Influência das espécies do plasma de N2 + O2 nas propriedades físicoquímicas das superfícies do pet

This work reports the influence of the poly (ethylene terephthalate) textile and films surface modification by plasmas of O2 and mixtures (N2 + O2), on their physical and chemical properties. The plasma surface polymeric modification has been used for many researchs, because it does not affect the e...

Mô tả đầy đủ

Đã lưu trong:
Chi tiết về thư mục
Tác giả chính: Costa, Thércio Henrique de Carvalho
Tác giả khác: Alves Júnior, Clodomiro
Định dạng: doctoralThesis
Ngôn ngữ:por
Được phát hành: Universidade Federal do Rio Grande do Norte
Những chủ đề:
Plasma
Polímeros
Tensão superficial
Espectroscopia ótica
Poliéster
Molhabilidade
Superfíceis poliméricas
Polymer
Surface tension
Optical Spectroscopy
Polyester
Wettability
polymer surface
CNPQ::CIENCIAS EXATAS E DA TERRA
Truy cập trực tuyến:https://repositorio.ufrn.br/jspui/handle/123456789/12753
Các nhãn: Thêm thẻ
Không có thẻ, Là người đầu tiên thẻ bản ghi này!
id ri-123456789-12753
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Plasma
Polímeros
Tensão superficial
Espectroscopia ótica
Poliéster
Molhabilidade
Superfíceis poliméricas
Plasma
Polymer
Surface tension
Optical Spectroscopy
Polyester
Wettability
polymer surface
CNPQ::CIENCIAS EXATAS E DA TERRA
spellingShingle Plasma
Polímeros
Tensão superficial
Espectroscopia ótica
Poliéster
Molhabilidade
Superfíceis poliméricas
Plasma
Polymer
Surface tension
Optical Spectroscopy
Polyester
Wettability
polymer surface
CNPQ::CIENCIAS EXATAS E DA TERRA
Costa, Thércio Henrique de Carvalho
Influência das espécies do plasma de N2 + O2 nas propriedades físicoquímicas das superfícies do pet
description This work reports the influence of the poly (ethylene terephthalate) textile and films surface modification by plasmas of O2 and mixtures (N2 + O2), on their physical and chemical properties. The plasma surface polymeric modification has been used for many researchs, because it does not affect the environment with toxic agents, the alterations remains only at nanometric layers and this technique shows expressive results. Then, due to its good acceptance, the treatment was carried out in a vacuum chamber. Some parameters remained constant during all treatment, such as: Voltage 470 V; Pressure 1,250 Mbar; Current: 0, 10 A and gas flow: 10 cm3/min, using oxygen plasma alternating the treatment time 10 to 60 min with an increase of 10 min to each subsequent treatment. Also, the samples were treated with a gas mixture (nitrogen + oxygen) which was varied only the gas composition from 0 to 100% leaving the treatment time remaining constant to all treatment (10 min). The plasma treatment was characterized in-situ with Optics Emission Spectroscopy (OES), and the samples was characterized by contact angle, surface tension, Through Capillary tests, Raman spectroscopy, Infrared attenuated total reflection (IR-ATR) and atomic force microscopy, scanning electronic Microscopy (SEM) and X-ray Photoelectron Spectroscopy (XPS). The results showed that oxygen treated fabrics presented high wettability, due to the hydrophilic groups incorporation onto the surface formed through spputering of carbon atoms. For the nitrogen atmosphere, there is the a film deposition of amine groups. Treatment with small oxygen concentration in the mixture with nitrogen has a higher spputered species of the samples
author2 Alves Júnior, Clodomiro
author_facet Alves Júnior, Clodomiro
Costa, Thércio Henrique de Carvalho
format doctoralThesis
author Costa, Thércio Henrique de Carvalho
author_sort Costa, Thércio Henrique de Carvalho
title Influência das espécies do plasma de N2 + O2 nas propriedades físicoquímicas das superfícies do pet
title_short Influência das espécies do plasma de N2 + O2 nas propriedades físicoquímicas das superfícies do pet
title_full Influência das espécies do plasma de N2 + O2 nas propriedades físicoquímicas das superfícies do pet
title_fullStr Influência das espécies do plasma de N2 + O2 nas propriedades físicoquímicas das superfícies do pet
title_full_unstemmed Influência das espécies do plasma de N2 + O2 nas propriedades físicoquímicas das superfícies do pet
title_sort influência das espécies do plasma de n2 + o2 nas propriedades físicoquímicas das superfícies do pet
publisher Universidade Federal do Rio Grande do Norte
publishDate 2014
url https://repositorio.ufrn.br/jspui/handle/123456789/12753
work_keys_str_mv AT costatherciohenriquedecarvalho influenciadasespeciesdoplasmaden2o2naspropriedadesfisicoquimicasdassuperficiesdopet
AT costatherciohenriquedecarvalho influenceofplasmaparametersinthephysicalandchemicalpropertiesofpolyesterpolymersurfaces
_version_ 1773961468734078976
