-quantitative chemical analysis. We determined the densities of the samples and measurement of microhardness. We studied the dissociation of carriers alloy after sintering at 1200 ° C for 60 minutes. Was evaluated also in the same sintering conditions, the influence of the variation of average particle size of the SiC carrier to the proportion of 3% by mass. Finally, we studied the influence of variation of the temperatures of sintering at 950, 1080 and 1200 ° C without landing and also with heights of 30, 60, 120 and 240 minutes for sintering where the temperature was 950 °C. Dilatometry curves showed that the SiC sintered Ni favors more effectively than other carriers alloy analyzed. SiC with average particle size of 15 μm active sintering the alloy more effectively than other SiC used. However, with the chemical and morphological analyzes for all leagues, it was observed that there was dissociation of SiC and Si3N4, as well as diffusion of Si in Ni matrix and carbon cluster and dispersed in the matrix, which also occurred for the alloys with Si carriers and metallic graphite. So the league that was presented better results containing Si Ni with graphite metallic alloy as carriers, since this had dispersed graphite best in the league, reaching the microstructural model proposed, which is necessary for material characteristic of solid lubricant, so how we got the best results when the density and hardness of the alloy
author2 Martinelli, Antônio Eduardo
author_facet Martinelli, Antônio Eduardo
Nicodemo, Juliana Pivotto
format masterThesis
author Nicodemo, Juliana Pivotto
author_sort Nicodemo, Juliana Pivotto
title Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita
title_short Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita
title_full Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita
title_fullStr Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita
title_full_unstemmed Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita
title_sort estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita
publisher Universidade Federal do Rio Grande do Norte
publishDate 2014
url https://repositorio.ufrn.br/jspui/handle/123456789/12758
work_keys_str_mv AT nicodemojulianapivotto estudodasinterabilidadedeligasdeniquelobtidaspormeiodosportadoresdeligasicsi3n4ousimetalicocomgrafita
_version_ 1773964485183143936
spelling ri-123456789-127582019-01-30T09:12:27Z Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita Nicodemo, Juliana Pivotto Martinelli, Antônio Eduardo http://lattes.cnpq.br/4877269210018911 http://lattes.cnpq.br/0022988322449627 Klein, Aloisio Nelmo http://lattes.cnpq.br/4087752487104746 Binder, Cristiano http://lattes.cnpq.br/0692818548181755 Peres, Maurício Mhirdaui http://lattes.cnpq.br/3068024292581677 Metalurgia do pó. Níquel. Portadores de liga. Carbeto de silício e nitreto de silício Powder metallurgy. Nickel. Alloy carrier. Silicon carbide and silicon nitride CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA Nickel alloys are frequently used in applications that require resistance at high temperatures associated with resistance to corrosion. Alloys of Ni-Si-C can be obtained by means of powder metallurgy in which powder mixtures are made of metallic nickel powders with additions of various alloying carriers for such were used in this study SiC, Si3N4 or Si metal with graphite. Carbonyl Ni powder with mean particle size of 11 mM were mixed with 3 wt% of SiC powders with an average particle size of 15, 30 and 50 μm and further samples were obtained containing 4 to 5% by mass of SiC with average particle size of 15 μm. Samples were also obtained by varying the carrier alloy, these being Si3N4 powder with graphite, with average particle size of 1.5 and 5 μm, respectively. As a metallic Si graphite with average particle size of 12.5 and 5 μm, respectively. The reference material used was nickel carbonyl sintered without adding carriers. Microstructural characterization of the alloys was made by optical microscopy and scanning electron microscopy with semi-quantitative chemical analysis. We determined the densities of the samples and measurement of microhardness. We studied the dissociation of carriers alloy after sintering at 1200 ° C for 60 minutes. Was evaluated also in the same sintering conditions, the influence of the variation of average particle size of the