Estudo de revestimentos inorgânicos com inibidor de corrosão aplicado na superfície do concreto

Taispeáin leaganacha eile (1)

The corrosive phenomenon on reinforced concrete structures is one of the most founded pathologies on the coastal area. With the objective to prevent the process development, or even, retard its beginning, it was studied the application of inorganic covering over concrete surfaces, after its cure,...

Cur síos iomlán

Sábháilte in:
Sonraí bibleagrafaíochta
Príomhchruthaitheoir: Nunes, Pollyanna Thaís Tavares Batista
Rannpháirtithe: Gomes, Uilame Umbelino
Formáid: Dissertação
Teanga:por
Foilsithe / Cruthaithe: Universidade Federal do Rio Grande do Norte
Ábhair:
Concreto
Corrosão
Curvas de polarização
Concrete
Corrosion
Polarization curves
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Rochtain ar líne:https://repositorio.ufrn.br/jspui/handle/123456789/12718
Clibeanna: Cuir clib leis
Níl clibeanna ann, Bí ar an gcéad duine le clib a chur leis an taifead seo!
id ri-123456789-12718
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Concreto
Corrosão
Curvas de polarização
Concrete
Corrosion
Polarization curves
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
spellingShingle Concreto
Corrosão
Curvas de polarização
Concrete
Corrosion
Polarization curves
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Nunes, Pollyanna Thaís Tavares Batista
Estudo de revestimentos inorgânicos com inibidor de corrosão aplicado na superfície do concreto
description The corrosive phenomenon on reinforced concrete structures is one of the most founded pathologies on the coastal area. With the objective to prevent the process development, or even, retard its beginning, it was studied the application of inorganic covering over concrete surfaces, after its cure, as well as, evaluate the efficiency of the covering applied on the concrete in reducing its porosity of concrete preventing the entrance of aggressive agents to preserve the integrity of the existing armor inside it, comparing the result obtained with the body-of-proof reference, that didn´t receive covering protection. On the concrete production it was used Portland Cement CP II 32, coarse aggregate, fine aggregate and water from the local distributive. Two types of covering were used, one resin based of silicon and solvent and other white cement based, selected sands and acrylic resin. The concrete mixture adopted was 1:1,5:2,5 (cement, fine aggregate, coarse aggregate) and 0.50 water/cement ratio. With the concrete on fresh state was made the experiment test to determinate the workability. On the hardened state was made the concrete resistance experiment, absorption of water and electrochemical experiments, through polarization curves. Also was held optical microscopy and Scanning Electron Microscopy experiments to analyze the layer of the covering applied to the concrete surface and the interface between the concrete and the layer. The obtained results shows that the covering applied to the concrete surface didn´t affect the resistance towards compression. On the absorption of water occurred a diminution of the percentage absorbed, improving the concrete development by making it more impermeable towards the entrance of aggressive agents. The electrochemical experiment results confirmed the water absorption results; the body-of-proof covered presented larger protection towards the development of corrosives process and retarded the evolution of the corrosive phenomenon
author2 Gomes, Uilame Umbelino
author_facet Gomes, Uilame Umbelino
Nunes, Pollyanna Thaís Tavares Batista
format masterThesis
author Nunes, Pollyanna Thaís Tavares Batista
author_sort Nunes, Pollyanna Thaís Tavares Batista
title Estudo de revestimentos inorgânicos com inibidor de corrosão aplicado na superfície do concreto
title_short Estudo de revestimentos inorgânicos com inibidor de corrosão aplicado na superfície do concreto
title_full Estudo de revestimentos inorgânicos com inibidor de corrosão aplicado na superfície do concreto
title_fullStr Estudo de revestimentos inorgânicos com inibidor de corrosão aplicado na superfície do concreto
title_full_unstemmed Estudo de revestimentos inorgânicos com inibidor de corrosão aplicado na superfície do concreto
title_sort estudo de revestimentos inorgânicos com inibidor de corrosão aplicado na superfície do concreto
publisher Universidade Federal do Rio Grande do Norte
publishDate 2014
url https://repositorio.ufrn.br/jspui/handle/123456789/12718
work_keys_str_mv AT nunespollyannathaistavaresbatista estudoderevestimentosinorganicoscominibidordecorrosaoaplicadonasuperficiedoconcreto
_version_ 1773967011256205312