spelling ri-123456789-127532019-01-29T21:46:31Z Influência das espécies do plasma de N2 + O2 nas propriedades físicoquímicas das superfícies do pet Influência das espécies do plasma de N2 + O2 nas propriedades físicoquímicas das superfícies do pet Influence of plasma parameters in the physical and chemical properties of polyester polymer surfaces Influence of plasma parameters in the physical and chemical properties of polyester polymer surfaces Costa, Thércio Henrique de Carvalho Alves Júnior, Clodomiro http://lattes.cnpq.br/3647710047561421 http://lattes.cnpq.br/7441669258580942 Silva, Djalma Ribeiro da http://lattes.cnpq.br/2791074318745945 Guerra Neto, Custódio Leopoldino Brito http://lattes.cnpq.br/5387010100082241 Rangel, Elidiane Cipriano http://lattes.cnpq.br/6885205382275380 Lima, José de Anchieta http://lattes.cnpq.br/0742445504420593 Plasma Polímeros Tensão superficial Espectroscopia ótica Poliéster Molhabilidade Superfíceis poliméricas Plasma Polymer Surface tension Optical Spectroscopy Polyester Wettability polymer surface CNPQ::CIENCIAS EXATAS E DA TERRA This work reports the influence of the poly (ethylene terephthalate) textile and films surface modification by plasmas of O2 and mixtures (N2 + O2), on their physical and chemical properties. The plasma surface polymeric modification has been used for many researchs, because it does not affect the environment with toxic agents, the alterations remains only at nanometric layers and this technique shows expressive results. Then, due to its good acceptance, the treatment was carried out in a vacuum chamber. Some parameters remained constant during all treatment, such as: Voltage 470 V; Pressure 1,250 Mbar; Current: 0, 10 A and gas flow: 10 cm3/min, using oxygen plasma alternating the treatment time 10 to 60 min with an increase of 10 min to each subsequent treatment. Also, the samples were treated with a gas mixture (nitrogen + oxygen) which was varied only the gas composition from 0 to 100% leaving the treatment time remaining constant to all treatment (10 min). The plasma treatment was characterized in-situ with Optics Emission Spectroscopy (OES), and the samples was characterized by contact angle, surface tension, Through Capillary tests, Raman spectroscopy, Infrared attenuated total reflection (IR-ATR) and atomic force microscopy, scanning electronic Microscopy (SEM) and X-ray Photoelectron Spectroscopy (XPS). The results showed that oxygen treated fabrics presented high wettability, due to the hydrophilic groups incorporation onto the surface formed through spputering of carbon atoms. For the nitrogen atmosphere, there is the a film deposition of amine groups. Treatment with small oxygen concentration in the mixture with nitrogen has a higher spputered species of the samples Coordenação de Aperfeiçoamento de Pessoal de Nível Superior Neste trabalho, investigou-se a influência do tratamento superficial a plasma utilizando como gases de trabalho o oxigênio e uma mistura de nitrogênio + oxigênio, sobre as propriedades físicas e químicas de tecidose filmes de Poliéster. A modificação superficial de superfícies poliméricas por plasma tem sido bastante utilizada, pois a mesma não apresenta agentes nocivos ao ambiente, às alterações promovidas no material são de escala nanométricas, e comprovadamente é a técnica que tem apresentado resultados mais expressivos. Então, tendo em vista a boa aceitabilidade do uso do plasma em materiais poliméricos, O tratamento foi realizado em uma câmara contendo os gases de trabalho sob baixa pressão (~ 1 mbar) mantendo-se constante durante todo ensaio alguns parâmetros do plasma, tais como, voltagem: 470 V; pressão: 1,250 mbar; corrente: 0,10 A e fluxo de gás: 10 cm3/min, usando plasma com atmosfera gasosa de oxigênio variando-se o tempo de tratamento de 10 - 60 min com incremento de 10 min a cada tratamento subseqüente, e também usou-se a atmosfera gasosa composta por uma mistura de nitrogênio e oxigênio, variando a concentração gasosa dos mesmos (de 0 100%), para um tempo de tratamento de 10 min. O tratamento por plasma foi caracterizado in-situ com o auxilio da Espectroscopia de Emissão Ótica,e as amostras foram caracterizadas por medidas de ângulo de contato, tensão superficial, arraste capilar, espectroscopia Raman, Espectroscopia de infravermelho de reflexão total atenuada (IR-ATR), e microscopia de força atômica (AFM), Microscopia Eletrônica de Varredura (MEV) e por espectroscopia de fotoelétrons excitados por raios-X (XPS). Os resultados mostraram que tecidos tratados com atmosfera de oxigênio apresentaram elevada molhabilidade, devido a incorporação de grupos hidrofílicos na superfície formados com o arrancamento de átomos de carbono. Para a atmosfera de nitrogênio, tem-se a deposição de um filme com base em em grupos aminas. Tratamentos com a concentração pequena de Oxigênio numa mistura com Nitrogênio tem-se maior arrancamento de espécies das amostras 2014-12-17T14:07:03Z 2010-07-16 2014-12-17T14:07:03Z 2010-03-29 doctoralThesis COSTA, Thércio Henrique de Carvalho. Influence of plasma parameters in the physical and chemical properties of polyester polymer surfaces. 2010. 112 f. Tese (Doutorado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2010. https://repositorio.ufrn.br/jspui/handle/123456789/12753 por Acesso Aberto application/pdf application/pdf Universidade Federal do Rio Grande do Norte BR UFRN Programa de Pós-Graduação em Ciência e Engenharia de Materiais Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part

Những quyển sách tương tự