Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida

In this work, was studied the formation of a composite of the refractory metal niobium with copper, through the process of high-energy milling and liquid phase sintering. The HEM can be used to synthesize composite powders with high homogeneity and fine size particle distribution. It may also produc...

ver descrição completa

Na minha lista:
Detalhes bibliográficos
Autor principal: Melchiors, Gilberto
Outros Autores: Gomes, Uilame Umbelino
Formato: Dissertação
Idioma:por
Publicado em: Universidade Federal do Rio Grande do Norte
Assuntos:
Compósitos Nb-Cu
Moagem de alta energia
Sinterização por fase líquida
Composite Nb-Cu
High-Energy Milling
Liquid Phase Sintering
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Endereço do item:https://repositorio.ufrn.br/jspui/handle/123456789/12716
Tags: Adicionar Tag
Sem tags, seja o primeiro a adicionar uma tag!
id ri-123456789-12716
record_format dspace
institution Repositório Institucional
collection RI - UFRN
language por
topic Compósitos Nb-Cu
Moagem de alta energia
Sinterização por fase líquida
Composite Nb-Cu
High-Energy Milling
Liquid Phase Sintering
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
spellingShingle Compósitos Nb-Cu
Moagem de alta energia
Sinterização por fase líquida
Composite Nb-Cu
High-Energy Milling
Liquid Phase Sintering
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Melchiors, Gilberto
Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida
description In this work, was studied the formation of a composite of the refractory metal niobium with copper, through the process of high-energy milling and liquid phase sintering. The HEM can be used to synthesize composite powders with high homogeneity and fine size particle distribution. It may also produce the solid solubility in immiscible systems such as Nb-Cu, or extend the solubility of systems with limited solubility. Therefore, in the immiscible system Cu-Nb, the high-energy milling was successfully used to obtain the composite powder particles. Initially, the formation of composite particles during the HEM and the effect of preparation technique on the microstructure of the material was evaluated. Four loads of Nb and Cu powders containing 20%wt Cu were synthesized by MAE in a planetary type ball mill under different periods of grinding. The influence of grinding time on the metal particles is evaluated during the process by the withdrawal of samples at intermediate times of milling. After compaction under different forces, the samples were sintered in a vacuum furnace. The liquid phase sintering of these samples prepared by HEM produced a homogeneous and fine grained. The composite particles forming the sintered samples are the addition of a hard phase (Nb) with a high melting point, and a ductile phase (Cu) with low melting point and high thermal and electrical conductivities. Based on these properties, the Nb-Cu system is a potential material for many applications, such as electrical contacts, welding electrodes, coils for generating high magnetic fields, heat sinks and microwave absorbers, which are coupled to electronic devices. The characterization techniques used in this study, were laser granulometry, used to evaluate the homogeneity and particle size, and the X-ray diffraction, in the phase identification and to analyze the crystalline structure of the powders during milling. The morphology and dispersion of the phases in the composite powder particles, as well the microstructures of the sintered samples, were observed by scanning electron microscopy (SEM). Subsequently, the sintered samples are evaluated for density and densification. And finally, they were characterized by techniques of measuring the electrical conductivity and microhardness, whose properties are analyzed as a function of the parameters for obtaining the composite
author2 Gomes, Uilame Umbelino
author_facet Gomes, Uilame Umbelino
Melchiors, Gilberto
format masterThesis
author Melchiors, Gilberto
author_sort Melchiors, Gilberto
title Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida
title_short Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida
title_full Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida
title_fullStr Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida
title_full_unstemmed Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida
title_sort caracterização de compósitos nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida
publisher Universidade Federal do Rio Grande do Norte
publishDate 2014
url https://repositorio.ufrn.br/jspui/handle/123456789/12716
work_keys_str_mv AT melchiorsgilberto caracterizacaodecompositosnb20cuobtidospormoagemdealtaenergiaesinterizadosporfaseliquida
_version_ 1773962320466149376