SiC carrier to the proportion of 3% by mass. Finally, we studied the influence of variation of the temperatures of sintering at 950, 1080 and 1200 ° C without landing and also with heights of 30, 60, 120 and 240 minutes for sintering where the temperature was 950 °C. Dilatometry curves showed that the SiC sintered Ni favors more effectively than other carriers alloy analyzed. SiC with average particle size of 15 μm active sintering the alloy more effectively than other SiC used. However, with the chemical and morphological analyzes for all leagues, it was observed that there was dissociation of SiC and Si3N4, as well as diffusion of Si in Ni matrix and carbon cluster and dispersed in the matrix, which also occurred for the alloys with Si carriers and metallic graphite. So the league that was presented better results containing Si Ni with graphite metallic alloy as carriers, since this had dispersed graphite best in the league, reaching the microstructural model proposed, which is necessary for material characteristic of solid lubricant, so how we got the best results when the density and hardness of the alloy Coordenação de Aperfeiçoamento de Pessoal de Nível Superior Ligas de Níquel são freqüentemente utilizadas em aplicações que requerem resistência mecânica a elevadas temperaturas associada à resistência à corrosão. Ligas de Ni-Si-C podem ser obtidas por meio de metalurgia do pó em que são realizadas misturas de pós de níquel metálico com adições de pós de diferentes portadores de liga, para tal foram utilizados neste trabalho SiC, Si3N4 ou Si metálico com grafita. Pós de Ni carbonila com tamanho médio de partículas de 11 μm foram misturados a 3% em massa de pós de SiC com tamanho médio de partículas de 15, 30 e 50 μm e foram obtidas ainda amostras contendo 4 e 5% em massa de SiC com tamanho médio de partículas de 15 μm. Também foram obtidas amostras variando-se o portador de liga, sendo estes pós de Si3N4 com grafita, com tamanho médio de partículas de 1,5 e 5 μm, respectivamente. Assim como Si metálico com grafita, com tamanho médio de partículas de 12,5 e 5 μm, respectivamente. O material de referência adotado foi níquel carbonila sinterizado sem adição de portadores. A caracterização microestrutural das ligas foi feita por microscopia óptica e eletrônica de varredura com análise química semi-quantitativa. Foram determinadas as densidades das amostras e obtidas medidas de microdureza Vickers. Foi estudada a dissociação dos portadores de liga após sinterização em 1200 ºC durante 60 minutos. Foi avaliada, ainda, para as mesmas condições de sinterização, a influencia da variação do tamanho médio de partículas do portador SiC, para a proporção de 3% em massa. Por fim, foi estudo a influencia da variação das temperaturas de sinterização em 950, 1080 e 1200 ºC sem patamar e, ainda, com patamares de 30, 60, 120 e 240 minutos para sinterização cuja temperatura foi de 950 ºC. As curvas de dilatometria mostraram que o SiC favorece a sinterização do Ni de forma mais eficaz que os demais portadores de liga analisados. O SiC com tamanho médio de partículas de 15 μm ativa a sinterização da liga de forma mais eficaz que os demais SiC utilizados. Porém, com as análises química e morfológica para todas as ligas, foi possível observar que houve dissociação do SiC e do Si3N4, assim como difusão do Si na matriz de Ni e carbono aglomerado e disperso na matriz, o que também ocorreu para as ligas com portadores Si metálico e grafita. Portanto, a liga que apresentou melhores resultados foi de Ni contendo Si metálico com grafita como portadores de liga, já que esta apresentou grafita melhor dispersa na liga, atingindo o modelo microestrutural proposto, do qual é necessário para material com característica de lubrificante sólido, assim como obteve os melhores resultados quando a densidade e dureza da liga 2014-12-17T14:07:04Z 2013-04-15 2014-12-17T14:07:04Z 2012-06-06 masterThesis NICODEMO, Juliana Pivotto. Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita. 2012. 131 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2012. https://repositorio.ufrn.br/jspui/handle/123456789/12758 por Acesso Aberto application/pdf application/pdf Universidade Federal do Rio Grande do Norte BR UFRN Programa de Pós-Graduação em Ciência e Engenharia de Materiais Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part

相似書籍