Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos
The present work has as objective the development of ceramic pigments based in iron oxides and cobalt through the polymeric precursor method, as well as study their characteristics and properties using methods of physical, chemical, morphological and optical characterizations.In this work was use...
Na minha lista:
| Autor principal: | |
|---|---|
| Outros Autores: | |
| Formato: | Dissertação |
| Idioma: | por |
| Publicado em: |
Universidade Federal do Rio Grande do Norte
|
| Assuntos: | |
| Endereço do item: | https://repositorio.ufrn.br/jspui/handle/123456789/12746 |
| Tags: |
Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
|
| id |
ri-123456789-12746 |
|---|---|
| record_format |
dspace |
| institution |
Repositório Institucional |
| collection |
RI - UFRN |
| language |
por |
| topic |
Pigmentos encapsulados Pechini Precursores poliméricos Encapsulated pigments Pechini Polymeric precursors CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
| spellingShingle |
Pigmentos encapsulados Pechini Precursores poliméricos Encapsulated pigments Pechini Polymeric precursors CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA Macêdo, Dárcia Sâmia Santos Moura de Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos |
| description |
The present work has as objective the development of ceramic pigments based
in iron oxides and cobalt through the polymeric precursor method, as well as
study their characteristics and properties using methods of physical, chemical,
morphological and optical characterizations.In this work was used iron nitrate,
and cobalt citrate as precursor and nanometer silica as a matrix. The synthesis
was based on dissolving the citric acid as complexing agent, addition of metal
oxides, such as chromophores ions and polymerization with ethylene glycol.
The powder obtained has undergone pre-ignition, breakdown and thermal
treatments at different calcination temperatures (700 °C, 800 °C, 900 °C, 1000
°C and 1100 °C). Thermogravimetric analyzes were performed (BT) and
Differential Thermal Analysis (DTA), in order to evaluate the term
decomposition of samples, beyond characterization by techniques such as BET,
which classified as microporous materials samples calcined at 700 ° C, 800 º C
and 900 º C and non-porous when annealed at 1000 ° C and 1100 º C, X-ray
diffraction (XRD), which identified the formation of two crystalline phases, the
Cobalt Ferrite (CoFe2O4) and Cristobalite (SiO2), Scanning Electron
Microscopy (SEM) revealed the formation of agglomerates of particles slightly
rounded;and Analysis of Colorimetry, temperature of 700 °C, 800 °C and 900
°C showed a brown color and 1000 °C and 1100 °C violet |
| author2 |
Paskocimas, Carlos Alberto |
| author_facet |
Paskocimas, Carlos Alberto Macêdo, Dárcia Sâmia Santos Moura de |
| format |
masterThesis |
| author |
Macêdo, Dárcia Sâmia Santos Moura de |
| author_sort |
Macêdo, Dárcia Sâmia Santos Moura de |
| title |
Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos |
| title_short |
Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos |
| title_full |
Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos |
| title_fullStr |
Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos |
| title_full_unstemmed |
Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos |
| title_sort |
síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos |
| publisher |
Universidade Federal do Rio Grande do Norte |
| publishDate |
2014 |
| url |
https://repositorio.ufrn.br/jspui/handle/123456789/12746 |
| work_keys_str_mv |
AT macedodarciasamiasantosmourade sintesedepigmentosceramicosinorganicosnanometricoseencapsuladoscomestruturacoreshellpelarotadosprecursorespolimericos |
| _version_ |
1773966542503936000 |
| spelling |
ri-123456789-127462019-01-30T09:17:27Z Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos Macêdo, Dárcia Sâmia Santos Moura de Paskocimas, Carlos Alberto http://lattes.cnpq.br/4660330319046456 http://lattes.cnpq.br/2365059843175411 Moraes, Márcio Luiz Varela Nogueira de http://lattes.cnpq.br/2573306822477569 Nascimento, Rubens Maribondo do http://lattes.cnpq.br/8671649752936793 Pigmentos encapsulados Pechini Precursores poliméricos Encapsulated pigments Pechini Polymeric precursors CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA The present work has as objective the development of ceramic pigments based in iron oxides and cobalt through the polymeric precursor method, as well as study their characteristics and properties using methods of physical, chemical, morphological and optical characterizations.In this work was used iron nitrate, and cobalt citrate as precursor and nanometer silica as a matrix. The synthesis was based on dissolving the citric acid as complexing agent, addition of metal oxides, such as chromophores ions and polymerization with ethylene glycol. The powder obtained has undergone pre-ignition, breakdown and thermal treatments at different calcination temperatures (700 °C, 800 °C, 900 °C, 1000 °C and 1100 °C). Thermogravimetric analyzes were performed (BT) and Differential Thermal Analysis (DTA), in order to evaluate the term decomposition of samples, beyond characterization by techniques such as BET, which classified as microporous materials samples calcined at 700 ° C, 800 º C and 900 º C and non-porous when annealed at 1000 ° C and 1100 º C, X-ray diffraction (XRD), which identified the formation of two crystalline phases, the Cobalt Ferrite (CoFe2O4) and Cristobalite (SiO2), Scanning Electron Microscopy (SEM) revealed the formation of agglomerates of particles slightly rounded;and Analysis of Colorimetry, temperature of 700 °C, 800 °C and 900 °C showed a brown color and 1000 °C and 1100 °C violet Coordenação de Aperfeiçoamento de Pessoal de Nível Superior O presente trabalho tem como objetivo o desenvolvimento de pigmentos cerâmicos a base de óxidos de ferro e cobalto através do método dos precursores poliméricos, bem como o estudo de suas características e propriedades através de métodos de caracterizações físicas, químicas, morfológicas e ópticas. Neste trabalho foi utilizado nitrato de ferro e citrato de cobalto como precursores e sílica nanométrica como matriz. A síntese foi baseada na dissolução do ácido cítrico, como agente complexante; adição dos óxidos metálicos, como íons cromóforos e polimerização com etileno glicol. O Pó obtido passou por pré-calcinação, desagregação e tratamentos térmicos em diferentes temperaturas de calcinação (700 ºC, 800 ºC, 900 ºC, 1000 ºC e 1100 °C). Foram feitas Análises de Termogravimetria (TG) e Análise Térmica Diferencial (DTA), a fim de se avaliar a termodecomposição das amostras, além de caracterizações por técnicas como BET, que classificou como materiais microporosos as amostras calcinadas a 700 ºC, 800 ºC e 900 ºC e não porosos quando calcinados a 1000 °C e 1100 ºC; Difração de Raios-X (DRX), que identificou a formação de duas fases cristalinas, a Ferrita de Cobalto (CoFe2O4) e a Cristobalita (SiO2); Microscopia Eletrônica de Varredura (MEV), que revelou a formação de aglomerados de partículas ligeiramente arredondadas; e análise de colorimetria na região do UV-Visível, verificando a variação e o potencial de cromaticidade do pigmento que a temperaturas de 700 °C, 800 °C e 900 °C apresentou a cor marrom e a 1000 °C e 1100 ºC a cor violeta 2014-12-17T14:07:02Z 2012-10-15 2014-12-17T14:07:02Z 2012-04-09 masterThesis MACÊDO, Dárcia Sâmia Santos Moura de. Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos. 2012. 90 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2012. https://repositorio.ufrn.br/jspui/handle/123456789/12746 por Acesso Aberto application/pdf application/pdf Universidade Federal do Rio Grande do Norte BR UFRN Programa de Pós-Graduação em Ciência e Engenharia de Materiais Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part |