spelling ri-123456789-127162019-01-17T11:16:30Z Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida Melchiors, Gilberto Gomes, Uilame Umbelino http://lattes.cnpq.br/2531564423665660 http://lattes.cnpq.br/9858094266525225 Costa, Franciné Alves da http://lattes.cnpq.br/8698567925323942 Silva, Ariadne de Souza http://lattes.cnpq.br/5623381698478389 Silva, Angelus Giuseppe Pereira da http://lattes.cnpq.br/1435330862718379 Compósitos Nb-Cu Moagem de alta energia Sinterização por fase líquida Composite Nb-Cu High-Energy Milling Liquid Phase Sintering CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA In this work, was studied the formation of a composite of the refractory metal niobium with copper, through the process of high-energy milling and liquid phase sintering. The HEM can be used to synthesize composite powders with high homogeneity and fine size particle distribution. It may also produce the solid solubility in immiscible systems such as Nb-Cu, or extend the solubility of systems with limited solubility. Therefore, in the immiscible system Cu-Nb, the high-energy milling was successfully used to obtain the composite powder particles. Initially, the formation of composite particles during the HEM and the effect of preparation technique on the microstructure of the material was evaluated. Four loads of Nb and Cu powders containing 20%wt Cu were synthesized by MAE in a planetary type ball mill under different periods of grinding. The influence of grinding time on the metal particles is evaluated during the process by the withdrawal of samples at intermediate times of milling. After compaction under different forces, the samples were sintered in a vacuum furnace. The liquid phase sintering of these samples prepared by HEM produced a homogeneous and fine grained. The composite particles forming the sintered samples are the addition of a hard phase (Nb) with a high melting point, and a ductile phase (Cu) with low melting point and high thermal and electrical conductivities. Based on these properties, the Nb-Cu system is a potential material for many applications, such as electrical contacts, welding electrodes, coils for generating high magnetic fields, heat sinks and microwave absorbers, which are coupled to electronic devices. The characterization techniques used in this study, were laser granulometry, used to evaluate the homogeneity and particle size, and the X-ray diffraction, in the phase identification and to analyze the crystalline structure of the powders during milling. The morphology and dispersion of the phases in the composite powder particles, as well the microstructures of the sintered samples, were observed by scanning electron microscopy (SEM). Subsequently, the sintered samples are evaluated for density and densification. And finally, they were characterized by techniques of measuring the electrical conductivity and microhardness, whose properties are analyzed as a function of the parameters for obtaining the composite Neste trabalho, foi estudada a formação de um compósito do metal refratário nióbio com o cobre, através do processo de moagem de alta energia e sinterização por fase líquida. A MAE pode ser usada para sintetizar pós compósitos com alta homogeneidade e fina distribuição de tamanho de partículas. Ela também pode produzir a solubilidade sólida em sistemas imiscíveis como o Nb-Cu, ou, estender a solubilidade de sistemas com limitada solubilidade. Portanto, no sistema imiscível Nb-Cu, a moagem de alta energia foi utilizada com sucesso para a obtenção das partículas do pó compósito. Inicialmente a formação das partículas compósitas durante a MAE e o efeito dessa técnica de preparação na microestrutura do material foi avaliada. Quatro cargas de pós de Nb e Cu contendo 20% em massa de Cu foram sintetizados por MAE em um moinho de bolas tipo planetário, sob diferentes períodos de moagem. A influência do tempo de moagem nas partículas metálicas é avaliada no decorrer do processo, através da retirada de amostras em tempos parciais da moagem. Após a compactação sob diferentes forças, as amostras foram sinterizadas em um forno à vácuo. A sinterização por fase líquida destas amostras preparadas por MAE produziu uma estrutura homogênea e com granulação refinada. As partículas compósitas que formam as amostras sinterizadas, são a junção de uma fase dura (Nb) com alto ponto de fusão, e uma fase dúctil (Cu) de baixo ponto de fusão e de elevadas condutividades térmica e elétrica. Com base nestas propriedades, o sistema Nb-Cu é um material em potencial para inúmeras aplicações, como contatos elétricos, eletrodos de solda, bobinas para geração de altos campos magnéticos, dissipadores de calor e absorvedores de microondas, que são acoplados a dispositivos eletrônicos. As técnicas de caracterização utilizadas neste estudo, foram a granulometria à laser para avaliar a homogeneidade e o tamanho das partículas, e a difração de raios-X, na identificação das fases e análise da estrutura cristalina dos pós durante a moagem. Já a morfologia e a dispersão das fases nas partículas do pó compósito, assim como as microestruturas das amostras sinterizadas, foram observadas através de microscopia eletrônica de varredura (MEV). Posteriormente, as amostras sinterizadas foram avaliadas quanto à densidade e densificação. E, finalmente, foram caracterizadas através de técnicas de medição da condutividade elétrica e microdureza Vickers, cujas propriedades são analisadas em função dos parâmetros de obtenção do compósito 2014-12-17T14:06:58Z 2012-02-13 2014-12-17T14:06:58Z 2011-01-31 masterThesis MELCHIORS, Gilberto. Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida. 2011. 120 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2011. https://repositorio.ufrn.br/jspui/handle/123456789/12716 por Acesso Aberto application/pdf application/pdf Universidade Federal do Rio Grande do Norte BR UFRN Programa de Pós-Graduação em Ciência e Engenharia de Materiais Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part

Registros relacionados