spelling ri-123456789-127182019-01-29T21:20:22Z Estudo de revestimentos inorgânicos com inibidor de corrosão aplicado na superfície do concreto Nunes, Pollyanna Thaís Tavares Batista Gomes, Uilame Umbelino http://lattes.cnpq.br/9858094266525225 Silva, Djalma Ribeiro da http://lattes.cnpq.br/2791074318745945 Huitle, Carlos Alberto Martinez http://lattes.cnpq.br/2485073932883264 Barreto, Alexandro Diógenes http://lattes.cnpq.br/7824794714646180 Concreto Corrosão Curvas de polarização Concrete Corrosion Polarization curves CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA The corrosive phenomenon on reinforced concrete structures is one of the most founded pathologies on the coastal area. With the objective to prevent the process development, or even, retard its beginning, it was studied the application of inorganic covering over concrete surfaces, after its cure, as well as, evaluate the efficiency of the covering applied on the concrete in reducing its porosity of concrete preventing the entrance of aggressive agents to preserve the integrity of the existing armor inside it, comparing the result obtained with the body-of-proof reference, that didn´t receive covering protection. On the concrete production it was used Portland Cement CP II 32, coarse aggregate, fine aggregate and water from the local distributive. Two types of covering were used, one resin based of silicon and solvent and other white cement based, selected sands and acrylic resin. The concrete mixture adopted was 1:1,5:2,5 (cement, fine aggregate, coarse aggregate) and 0.50 water/cement ratio. With the concrete on fresh state was made the experiment test to determinate the workability. On the hardened state was made the concrete resistance experiment, absorption of water and electrochemical experiments, through polarization curves. Also was held optical microscopy and Scanning Electron Microscopy experiments to analyze the layer of the covering applied to the concrete surface and the interface between the concrete and the layer. The obtained results shows that the covering applied to the concrete surface didn´t affect the resistance towards compression. On the absorption of water occurred a diminution of the percentage absorbed, improving the concrete development by making it more impermeable towards the entrance of aggressive agents. The electrochemical experiment results confirmed the water absorption results; the body-of-proof covered presented larger protection towards the development of corrosives process and retarded the evolution of the corrosive phenomenon O fenômeno de corrosão em estruturas de concreto armado é uma das patologias mais encontradas em áreas litorâneas. Com o objetivo de impedir que o processo se desenvolva ou mesmo retardar o seu início, estudou-se a aplicação de revestimentos inorgânicos sobre a superfície do concreto, após sua cura, bem como, foi avaliado a eficiência dos revestimentos aplicados a superfície do concreto em reduzir a sua porosidade, impedindo a entrada dos agentes agressivos para preservar a integridade da armadura existente no seu interior, comparando o resultado obtido com corpos-de-prova referência, que não receberam nenhum revestimento de proteção. Na produção do concreto utilizou-se o Cimento Portland CP II F 32, agregado graúdo, agregado miúdo e água da concessionária local. Como revestimentos foram utilizados dois tipos, um à base de resina de silicone e solvente e o outro, à base de cimento branco, areias selecionadas e resina acrílica. O traço adotado para o estudo foi 1:1,5:2,5 (cimento, areia e brita) e relação a/c = 0,50. Com o concreto no estado fresco, realizou-se o ensaio de abatimento de tronco de cone para determinação da trabalhabilidade. Já no estado endurecido, realizou-se o ensaio de resistência à compressão, absorção de água e os ensaios eletroquímicos, através de curvas de polarização. Também foram realizados ensaios de Microscopia Óptica e Microscopia Eletrônica de Varredura para análise da camada de revestimento aplicada à superfície do concreto e a interface entre o concreto e a camada. Os resultados obtidos mostram que os revestimentos aplicados à superfície do concreto não afetaram a resistência à compressão. Já em relação à absorção de água houve uma diminuição do percentual absorvido, melhorando o desempenho do concreto por torná-lo mais impermeável à entrada dos agentes agressivos. Os resultados dos ensaios eletroquímicos confirmaram o resultado do ensaio de absorção de água; os CP´s revestidos apresentaram uma maior proteção ao desenvolvimento de processos corrosivos e retardaram a evolução do fenômeno de corrosão 2014-12-17T14:06:58Z 2012-02-13 2014-12-17T14:06:58Z 2011-07-01 masterThesis NUNES, Pollyanna Thaís Tavares Batista. Estudo de revestimentos inorgânicos com inibidor de corrosão aplicado na superfície do concreto. 2011. 86 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2011. https://repositorio.ufrn.br/jspui/handle/123456789/12718 por Acesso Aberto application/pdf application/pdf Universidade Federal do Rio Grande do Norte BR UFRN Programa de Pós-Graduação em Ciência e Engenharia de Materiais Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part

Míreanna comhchosúla